摘要
本文在研制成功大掺量煤矸石水泥的基础上，对其碳化性能进行了研究。研究结果表明，大掺量煤矸石水泥与普通煤矸石水泥相比、所配制的混凝土具有良好的抗碳化性能。其原因主要在于前者水化产物中氢氧化钙含量较低，水泥石的孔隙率较小且有害孔所占的比例较小。
Based on the development of high gangue content cement. carbonation resistance is studied. It's revealed that the concrete made with this kind of cement has bettercarbonation resistance due to the low porosity, less percent of harmful pores and lower content of Ca(OH )2.
出处
《中国建材科技》
1998年第1期28-30,48,共4页
China Building Materials Science & Technology