摘要
基于对高性能混凝土性能影响的研究报道大多是单掺或双掺,利用均匀设计采用多种复合掺,研究不同品种和不同用量的矿物质超细粉复合作用对高性能混凝土工作性、力学性能的影响。结果表明,当配比组合为水泥:磨细矿渣:粉煤灰:硅灰:膨胀剂=3:1:1:0.2:0.02时,塌落度超过130 mm,7d、28d、56d劈拉及抗压强度分别达到5.5/45.55 MPa、7.7/71.05 MPa、8.3/88.8 MPa。研究中利用SPSS软件中的逐步回归分析法和MATLAB中的优化技术,利用计算机技术实现了高性能混凝土配合比设计的优化与预测。
This paper studies the effect of different brands and different quantities of super-thin mineral power on the workability and mechanics function of the high performance concrete with uniform design, because nobody has studies it. The result shows the slump of concrete is beyond 130mm and compressive strength at 7d,28d and 56d are 5.5/45.55MPa,7.7/71.05MPa, 8.3/88.8MPa, respectively when the mixture ratio of concrete is cement： super-thin mineral power： fly ash： silica fume： expansion admixture = 3：1：1：0.2：0.02. In addition, this research realizes the optimization and prediction of the mix ratio of concrete by utilizing the stepwise regression of SPSS and the optimization technique of MATLAB.
出处
《辽宁工程技术大学学报（自然科学版）》
EI
CAS
北大核心
2006年第2期211-213,共3页
Journal of Liaoning Technical University (Natural Science)
基金
辽宁省教育厅高等学校科学技术基金资助项目(05L170)
关键词
矿物质超细粉
均匀设计
高性能混凝土工作性
力学性能
super-thin mineral power
uniform design
high-performance concrete
workability
mechanics function