摘要
The effects of slurry temperature, injection pressure, and piston velocity on the rheo-filling ability of semisolid A356 alloys were studied by the reho-diecasting methods. The results show that the slurry temperature of the semi-solid A356 aluminum alloy has an important effect on the filling ability; the higher the slurry temperature, the better is the filling ability, and the appropriate slurry temperature for rheo-filling is in the range of 585-595℃. The injection pressure also has a great effect on the filling ability, and it is appropriate to the rheo-filling when the injection pressure is in the range of 15-25 MPa. The piston velocity also has a great effect on the filling ability, and it is appropriate to the rheo-filling when the piston velocity is in the range of 0.072-0.12 m/s. The filling ability of the slurry prepared by low superheat pouring with weak electromagnetic stirring is very good and the microstructural distribution in the rheo-formed die castings is homogeneous, which is advantageous to the high quality die casting. 2008 University of Science and Technology Beijing. All rights reserved.
The effects of slurry temperature, injection pressure, and piston velocity on the rheo-filling ability of semisolid A356 alloys were studied by the reho-diecasting methods. The results show that the slurry temperature of the semi-solid A356 aluminum alloy has an important effect on the filling ability; the higher the slurry temperature, the better is the filling ability, and the appropriate slurry temperature for rheo-filling is in the range of 585-595℃. The injection pressure also has a great effect on the filling ability, and it is appropriate to the rheo-filling when the injection pressure is in the range of 15-25 MPa. The piston velocity also has a great effect on the filling ability, and it is appropriate to the rheo-filling when the piston velocity is in the range of 0.072-0.12 m/s. The filling ability of the slurry prepared by low superheat pouring with weak electromagnetic stirring is very good and the microstructural distribution in the rheo-formed die castings is homogeneous, which is advantageous to the high quality die casting. 2008 University of Science and Technology Beijing. All rights reserved.
基金
the National Nature Science Foundation of China(No.50774007)
the National High Technology Research and Development Program of China(No.2006AA03Z115)
the National Key Basic Research Program of China(No.2006CB605203).