In twin-roll strip casting process, metal flow and temperature distribution in the molten pool directly affect the stability of the process and the quality of products. In this paper, a 3D coupled thermal-flow fenite element modeling （FEM） simulation for twin-roll strip casting of stainless steel was performed. Influences of the pouring temperature and casting speed on the temperature fields were obtained from the numerical simulation. The micro-segregation of the solutes during the strip casting process of stainless steel was also simulated. A developed micro-segregation model was used to calculate the micro-segregation of solutes in twin-roll casting of stainless steel. The relationship between the solidus fraction in solidification and temperature was given, which was used to determine the LIT （liquid impermeable temperature）, ZST （zero strength temperature） and ZDT （zero ductility temperature） in the period of non-equilibrium solidification. The effect of temperature on the micro-segregation was discussed. According to the computational results, the solidification completion temperature in the twin-roll strip casting of stainless steel was then determined, which can provide a basis for controlling the location of solidification completion temperature and analysing the crack of the casting strip.
In twin-roll strip casting process, metal flow and temperature distribution in the molten pool directly affect the stability of the process and the quality of products. In this paper, a 3D coupled thermal-flow fenite element modeling （FEM） simulation for twin-roll strip casting of stainless steel was performed. Influences of the pouring temperature and casting speed on the temperature fields were obtained from the numerical simulation. The micro-segregation of the solutes during the strip casting process of stainless steel was also simulated. A developed micro-segregation model was used to calculate the micro-segregation of solutes in twin-roll casting of stainless steel. The relationship between the solidus fraction in solidification and temperature was given, which was used to determine the LIT （liquid impermeable temperature）, ZST （zero strength temperature） and ZDT （zero ductility temperature） in the period of non-equilibrium solidification. The effect of temperature on the micro-segregation was discussed. According to the computational results, the solidification completion temperature in the twin-roll strip casting of stainless steel was then determined, which can provide a basis for controlling the location of solidification completion temperature and analysing the crack of the casting strip.
基金
The authors thank the financial support by the National Natural Science Foundation of China （No. 50474016）.