终锻温度和锻压比对贝氏体非调质钢铁素体析出的影响 被引量:1

Influence of Finishing Forging Temperature and Forging Ratio on Precipitation of Ferrite in Non-Quenched and Tempered Bainitic Steel
在线阅读 下载PDF
导出
摘要 研究了终锻温度810~960℃和锻压比3~6对贝氏体钢(%:0.16C、0.91Si、1.98Mn、1.03Cr、0.17Mo、0.065V、0.001Ti)铁素体析出的影响。结果表明,贝氏体钢锻造过程中的变形提高了钢中奥氏体至铁素体相变的临界温度;在终锻温度为810~820℃时,钢中产生变形诱导铁素体相变,当锻压比由3增至6时,铁素体的体积分数由1.8%增至9.6%,铁素体由针状趋于演变为块状;终锻温度为940~960℃时,钢中铁素体主要为针状,随着锻压比由3增至6,钢中铁素体体积分数由3.0%降至0.6%。 Influence of finishing temperature 810 -960 ℃ and forging ratio 3 -6 on precipitation of ferrite in bainitic steel- 0. 16C, 0. 91Si, 1.98Mn, 1.03Cr, 0. 17Mo, 0. 065V, 0. 001Ti has been studied. Results showed that the critical temperature of phase transformation for austenite to ferrite increased by deformation of the bainitie steel during forging; with forging finishing at 810-820 ℃ the deformation induced ferrite precipitation occurred in steel and with increasing forging ratio from 3 to 6, the volume fraction of ferrite in steel increased from 1.8% to 9. 6% accompanied acicular ferrite evolving to massive ferrite ; and with forging finishing at 940 - 960 ℃, most of ferrite in steel was acicular, with increasing forging ratio from 3 to 6 the volume fraction of ferrite in steel decreased from 3.0% to 0. 6%.
出处 《特殊钢》 北大核心 2009年第1期66-67,共2页 Special Steel
基金 先进钢铁材料国家研究中心课题资助项目(D.09-0110-07-002)
关键词 贝氏体钢 锻压比 铁素体 析出 Bainitic Steel, Forging Ratio, Ferrite, Precipitation
  • 相关文献

参考文献5

二级参考文献17

  • 1牧正志,热处理,1997年,37卷,5页
  • 2Priestner R. Strain Induced γ→αTransformation in the Roll Gap in Carbon and M icroalloyed Stee1[ C]. Proceedings of an International Conference on the Thermomechanical Processing of Microalloyed Austenite, Metallurgical Society of AIME,Edited by A.J.DeArdo,G.A.Ratz,P.J.Wray, 1981,455.
  • 3Matsumura Y, Yada H. Evolution of Ultrafine - grained Ferrite in Hot Successive Deformation[ J]. Trans. ISIJ' 1987,27: 492- 498.
  • 4Beynon,J H,Gloss R,Hodgson P D.The Production of Ultrafine Equiaxed Ferrite in a Low Carbon Microalloyed Steel by Thermomechanical Treatment[J]. Mater. Forum , 1992, 16:37~42.
  • 5Lee S,Kwon D,Lee T K ,et al..Transformation Strengthening byThermomechanical Treatments in C- Mn- Ni- Nb Steels[J]. Metal1. Mater. Trans. A., 1995, 26A: 1093 -1100.
  • 6Choo W Y,Lee J S,Lee C S,et al.. Strain Induced Dynamic Transformation of Austenite to Fine Ferrite and It's Characteristics[ J]. CAMP- ISIJ,2000,13:1144.
  • 7Beynon J H, Gloss R, Hodgson P D. The production of ultrafine equiaxed ferrite in a low carbon microalloyed steel by thermomechanical treatment[J]. Materials Fourm, 1992, 16(1) :37 - 42.
  • 8Hodgson P D, Hickson M R, Gibbss R K, The production and mechanical properties of ultrafine ferrite[J]. Mater Sci Fourm, 1998,284 - 286:63 - 72.
  • 9Hickson M R, Gibbs R K, Hodgson PD. The effect of chemistry on the formation of ultrafine ferrite in steel[J] .ISIJ International, 1999,39(11): 1176 - 1180.
  • 10Priestner R, Ibraheem A K. Processing of steel for ultrafine ferrite grain structures[J]. Mater Sci Tech. 2000, 16( 11-12): 1267 - 1272.

共引文献97

同被引文献4

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部