通过试验证明了316L焊接接头做晶间腐蚀时,经常会由于熔敷金属塑性不足而发生焊缝开裂或断裂,影响了正常的试验过程与结果评判;并对GB／T4334．5提出补充建议。
Cracks often occurs because of poor ductility when test intergranular corrosion on 316L weld metal, which impact the test course and result seriously. Gives some suggestions to the standard GB/T4334.5.