Nano-zinc oxides(ZnO)demonstrate remarkable antibacterial properties.To further enhance the corrosion resistance and antibacterial efficiency of magnesium alloy micro-arc oxidation(MAO)coatings,this study investigates...Nano-zinc oxides(ZnO)demonstrate remarkable antibacterial properties.To further enhance the corrosion resistance and antibacterial efficiency of magnesium alloy micro-arc oxidation(MAO)coatings,this study investigates the preparation of ZnO-containing micro-arc oxidation coatings with dual functionality by incorporating nano-ZnO into MAO electrolyte.The influence of varying ZnO concentrations on the microstructure,corrosion resistance,and antibacterial properties of the coating was examined through microstructure analysis,immersion tests,electrochemical experiments,and antibacterial assays.The findings revealed that the addition of nano-ZnO significantly enhanced the corrosion resistance of the MAO-coated alloy.Specifically,when the ZnO concentration in the electrolyte was 5 g/L,the corrosion rate was more than ten times lower compared to the MAO coatings without ZnO.Moreover,the antibacterial efficacy of ZnO+MAO coating,prepared with a ZnO concentration of 5 g/L,surpassed 95%after 24 h of co-culturing with Staphylococcus aureus(S.aureus).The nano-ZnO+MAO-coated alloy exhibited exceptional degradation resistance,corrosion resistance,and antibacterial effectiveness.展开更多
TC4 micro-arc oxidation(MAO)coatings were prepared by adding SiO_(2) nanoparticles or sodium silicate to the sodium meta-aluminate-based electrolyte.The effect of additives was investigated by XRD,SEM,EDS,electrochemi...TC4 micro-arc oxidation(MAO)coatings were prepared by adding SiO_(2) nanoparticles or sodium silicate to the sodium meta-aluminate-based electrolyte.The effect of additives was investigated by XRD,SEM,EDS,electrochemical and wear tests.The results show that additives can considerably accelerate the formation of MAO coatings.The coatings are mostly composed of rutile and anatase TiO_(2),α-Al_(2)O_(3),γ-Al_(2)O_(3),Al_(2)TiO_(5) and SiO_(2).Sodium silicate and SiO_(2) nanoparticles added to the coating can effectively reduce the size of micropores and increase its thickness,whereas SiO_(2) nanoparticles with superior physical properties can be directly deposited at the discharge channel,significantly increasing the coating's resistance to wear and corrosion.The coating with SiO_(2) nanoparticles exhibits the best overall performance,with the lowest corrosion rate and average friction coefficient of 4.095×10^(-5)mm/a and 0.30,respectively.展开更多
Micro-arc oxidation(MAO)flm can only provide common mechanical protection for magnesium(Mg)–lithium(Li)alloys.These alloys are susceptible to severe localized corrosion,if the MAO flm is disrupted.This work reports t...Micro-arc oxidation(MAO)flm can only provide common mechanical protection for magnesium(Mg)–lithium(Li)alloys.These alloys are susceptible to severe localized corrosion,if the MAO flm is disrupted.This work reports the successful hydrothermal preparation of a MgLiAlCe-LDHs@GO flm on a MAO-coated Mg–Li alloy following Ce confnement.The graphene oxide(GO)sheet increased the difusion path of the corrosive media,and the addition of rare-earth cerium ions(Ce^(3+))endowed the flm with a certain self-healing ability,which signifcantly improved the corrosion resistance of the flm,and the corrosion current density(icorr)reached 3.27×10^(−8)A cm^(−2).The synergistic action of GO and Ce^(3+)can achieve long-term corrosion protection for the substrate.The corrosion resistance mechanism of MgLiAlCe-LDHs@GO flm was discussed by the scanning vibration electrode technique(SVET).展开更多
This research systematically examined the degradation,antibacterial effects,and biocompatibility of micro-arc oxidation(MAO)coatings with nano CuO and ZnO on extruded Mg alloys.Both copper(Cu)and Zinc(Zn)possess antib...This research systematically examined the degradation,antibacterial effects,and biocompatibility of micro-arc oxidation(MAO)coatings with nano CuO and ZnO on extruded Mg alloys.Both copper(Cu)and Zinc(Zn)possess antibacterial properties.The findings demonstrated that adding ZnO will appreciably reduce the degradation rate of MAO-coating alloy due to the self-sealing micro holes.CuO+MAO coating exhibited excellent antibacterial performance,with an antibacterial rate of over 90%within 6 h co-cultured with Staphylococcus aureus.Similarly,the antibacterial rate of ZnO+MAO coating reached 90%after 12 h co-culture.Cytotoxicity test using MG63 cell indicated that the incorporation of CuO and ZnO did not notably affect the cell viability rate of the coating.Moreover,after 14 days of culture,the CuO+MAO and ZnO+MAO coated samples exhibited higher alkaline phosphatase(ALP)activity than the MAO-coated and uncoated samples,suggesting favorable osteogenic properties.展开更多
Oxide ceramic coatings were fabricated on tantalum alloys by micro-arc oxidation (MAO) to improve their hardness and tribological properties. The MAO coatings were manufactured in a mixed silicatephosphate electrolyte...Oxide ceramic coatings were fabricated on tantalum alloys by micro-arc oxidation (MAO) to improve their hardness and tribological properties. The MAO coatings were manufactured in a mixed silicatephosphate electrolyte containing NaF and/or EDTA (ethylene diamine tetraacetic acid). The surface morphology,cross-sectional view, chemical composition, hardness, and wear performance of the coatings were analysed. As revealed by the scanning electron microscopy, silica-rich nodules appear on the MAO coating obtained in the silicate-phosphate electrolyte, but the formation of nodules is inhibited with NaF and/or EDTA in the electrolyte.Also, they reduce the roughness and improve the compactness of the coatings, which are composed of Ta_(2)O_(5),(Ta, O), and TaO. A thick and hard coating is obtained in the NaF-containing electrolyte, and the tribology performance is effectively improved. With additives, the nodule structure is detached from the coating surface and dissolved in the electrolyte. By using NaF as an electrolyte additive, the abrasion performance of the MAO coating is enhanced by decreasing the nodule structure, increasing the size of micropores, and improving the coating hardness.展开更多
Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc...Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.展开更多
The microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy obtained in silicate-,borate- and aluminate-based electrolyte without and with nanoadditive Al2O3 and TiO2 by micro-arc o...The microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy obtained in silicate-,borate- and aluminate-based electrolyte without and with nanoadditive Al2O3 and TiO2 by micro-arc oxidation（MAO） were studied by scanning electron microscopy（SEM）,energy-dispersive X-ray spectroscopy（EDS）,X-ray diffraction（XRD）,microhardness and friction-abrasion tests,respectively.SEM results show that coatings with nanoadditive have less porosities than those without nanoadditive.XRD results reveal that nanoadditive-containing coatings contain more oxides compared with nanoadditive-free coatings in all cases,which are consistent with the EDS analysis.Mechanical properties tests show that nanoadditive Al2O3-containing coatings have higher microhardness values compared with the other coatings obtained in silicate-,borate- and aluminate-based electrolyte.On the other hand,nanoadditive has a positive effect on improving the wearing-resistance of MAO coatings in all cases.Furthermore,the borate-MAO coatings present an inferior anti-wearing property compared with the silicate- and aluminate-MAO coatings for both the nanoadditive-free and nanoadditive-containing coatings.展开更多
Magnesium alloy wires were processed by micro-arc oxidation （MAO） in a modified silicate-phosphate composite electrolyte containing hydroxyapatite （HA） nanopowders and NaOH. Effects of NaOH content in the composit...Magnesium alloy wires were processed by micro-arc oxidation （MAO） in a modified silicate-phosphate composite electrolyte containing hydroxyapatite （HA） nanopowders and NaOH. Effects of NaOH content in the composite electrolyte on the microstructure and properties of the MAO ceramic coatings on magnesium alloy wires were studied. It is found that the arc voltage of magnesium alloy wires in the micro-arc oxidation process is significantly reduced while the oxidation rate is accelerated. Addition of 2 g/L NaOH in the composite electrolyte is a better choice for improving corrosion resistance of magnesium alloy wires. During early simulated body fluids （SBF） immersion, the micro-arc oxidized magnesium alloy wires undergo a slow and stable degradation. After soaking for 28 d, the protective ceramic coating still shows no damage but significant degradation is observed for magnesium alloy wires after immersion for more than 60 d.展开更多
Ceramic oxide coatings were prepared on AZ91D magnesium alloys in alkaline silicate solution using micro-arc oxidation（MAO） technique.The corrosion behavior of MAO coating on AZ91D magnesium alloys in NaCl solutions...Ceramic oxide coatings were prepared on AZ91D magnesium alloys in alkaline silicate solution using micro-arc oxidation（MAO） technique.The corrosion behavior of MAO coating on AZ91D magnesium alloys in NaCl solutions with different concentrations（0.1%,0.5%,1.0%,3.5% and 5.0% in mass fraction） was evaluated by electrochemical measurements and immersion tests.The results showed that the corrosion rate of the MAO coated AZ91D increased with increasing chloride ion concentration.The main form of corrosion failure was localized corrosion for the MAO coated AZ91D immersed in higher concentration NaCl solutions（1.0%,3.5% and 5.0%）,while it was general corrosion in dilute NaCl solutions（0.1% and 0.5%）.Two different stages of the failure process of the MAO coated AZ91D could be identified：1） occurrence of the metastable pits and 2） growth of the pits.Different equivalent circuits were also proposed based on the results of electrochemical impedance spectroscopy（EIS） for the MAO coated AZ91D immersed in different concentrations of NaCl solutions for 120 h.展开更多
Ceramic coatings were fabricated on aluminum doped with different concentrations of TiO2 nano-additive. alloy substrates by micro-arc oxidation （MAO） in silicate electrolytes Effects of nano-additive concentration o...Ceramic coatings were fabricated on aluminum doped with different concentrations of TiO2 nano-additive. alloy substrates by micro-arc oxidation （MAO） in silicate electrolytes Effects of nano-additive concentration on the structural and mechanical properties of the MAO coatings were analyzed. The results revealed that some nano-particle were incorporated into the resulting coating during the MAO process, while there was a reasonable concentration for the TiO2 nano-additive. With increasing the nano-additive concentration to 3.2 g/L, the adhesion value increased, while mean friction coefficient and mass loss decreased. A further increase of nano-additive deteriorated the adhesion and mean friction coefficient values, which was consistent with the micro-hardness tests.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
