利用熔体铜模喷铸法制备出直径为3 mm的Mg65Cu25-xNixTb10(x=0,5,10)非晶合金。利用X射线衍射、差热分析、压缩实验分析和扫描电镜分析了添加Ni元素对Mg-Cu-Tb非晶合金形成能力及力学性能的影响。研究表明:随着Ni含量的增加,合金的玻璃转变温度Tg增大;开始结晶温度Tx降低;过冷液相区宽度ΔTx减小,约化玻璃转变温度Trg从0.562降至0.530,非晶形成能力逐渐降低。压缩实验结果表明:当Ni含量增加到5%时可以明显提高Mg-Cu-Tb-Ni非晶合金的断裂强度。
The Mg65Cu25-xNixTb10（x=0, 5, 10） bulk amorphous alloy rods with 3 mm diameters were prepared by copper mold casting technique, and the effect of Ni addition on the glass forming ability （GFA） and mechanical properties of Mg65Cu25-xNixTb10（x=0, 5, 10） alloys were studied by to X-ray diffractometry （XRD）, differential scanning calorimeter （DSC） , compression tests and scanning electron microscopy （SEM）. The results show that the glass transition temperature （Tg） of the Mg65Cu25-xNixTb10 alloys increases slightly whereas the onset temperature of crystallization （Tx）, decreases slightly with the increase of Ni content, which results in the decrease of the supercooled liquid region and the glass forming ability. However, an appropriate substitution of Cu by Ni（5%, mole fraction） in Mg65Cu25Tb10 significantly improves the mechanical properties.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
2007年第2期303-307,共5页
The Chinese Journal of Nonferrous Metals
基金
陕西省科技攻关资助项目(2005k06-G2)
新世纪优秀人才支持计划资助项目
西北工业大学科技创新计划资助项目
英才计划支持资助项目
关键词
镁基非晶合金
非晶形成能力
热稳定性
力学性能
Mg-based metallic glasses
glass-forming ability
thermal stability
mechanical properties Mg-based metallic glasses
glass-forming ability
thermal stability
mechanical properties