摘要
To enhance the blood compatibility of Polyvinyl Chloride (PVC) film, the film was modified by SO2/O2 gas plasma treatment. The effect of surface sulfonation of PVC treated by various SO2/O2 gas plasma depended on the volume ratio O2/(SO2 +O2). When the volume ratio was 0.5, the effect of sulfonation was the best. Sulfonic acid groups were specifically and efficiently introduced onto the PVC surface, which was proved by X-ray photoelectron spectroscopy (XPS) and Attenuated Total Reflectance Fourier Transfer Infrared (ATR-FTIR) spectroscopy. The surface microstructure of modified PVC film was studied with scanning electron microscopy (SEM). The antithrombogenicity of the samples was determined by the activated partial thromboplastin time (APTT), prothrombin time (PT), thrombin time (TT) and plasma recalcification time (PRT) tests and platelet adhesion experiment. The results indicated that the antithrombogenicity of modified PVC was improved remarkably.
To enhance the blood compatibility of Polyvinyl Chloride (PVC) film, the film was modified by SO2/O2 gas plasma treatment. The effect of surface sulfonation of PVC treated by various SO2/O2 gas plasma depended on the volume ratio O2/(SO2 +O2). When the volume ratio was 0.5, the effect of sulfonation was the best. Sulfonic acid groups were specifically and efficiently introduced onto the PVC surface, which was proved by X-ray photoelectron spectroscopy (XPS) and Attenuated Total Reflectance Fourier Transfer Infrared (ATR-FTIR) spectroscopy. The surface microstructure of modified PVC film was studied with scanning electron microscopy (SEM). The antithrombogenicity of the samples was determined by the activated partial thromboplastin time (APTT), prothrombin time (PT), thrombin time (TT) and plasma recalcification time (PRT) tests and platelet adhesion experiment. The results indicated that the antithrombogenicity of modified PVC was improved remarkably.
基金
The project supported by the Natural Science Foundation of Shanxi Province ( No. 2001H18) and the Research Foundation of Shanxi Province for Abroad Returnee (No. 200177)