Micro-arc oxidation （MAO） process was carried out in a dual electrolyte system of NaAlO 2 and Na 3 PO 4 to develop compact, smooth and corrosion-resistant coatings on ZK60 Mg alloy by single factor experiments. The ...Micro-arc oxidation （MAO） process was carried out in a dual electrolyte system of NaAlO 2 and Na 3 PO 4 to develop compact, smooth and corrosion-resistant coatings on ZK60 Mg alloy by single factor experiments. The microstructural characteristics of coatings were investigated by X-ray diffractometry （XRD） and scanning electron microscopy （SEM） coupled with energy dispersive X-ray spectroscopy （EDS）. Test of mass loss was conducted at a 3.5% NaCl solution to assess the resistance to corrosion. The effect of every element in the dual electrolyte system on voltage—time responses during MAO process and the coating characteristic were also analyzed and discussed systematically via single factor experiments. The results reveal that the main components of NaAlO 2 and Na 3 PO 4 as well as additives of NaOH, NaB4O7 and C6H5Na3O7 demonstrate different effects on MAO process and coating characteristics. By means of single factor experiments, an optimized dual electrolyte system was developed, containing 17.5 g/L NaAlO 2, 5.0 g/LNa3 PO4, 5.0 g/L NaOH, 3.0 g/L NaB4O7 and 4.2g/LC6H5Na3O7 .展开更多
A composite ceramic coating containing Y2O3-ZrO2-MgO（YSZ-MgO） was prepared on AZ91D magnesium alloy,which was immersed in Y（NO3）3 aqueous solution as pretreatment,by micro-arc oxidation（MAO） process.The morpholo...A composite ceramic coating containing Y2O3-ZrO2-MgO（YSZ-MgO） was prepared on AZ91D magnesium alloy,which was immersed in Y（NO3）3 aqueous solution as pretreatment,by micro-arc oxidation（MAO） process.The morphology,elemental and phase compositions,corrosion behavior and thermal stability of the coatings were studied by SEM,EDX,XRD,electrochemical corrosion test,high temperature oxidation and thermal shock test.The results show that the coating mainly consists of ZrO2,Y2O3,MgO,Mg2SiO4,and MgF2.Among these compounds,Y2O3 accounts for 26.7% of（Y2O3 ＋ ZrO2）.The thickness of YSZ-MgO coating is smaller than that of ZrO2-MgO coating,but its compactness and surface roughness are better than those of ZrO2-MgO coating.YSZ-MgO coating has a good corrosion resistance,and its corrosion rate in 5% NaCl aqueous solution is lower than that of ZrO2-MgO and only about 8.5% of that of AZ91D magnesium alloy.After oxidation at 410 °C,the mass gain of AZ91D magnesium alloy presents a linear increase with the oxidation time.The YSZ-MgO coating and ZrO2-MgO coating can remarkably decrease the oxidation mass gain.The oxidation mass gain of YSZ-MgO coating is lower than that of ZrO2-MgO coating,especially during a long oxidation period.The thermal shock resistance of YSZ-MgO coating is superior to ZrO2-MgO coating.展开更多
A layer of porous film containing Ca and P was prepared by the micro-arc oxidation method on the surface of a novel near β biomedical Ti-3Zr-2Sn-3Mo-25Nb alloy, and then NH2- active group was introduced to the films ...A layer of porous film containing Ca and P was prepared by the micro-arc oxidation method on the surface of a novel near β biomedical Ti-3Zr-2Sn-3Mo-25Nb alloy, and then NH2- active group was introduced to the films by activation treatment. The phase composition, surface micro-topography and elemental characteristics of the micro-arc oxidation films were investigated with XRD, SEM, EDS and XPS, and the osteoinduction of the micro-arc oxidation films was tested using the simulated body fluid immersion, the in-vitro osteoblast cultivation test and animal experiment. The results show that the oxide layer is a kind of porous ceramic intermixture and contains Ca and P. The films in the simulated body fluid can induce apatite formation, resulting in excellent bioactivity. The cell test discovers that osteoblasts can grow well on the surface of micro-arc oxidation films. And the Ti-3Zr-2Sn-3Mo-25Nb biomedical alloy coated with active porous calcium-phosphate films shows better osteoinduction in vivo.展开更多
A hydrophobic surface was fabricated on a micro-arc oxidation (MAO) treated AZ31 Mg alloys via surface modification with myristic acid. The effects of modification time on the wettability of the coatings were investig...A hydrophobic surface was fabricated on a micro-arc oxidation (MAO) treated AZ31 Mg alloys via surface modification with myristic acid. The effects of modification time on the wettability of the coatings were investigated using the contact angle measuring device. The surface morphologies and structure of the coatings were evaluated using SEM, XRD and FT-IR. The corrosion resistance was investigated by potentiodynamic polarization curves and long-term immersion test. The results showed that the water contact angle (CA) increases gradually with modification time from 0 to 5 h, the highest CA reaches 138° after being modified for 5 h, and the number and size of the micro pores are decreased. The modification method hardly alters crystalline structure of the MAO coating, but improves the corrosion resistance based on the much positive potential and low current density. Moreover, the corrosion resistance and hydrophobicity can be enhanced with increasing the alkyl chain. The wetting and spreading for the alkylcarboxylate with low surface energy become easier on the micro-porous surface, and alkylcarboxylate monolayer will be formed through bidentate bonding, which changes the surface micropores to a sealing or semi-sealing structure and makes the MAO coating dense and hydrophobic. All the results demonstrate that the modification process improves the corrosion protection ability of the MAO coating on AZ31B Mg alloy.展开更多
