摘要
研究了Ｆｅ－３０Ｎｉ－２０Ｃｒ－６Ｍｏ铸造合金中微量元素Ｃ对合金元素偏析和耐蚀性的影响。结果表明，当Ｃ含量低时（０．０１７％Ｃ），合金为单一奥氏体组织，合金元素偏析程度小，在ＨＣｌ中耐蚀性较好；提高Ｃ含量（０．０６％Ｃ），合金中Ｃｒ、Ｍｏ、Ｃｕ、Ｓｉ的偏析程度明显增加，并形成了Ｍ６Ｃ型碳化物．因而合金耐蚀性大大下降。
The effect of carbon content on element segregation and corrosion resistance of the cast alloy Fe 30Ni 20Cr 6Mo has been investigated. The results showed that, when carbon content was equal to or lower than 0.017%wt, the structure of alloy was single phase of a ustenite and the segregation degree of alloying elements was low resulting in a high corrosion resistance in HCl aqueous solution; while the carbon content raised to 0.06%wt, the segregation degree of alloying elements Cr, Mo, Cu, Si increased obviously and carbide M 6C was formed in γ matrix, resulting in a low corrosion resistance.
出处
《腐蚀科学与防护技术》
CAS
CSCD
1996年第3期210-213,共4页
Corrosion Science and Protection Technology
关键词
铸造合金
偏析
碳含量
耐蚀性
cast alloy, element segregation, carbon content, corrosion resistance