The flow stress at elevated temperatures for magnesium alloy AZ31 was studied using isothermal compression testing. The effect of deformation paranwters on the flow stress was studied aa well. The kinetics of elevated temperature deformation was expressed by means of some empirical rate equations. The activation parameter has been calculated. A mechanism for the dynamic softening of AZ31 alloy in a hot deformation experiment was identified to be the dynamic recrystallization.
The flow stress at elevated temperatures for magnesium alloy AZ31 was studied using isothermal compression testing. The effect of deformation paranwters on the flow stress was studied aa well. The kinetics of elevated temperature deformation was expressed by means of some empirical rate equations. The activation parameter has been calculated. A mechanism for the dynamic softening of AZ31 alloy in a hot deformation experiment was identified to be the dynamic recrystallization.