Microstructures and mechanical properties of Ti-V micro-alloyed TRIP（ transformation-induced plasticity） steel with different compositions were investigated by tensile test,scanning electron microscopy（ SEM）,trans...Microstructures and mechanical properties of Ti-V micro-alloyed TRIP（ transformation-induced plasticity） steel with different compositions were investigated by tensile test,scanning electron microscopy（ SEM）,transmission electron microscopy（ TEM）,X-ray diffraction（ XRD） and thermodynamic calculation（ TC）. The results indicated that the steel exhibited high ultimate tensile strength（ 1 079MPa）,sufficient ductility（ 28%） and the highest product of strength and ductility（ 30 212 MPa·%） heat treated after intercritical annealing at 800℃ for 3 min and bainitic annealing at 430 ℃ for 5 min. In addition,the change of volume fraction of retained austenite（ VF-RA） versus tensile strain was measured using in-situ analysis by X-ray stress apparatus and micro-electronic universal testing machine. It was concluded that a-value could be used to evaluate the stability of retained austenite（ S-RA） in the investigated Ti-V micro-alloyed TRIP steel. The smaller a-value indicated the higher stability of retained austenite（ S-RA） and the higher mechanical properties of Ti-V micro-alloyed TRIP steel.展开更多
基金supported by the Shanghai Municipal Science and Technology Commission(Grant No.15DZ2260300,15DZ2260301)Shanghai Municipal Natural Science Foundation(17ZR1410400)
文摘Microstructures and mechanical properties of Ti-V micro-alloyed TRIP（ transformation-induced plasticity） steel with different compositions were investigated by tensile test,scanning electron microscopy（ SEM）,transmission electron microscopy（ TEM）,X-ray diffraction（ XRD） and thermodynamic calculation（ TC）. The results indicated that the steel exhibited high ultimate tensile strength（ 1 079MPa）,sufficient ductility（ 28%） and the highest product of strength and ductility（ 30 212 MPa·%） heat treated after intercritical annealing at 800℃ for 3 min and bainitic annealing at 430 ℃ for 5 min. In addition,the change of volume fraction of retained austenite（ VF-RA） versus tensile strain was measured using in-situ analysis by X-ray stress apparatus and micro-electronic universal testing machine. It was concluded that a-value could be used to evaluate the stability of retained austenite（ S-RA） in the investigated Ti-V micro-alloyed TRIP steel. The smaller a-value indicated the higher stability of retained austenite（ S-RA） and the higher mechanical properties of Ti-V micro-alloyed TRIP steel.