本文采用平板法研究了一种双酚A型氰酸酯树脂的流变特性,通过恒温预固化的方法对其进行改性,并借助红外光谱、差示扫描量热法(DSC)和凝胶渗透色谱法(GPC)等手段分析了预固化对氰酸酯树脂化学结构的影响。在此基础上,针对S-2玻璃纤维/氰酸酯复合材料层板,采用热压机工艺考察了加压时机和预固化对层板成型质量的影响。研究结果表明,该氰酸酯树脂反应活性低且流动性高,热压工艺中树脂流动不易控制;预固化可使氰酸酯树脂发生一定程度的自聚反应,从而降低其流动性,可明显改善氰酸酯树脂的工艺性,提高了层板的成型质量。
The rheological property of a bisphenol A cyanate resin was investigated by means of parallel plate method, it was modified by isothermal precure process. The effects of precure process on the chemical structure of resin were studied by IR, DSC and GPC methods. In addition, the influence of the pressure applying moment and precure conditions on the quality of S-2 glass fiber/cyanate resin composite laminates was analyzed for hot press process. It is shown that the cyanate resin has low cure reactivity and high flowability, so the resin flow can not be controlled easily. The precure process makes the resin cure to a certain extent, decreases resin flowability, improves resin processability significantly, and enhances the composite laminates quality.
出处
《玻璃钢／复合材料》
CAS
CSCD
2009年第4期63-66,共4页
Fiber Reinforced Plastics/Composites
基金
国家自然基金项目(50803002)
关键词
复合材料
热压工艺
流变特性
氰酸酯树脂
composite
hot press process
rheological property
cyanate resin