One of the major obstacles for the clinical use of biodegradable magnesium(Mg)-based materials is their high corrosion rate. Micro-arc oxidation(MAO) coatings on Mg alloys provide mild corrosion protection owing to th...One of the major obstacles for the clinical use of biodegradable magnesium(Mg)-based materials is their high corrosion rate. Micro-arc oxidation(MAO) coatings on Mg alloys provide mild corrosion protection owing to their porous structure. Hence, in this study a dense Mg(OH)2 film was fabricated on MAO-coated Mg alloy AZ31 in an alkaline electrolyte containing ethylenediamine tetraacetic acid disodium(EDTA-2 Na) to reinforce the protection. Surface morphology, chemical composition and growth process of the MAO/Mg(OH)2 hybrid coating were examined using field-emission scanning electron microscopy, energy dispersive X-ray spectrometer, X-ray diffraction, X-ray photoelectron spectroscopy and Fourier transform infrared spectrophotometer. Corrosion resistance of the coatings was evaluated via potentiodynamic polarization curves and hydrogen evolution tests. Results manifested that the Mg(OH)2 coating possesses a porous nano-sized structure and completely seals the micro-pores and micro-cracks of the MAO coating.The intermetallic compound of AlMn phase in the substrate plays a key role in the growth of Mg(OH)2 film. The current density of Mg(OH)2-MAO composite coating decreases three orders of magnitude in comparison with that of bare substrate, indicating excellent corrosion resistance. The Mg(OH)2-MAO composite coating is beneficial to the formation of calcium phosphate corrosion products on the surface of Mg alloy AZ31, demonstrating a great promise for orthopaedic applications.展开更多
Ceramic coatings were prepared on AZ91 D Mg alloy by micro-arc oxidation （MAO） in aluminate electrolytes, with Al2O3 nano-additive suspending at different concentrations. Effects of nano-additive concentration on th...Ceramic coatings were prepared on AZ91 D Mg alloy by micro-arc oxidation （MAO） in aluminate electrolytes, with Al2O3 nano-additive suspending at different concentrations. Effects of nano-additive concentration on the structure, phase composition, hardness and anti-corrosion property of the MAO coatings were analyzed by scanning electron microscopy, X-ray diffraction, micro-hardness test and electrochemical method, respectively. The results revealed that Al2O3 nano-particles were mostly incorporated into ceramic coating chemically, transferred into MgAl2O4, rather than being trapped mechanically during MAO process. With the increase of Al2O3 concentration, the voltage-time response, content of MgAl2O4, hardness and anti-corrosion property increased. However, when the concentration varied from 10 g/L to 15 g/L, these behaviors and properties changed only a little. This result indicated that, after the concentration of Al2O3 nano-additive reaching 10 g/L, the incorporation of Al2O3 nano-particles turned into a saturation state, due to the complex process during MAO treatment. Therefore, 10 g/L might be a proper concentration for MAO coating to incorporate Al2O3 nano-particles,展开更多
Magnesium and its alloys have been used in many industries, but they are reactive and require protection against aggressive environments. In this study, oxide coatings were applied on AZ91D magnesium alloy using micro...Magnesium and its alloys have been used in many industries, but they are reactive and require protection against aggressive environments. In this study, oxide coatings were applied on AZ91D magnesium alloy using micro-arc oxidation （MAO） process. Then, in order to seal the pores of the MAO coatings, the samples were immersed in cerium bath for different times. The surface morphologies and compositions of the coatings were analyzed by scanning electron microscopy （SEM） and X-ray energy dispersive spectroscopy （EDS）, respectively. The corrosion behavior of the coatings was investigated with electrochemical impedance spectroscopy （EIS） and potentiodynamic polarization tests in 3.5 wt.% NaCl solution. The amount of the porosity of the coating was measured by electrochemical method. It was found that the sealing treatments by immersion in cerium bath successfully sealed the pores of the MAO coatings. The results of the corrosion tests showed that the MAO coating which was sealed in Ce bath for 10 min enhanced the corrosion resistance of the substrate significantly. Furthermore, this coating had the lowest amount of the porosity among the coatings.展开更多
The regulation of ceramic coating formed by micro-arc oxidation on Mg-11Gd-1Y-0.5Zn (wt.%) magnesium alloys was investigated by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The relation of phase ...The regulation of ceramic coating formed by micro-arc oxidation on Mg-11Gd-1Y-0.5Zn (wt.%) magnesium alloys was investigated by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The relation of phase structure and corrosion resistance of MgO coating formed by micro-arc oxidation in different growth stages was analyzed. The results showed that the growth of coating accorded with linear regularity in the initial stage of micro-arc oxidation, which was the stage of anodic oxidation controlled ...展开更多
To improve the surface wear resistance of the ceramic coating fabricated by micro-arc oxidation （MAO） on AZ91D magnesium alloy,ceramic coatings embedded with SiC nano-particles at different current frequency （500 H...To improve the surface wear resistance of the ceramic coating fabricated by micro-arc oxidation （MAO） on AZ91D magnesium alloy,ceramic coatings embedded with SiC nano-particles at different current frequency （500 Hz,700 Hz,and 900 Hz） were produced during the MAO process.The morphology and phase composition of the coatings were investigated by scanning electron microscopy （SEM）,field emission scanning electron microscopy （FESEM）,and X-ray diffraction （XRD）.The surface roughness of the coatings was characterized by confocal laser scanning microscopy （CLSM）.Simultaneously,the tribological properties of the composite coatings were evaluated by using a universal materials tester （UMT）.The results shows that the wear resistance of the ceramic coatings with SiC nano-particles was improved significantly compared to the ceramic coatings without SiC nano-particles.Furthermore,the composite coating formed at current frequency 900 Hz showed the better wear resistance than the others.展开更多
基金supported by the National Natural Science Foundation of China(No.52001034)the China Postdoctoral Science Foundation(No.2023M731677)the Postgraduate Research&Practice Innovation Program of Jiangsu Province(No.KYCX23_3032).
