In order to improve the prediction capability of spring-back in aluminum sheet metal forming, the influence of the plastic deformation on elastic modulus is considered when the material undergoes a large plastic deformation. The present work focused on establishing a new model to accurately describe the relation of elastic modulus and plastic deformation. The tensile tests were performed to investigate the influence of plastic deformation on elastic modulus at low strain rate. Two different aluminum sheets were used, AA2024-T3 and LY12-CZ, and the thickness of sheet metals was 1.3 mm and 2.0 mm, respectively. In order to overcome the drawback, which is directly measuring the slope of tension curve to obtain elastic modulus, an extrapolation method was adopted. The proposal macroscopic piecewise sinusoidal function can accurately model the elastic modulus variation.
In order to improve the prediction capability of spring-back in aluminum sheet metal forming, the influence of the plastic deformation on elastic modulus is considered when the material undergoes a large plastic deformation. The present work focused on establishing a new model to accurately describe the relation of elastic modulus and plastic deformation. The tensile tests were performed to investigate the influence of plastic deformation on elastic modulus at low strain rate. Two different aluminum sheets were used, AA2024-T3 and LY12-CZ, and the thickness of sheet metals was 1.3 mm and 2.0 mm, respectively. In order to overcome the drawback, which is directly measuring the slope of tension curve to obtain elastic modulus, an extrapolation method was adopted. The proposal macroscopic piecewise sinusoidal function can accurately model the elastic modulus variation.
出处
《中国有色金属学会会刊：英文版》
CSCD
2006年第A03期1314-1318,共5页
Transactions of Nonferrous Metals Society of China
基金
Project(06-13) supported by the Foundation of State Key Laboratory of Plastic Forming Simulation and Die & Mould Technology, China
关键词
塑料变形
铝片
金属加工
可成形性
plastic deformation
elastic modulus
aluminum alloy
spring-back