文摘Nano-zinc oxides(ZnO)demonstrate remarkable antibacterial properties.To further enhance the corrosion resistance and antibacterial efficiency of magnesium alloy micro-arc oxidation(MAO)coatings,this study investigates the preparation of ZnO-containing micro-arc oxidation coatings with dual functionality by incorporating nano-ZnO into MAO electrolyte.The influence of varying ZnO concentrations on the microstructure,corrosion resistance,and antibacterial properties of the coating was examined through microstructure analysis,immersion tests,electrochemical experiments,and antibacterial assays.The findings revealed that the addition of nano-ZnO significantly enhanced the corrosion resistance of the MAO-coated alloy.Specifically,when the ZnO concentration in the electrolyte was 5 g/L,the corrosion rate was more than ten times lower compared to the MAO coatings without ZnO.Moreover,the antibacterial efficacy of ZnO+MAO coating,prepared with a ZnO concentration of 5 g/L,surpassed 95%after 24 h of co-culturing with Staphylococcus aureus(S.aureus).The nano-ZnO+MAO-coated alloy exhibited exceptional degradation resistance,corrosion resistance,and antibacterial effectiveness.
基金Sichuan Science and Technology Program(2022YFSY0018)。
文摘TC4 micro-arc oxidation(MAO)coatings were prepared by adding SiO_(2) nanoparticles or sodium silicate to the sodium meta-aluminate-based electrolyte.The effect of additives was investigated by XRD,SEM,EDS,electrochemical and wear tests.The results show that additives can considerably accelerate the formation of MAO coatings.The coatings are mostly composed of rutile and anatase TiO_(2),α-Al_(2)O_(3),γ-Al_(2)O_(3),Al_(2)TiO_(5) and SiO_(2).Sodium silicate and SiO_(2) nanoparticles added to the coating can effectively reduce the size of micropores and increase its thickness,whereas SiO_(2) nanoparticles with superior physical properties can be directly deposited at the discharge channel,significantly increasing the coating's resistance to wear and corrosion.The coating with SiO_(2) nanoparticles exhibits the best overall performance,with the lowest corrosion rate and average friction coefficient of 4.095×10^(-5)mm/a and 0.30,respectively.
基金supported by the National Key R&D Program of China(2021YFB3701100)the National Natural Science Foundation of China(52171101)the Fundamental Research Funds for the Central Universities(2024IAIS-QN009).
文摘Micro-arc oxidation(MAO)flm can only provide common mechanical protection for magnesium(Mg)–lithium(Li)alloys.These alloys are susceptible to severe localized corrosion,if the MAO flm is disrupted.This work reports the successful hydrothermal preparation of a MgLiAlCe-LDHs@GO flm on a MAO-coated Mg–Li alloy following Ce confnement.The graphene oxide(GO)sheet increased the difusion path of the corrosive media,and the addition of rare-earth cerium ions(Ce^(3+))endowed the flm with a certain self-healing ability,which signifcantly improved the corrosion resistance of the flm,and the corrosion current density(icorr)reached 3.27×10^(−8)A cm^(−2).The synergistic action of GO and Ce^(3+)can achieve long-term corrosion protection for the substrate.The corrosion resistance mechanism of MgLiAlCe-LDHs@GO flm was discussed by the scanning vibration electrode technique(SVET).
基金This work was supported by the National Natural Science Foundation of China(No.52001034)the China Postdoctoral Science Foundation(No.2023M731677)the Major Project of 2025 Sci&Tech Innovation of Ningbo(No.2020Z096).
文摘This research systematically examined the degradation,antibacterial effects,and biocompatibility of micro-arc oxidation(MAO)coatings with nano CuO and ZnO on extruded Mg alloys.Both copper(Cu)and Zinc(Zn)possess antibacterial properties.The findings demonstrated that adding ZnO will appreciably reduce the degradation rate of MAO-coating alloy due to the self-sealing micro holes.CuO+MAO coating exhibited excellent antibacterial performance,with an antibacterial rate of over 90%within 6 h co-cultured with Staphylococcus aureus.Similarly,the antibacterial rate of ZnO+MAO coating reached 90%after 12 h co-culture.Cytotoxicity test using MG63 cell indicated that the incorporation of CuO and ZnO did not notably affect the cell viability rate of the coating.Moreover,after 14 days of culture,the CuO+MAO and ZnO+MAO coated samples exhibited higher alkaline phosphatase(ALP)activity than the MAO-coated and uncoated samples,suggesting favorable osteogenic properties.
基金Funded by the National Natural Science Foundation of China (No. 51905506)。
文摘Oxide ceramic coatings were fabricated on tantalum alloys by micro-arc oxidation (MAO) to improve their hardness and tribological properties. The MAO coatings were manufactured in a mixed silicatephosphate electrolyte containing NaF and/or EDTA (ethylene diamine tetraacetic acid). The surface morphology,cross-sectional view, chemical composition, hardness, and wear performance of the coatings were analysed. As revealed by the scanning electron microscopy, silica-rich nodules appear on the MAO coating obtained in the silicate-phosphate electrolyte, but the formation of nodules is inhibited with NaF and/or EDTA in the electrolyte.Also, they reduce the roughness and improve the compactness of the coatings, which are composed of Ta_(2)O_(5),(Ta, O), and TaO. A thick and hard coating is obtained in the NaF-containing electrolyte, and the tribology performance is effectively improved. With additives, the nodule structure is detached from the coating surface and dissolved in the electrolyte. By using NaF as an electrolyte additive, the abrasion performance of the MAO coating is enhanced by decreasing the nodule structure, increasing the size of micropores, and improving the coating hardness.
基金Projects(41827805,41976044)supported by the National Natural Science Foundation of ChinaProject(ZDYF2021GXJS210)supported by the Hainan Provincial Science and Technology Special Fund,China+2 种基金Project(2021CXLH0005)supported by the Hainan Provincial Joint Project of Sanya Yazhou Bay Science and Technology City,ChinaProject(2021WHZZB2301)supported by the Wenhai Program of the S&T Fund of Shandong Province for Pilot National Laboratory for Marine Science and Technology,ChinaProject(121311KYSB20210005)supported by the Overseas Science and Education Centers of Bureau of International Cooperation Chinese Academy of Sciences。
文摘Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.
基金Project(51371039)supported by the National Natural Science Foundation of China
文摘The microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy obtained in silicate-,borate- and aluminate-based electrolyte without and with nanoadditive Al2O3 and TiO2 by micro-arc oxidation（MAO） were studied by scanning electron microscopy（SEM）,energy-dispersive X-ray spectroscopy（EDS）,X-ray diffraction（XRD）,microhardness and friction-abrasion tests,respectively.SEM results show that coatings with nanoadditive have less porosities than those without nanoadditive.XRD results reveal that nanoadditive-containing coatings contain more oxides compared with nanoadditive-free coatings in all cases,which are consistent with the EDS analysis.Mechanical properties tests show that nanoadditive Al2O3-containing coatings have higher microhardness values compared with the other coatings obtained in silicate-,borate- and aluminate-based electrolyte.On the other hand,nanoadditive has a positive effect on improving the wearing-resistance of MAO coatings in all cases.Furthermore,the borate-MAO coatings present an inferior anti-wearing property compared with the silicate- and aluminate-MAO coatings for both the nanoadditive-free and nanoadditive-containing coatings.
基金Project (BE2011778) supported by Science and Technology Support Program of Jiangsu Province,ChinaProjects (CityU 112510,112212) supported by Hong Kong Research Grants Council (RGC) General Research Funds (GRF) ,China
文摘Magnesium alloy wires were processed by micro-arc oxidation （MAO） in a modified silicate-phosphate composite electrolyte containing hydroxyapatite （HA） nanopowders and NaOH. Effects of NaOH content in the composite electrolyte on the microstructure and properties of the MAO ceramic coatings on magnesium alloy wires were studied. It is found that the arc voltage of magnesium alloy wires in the micro-arc oxidation process is significantly reduced while the oxidation rate is accelerated. Addition of 2 g/L NaOH in the composite electrolyte is a better choice for improving corrosion resistance of magnesium alloy wires. During early simulated body fluids （SBF） immersion, the micro-arc oxidized magnesium alloy wires undergo a slow and stable degradation. After soaking for 28 d, the protective ceramic coating still shows no damage but significant degradation is observed for magnesium alloy wires after immersion for more than 60 d.
基金Project (2007CB613700) supported by the National Basic Research Program of ChinaProject supported by Research Program of Excellent Scholars Studying Abroad of Ministry of Human Resources and Social Security,China
文摘Ceramic oxide coatings were prepared on AZ91D magnesium alloys in alkaline silicate solution using micro-arc oxidation（MAO） technique.The corrosion behavior of MAO coating on AZ91D magnesium alloys in NaCl solutions with different concentrations（0.1%,0.5%,1.0%,3.5% and 5.0% in mass fraction） was evaluated by electrochemical measurements and immersion tests.The results showed that the corrosion rate of the MAO coated AZ91D increased with increasing chloride ion concentration.The main form of corrosion failure was localized corrosion for the MAO coated AZ91D immersed in higher concentration NaCl solutions（1.0%,3.5% and 5.0%）,while it was general corrosion in dilute NaCl solutions（0.1% and 0.5%）.Two different stages of the failure process of the MAO coated AZ91D could be identified：1） occurrence of the metastable pits and 2） growth of the pits.Different equivalent circuits were also proposed based on the results of electrochemical impedance spectroscopy（EIS） for the MAO coated AZ91D immersed in different concentrations of NaCl solutions for 120 h.
文摘Ceramic coatings were fabricated on aluminum doped with different concentrations of TiO2 nano-additive. alloy substrates by micro-arc oxidation （MAO） in silicate electrolytes Effects of nano-additive concentration on the structural and mechanical properties of the MAO coatings were analyzed. The results revealed that some nano-particle were incorporated into the resulting coating during the MAO process, while there was a reasonable concentration for the TiO2 nano-additive. With increasing the nano-additive concentration to 3.2 g/L, the adhesion value increased, while mean friction coefficient and mass loss decreased. A further increase of nano-additive deteriorated the adhesion and mean friction coefficient values, which was consistent with the micro-hardness tests.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
基金Project(JSAWT-09-02)supported by the Key Laboratory of Advanced Welding Technology of Jiangsu Province,ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘Micro-arc oxidation （MAO） process was carried out in a dual electrolyte system of NaAlO 2 and Na 3 PO 4 to develop compact, smooth and corrosion-resistant coatings on ZK60 Mg alloy by single factor experiments. The microstructural characteristics of coatings were investigated by X-ray diffractometry （XRD） and scanning electron microscopy （SEM） coupled with energy dispersive X-ray spectroscopy （EDS）. Test of mass loss was conducted at a 3.5% NaCl solution to assess the resistance to corrosion. The effect of every element in the dual electrolyte system on voltage—time responses during MAO process and the coating characteristic were also analyzed and discussed systematically via single factor experiments. The results reveal that the main components of NaAlO 2 and Na 3 PO 4 as well as additives of NaOH, NaB4O7 and C6H5Na3O7 demonstrate different effects on MAO process and coating characteristics. By means of single factor experiments, an optimized dual electrolyte system was developed, containing 17.5 g/L NaAlO 2, 5.0 g/LNa3 PO4, 5.0 g/L NaOH, 3.0 g/L NaB4O7 and 4.2g/LC6H5Na3O7 .
基金Project (gf200901002) support by the National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘A composite ceramic coating containing Y2O3-ZrO2-MgO（YSZ-MgO） was prepared on AZ91D magnesium alloy,which was immersed in Y（NO3）3 aqueous solution as pretreatment,by micro-arc oxidation（MAO） process.The morphology,elemental and phase compositions,corrosion behavior and thermal stability of the coatings were studied by SEM,EDX,XRD,electrochemical corrosion test,high temperature oxidation and thermal shock test.The results show that the coating mainly consists of ZrO2,Y2O3,MgO,Mg2SiO4,and MgF2.Among these compounds,Y2O3 accounts for 26.7% of（Y2O3 ＋ ZrO2）.The thickness of YSZ-MgO coating is smaller than that of ZrO2-MgO coating,but its compactness and surface roughness are better than those of ZrO2-MgO coating.YSZ-MgO coating has a good corrosion resistance,and its corrosion rate in 5% NaCl aqueous solution is lower than that of ZrO2-MgO and only about 8.5% of that of AZ91D magnesium alloy.After oxidation at 410 °C,the mass gain of AZ91D magnesium alloy presents a linear increase with the oxidation time.The YSZ-MgO coating and ZrO2-MgO coating can remarkably decrease the oxidation mass gain.The oxidation mass gain of YSZ-MgO coating is lower than that of ZrO2-MgO coating,especially during a long oxidation period.The thermal shock resistance of YSZ-MgO coating is superior to ZrO2-MgO coating.
基金Project (2005CB623904) supported by the National Basic Research Program of ChinaProject (30770586) supported by the National Natural Science Foundation of China+1 种基金Project (31011120049) supported by the Australia-China special fund, International Science Linkages Program co-supported by the Department of Innovation, Industry, Science and Research of Australia, and the Ministry of Science and Technology and National Science Foundation of ChinaProject (2010ZDKG-96) supported by the major Subject of "13115" Programs of Shaan’xi Province, China
文摘A layer of porous film containing Ca and P was prepared by the micro-arc oxidation method on the surface of a novel near β biomedical Ti-3Zr-2Sn-3Mo-25Nb alloy, and then NH2- active group was introduced to the films by activation treatment. The phase composition, surface micro-topography and elemental characteristics of the micro-arc oxidation films were investigated with XRD, SEM, EDS and XPS, and the osteoinduction of the micro-arc oxidation films was tested using the simulated body fluid immersion, the in-vitro osteoblast cultivation test and animal experiment. The results show that the oxide layer is a kind of porous ceramic intermixture and contains Ca and P. The films in the simulated body fluid can induce apatite formation, resulting in excellent bioactivity. The cell test discovers that osteoblasts can grow well on the surface of micro-arc oxidation films. And the Ti-3Zr-2Sn-3Mo-25Nb biomedical alloy coated with active porous calcium-phosphate films shows better osteoinduction in vivo.
基金Project(2014RC18)supported by Talent Introduction Funds of the Sichuan University of Science and Engineering,ChinaProject(2013CL01)supported by the Opening Project of the Material Corrosion and Protection Key Laboratory of Sichuan Province,ChinaProject(2013X06)supported by the Science and Technology Planning Project of Zigong City,China
文摘A hydrophobic surface was fabricated on a micro-arc oxidation (MAO) treated AZ31 Mg alloys via surface modification with myristic acid. The effects of modification time on the wettability of the coatings were investigated using the contact angle measuring device. The surface morphologies and structure of the coatings were evaluated using SEM, XRD and FT-IR. The corrosion resistance was investigated by potentiodynamic polarization curves and long-term immersion test. The results showed that the water contact angle (CA) increases gradually with modification time from 0 to 5 h, the highest CA reaches 138° after being modified for 5 h, and the number and size of the micro pores are decreased. The modification method hardly alters crystalline structure of the MAO coating, but improves the corrosion resistance based on the much positive potential and low current density. Moreover, the corrosion resistance and hydrophobicity can be enhanced with increasing the alkyl chain. The wetting and spreading for the alkylcarboxylate with low surface energy become easier on the micro-porous surface, and alkylcarboxylate monolayer will be formed through bidentate bonding, which changes the surface micropores to a sealing or semi-sealing structure and makes the MAO coating dense and hydrophobic. All the results demonstrate that the modification process improves the corrosion protection ability of the MAO coating on AZ31B Mg alloy.
基金supported by the National Natural Science Foundation of China(Nos.51571134 and 51601108)the SDUST Research Fund(No.2014TDJH104)
文摘One of the major obstacles for the clinical use of biodegradable magnesium(Mg)-based materials is their high corrosion rate. Micro-arc oxidation(MAO) coatings on Mg alloys provide mild corrosion protection owing to their porous structure. Hence, in this study a dense Mg(OH)2 film was fabricated on MAO-coated Mg alloy AZ31 in an alkaline electrolyte containing ethylenediamine tetraacetic acid disodium(EDTA-2 Na) to reinforce the protection. Surface morphology, chemical composition and growth process of the MAO/Mg(OH)2 hybrid coating were examined using field-emission scanning electron microscopy, energy dispersive X-ray spectrometer, X-ray diffraction, X-ray photoelectron spectroscopy and Fourier transform infrared spectrophotometer. Corrosion resistance of the coatings was evaluated via potentiodynamic polarization curves and hydrogen evolution tests. Results manifested that the Mg(OH)2 coating possesses a porous nano-sized structure and completely seals the micro-pores and micro-cracks of the MAO coating.The intermetallic compound of AlMn phase in the substrate plays a key role in the growth of Mg(OH)2 film. The current density of Mg(OH)2-MAO composite coating decreases three orders of magnitude in comparison with that of bare substrate, indicating excellent corrosion resistance. The Mg(OH)2-MAO composite coating is beneficial to the formation of calcium phosphate corrosion products on the surface of Mg alloy AZ31, demonstrating a great promise for orthopaedic applications.
文摘Ceramic coatings were prepared on AZ91 D Mg alloy by micro-arc oxidation （MAO） in aluminate electrolytes, with Al2O3 nano-additive suspending at different concentrations. Effects of nano-additive concentration on the structure, phase composition, hardness and anti-corrosion property of the MAO coatings were analyzed by scanning electron microscopy, X-ray diffraction, micro-hardness test and electrochemical method, respectively. The results revealed that Al2O3 nano-particles were mostly incorporated into ceramic coating chemically, transferred into MgAl2O4, rather than being trapped mechanically during MAO process. With the increase of Al2O3 concentration, the voltage-time response, content of MgAl2O4, hardness and anti-corrosion property increased. However, when the concentration varied from 10 g/L to 15 g/L, these behaviors and properties changed only a little. This result indicated that, after the concentration of Al2O3 nano-additive reaching 10 g/L, the incorporation of Al2O3 nano-particles turned into a saturation state, due to the complex process during MAO treatment. Therefore, 10 g/L might be a proper concentration for MAO coating to incorporate Al2O3 nano-particles,
文摘Magnesium and its alloys have been used in many industries, but they are reactive and require protection against aggressive environments. In this study, oxide coatings were applied on AZ91D magnesium alloy using micro-arc oxidation （MAO） process. Then, in order to seal the pores of the MAO coatings, the samples were immersed in cerium bath for different times. The surface morphologies and compositions of the coatings were analyzed by scanning electron microscopy （SEM） and X-ray energy dispersive spectroscopy （EDS）, respectively. The corrosion behavior of the coatings was investigated with electrochemical impedance spectroscopy （EIS） and potentiodynamic polarization tests in 3.5 wt.% NaCl solution. The amount of the porosity of the coating was measured by electrochemical method. It was found that the sealing treatments by immersion in cerium bath successfully sealed the pores of the MAO coatings. The results of the corrosion tests showed that the MAO coating which was sealed in Ce bath for 10 min enhanced the corrosion resistance of the substrate significantly. Furthermore, this coating had the lowest amount of the porosity among the coatings.
基金Project supported by the Natioanl Defence Major Safety Foundation of China (6133002B2008)
文摘The regulation of ceramic coating formed by micro-arc oxidation on Mg-11Gd-1Y-0.5Zn (wt.%) magnesium alloys was investigated by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The relation of phase structure and corrosion resistance of MgO coating formed by micro-arc oxidation in different growth stages was analyzed. The results showed that the growth of coating accorded with linear regularity in the initial stage of micro-arc oxidation, which was the stage of anodic oxidation controlled ...
基金Jilin Provincial Science & Technology Department for supporting this research under contract number 20080505
文摘To improve the surface wear resistance of the ceramic coating fabricated by micro-arc oxidation （MAO） on AZ91D magnesium alloy,ceramic coatings embedded with SiC nano-particles at different current frequency （500 Hz,700 Hz,and 900 Hz） were produced during the MAO process.The morphology and phase composition of the coatings were investigated by scanning electron microscopy （SEM）,field emission scanning electron microscopy （FESEM）,and X-ray diffraction （XRD）.The surface roughness of the coatings was characterized by confocal laser scanning microscopy （CLSM）.Simultaneously,the tribological properties of the composite coatings were evaluated by using a universal materials tester （UMT）.The results shows that the wear resistance of the ceramic coatings with SiC nano-particles was improved significantly compared to the ceramic coatings without SiC nano-particles.Furthermore,the composite coating formed at current frequency 900 Hz showed the better wear resistance than the others.