Mechanochemical synthesis has been applied for many novel material preparations and gained more and more attention due to green and high-efficiency recently. In order to explore the influences of iron precursors on st...Mechanochemical synthesis has been applied for many novel material preparations and gained more and more attention due to green and high-efficiency recently. In order to explore the influences of iron precursors on structure and performance of iron molybdate catalyst prepared by mechanochemical route, three typical and cheap iron precursors have been used in preparation of iron molybdate catalyst. Many characterization methods have been employed to obtain the physical and chemical properties of iron molybdate catalyst. Results indicate that iron precursors have the significant impact on the phase composition, crystal morphology and catalytic performance in the conversion of methanol to formaldehyde. It is hard to regulate the phase composition by changing Mo/Fe mole ratios for Fe2(SO4)3 as iron precursor. In addition, as for Fe2(SO4)3, the formaldehyde yield is lower than that from iron molybdate catalyst prepared with Fe(NO3)3·9H2O due to the reduction in Fe2(MoO4)3 phase as active phase. Based on mechanochemical and coprecipitation method, the solvent water could be a key factor for the formation of MoO3 and Fe2(MoO4) for FeCl3·6H2O and Fe2(SO4)3 as precursors. Iron molybdate catalyst prepared with Fe(NO3)3·9H2O by mechanochemical route, shows the best methanol conversion and formaldehyde yield in this reaction.展开更多
The effect of the precursor composition of fused iron catalyst on the performance of Fischer-Tropsch synthesis was investigated. XRD, BET and CO2 adsorption experiments were carried out to provide better insight into ...The effect of the precursor composition of fused iron catalyst on the performance of Fischer-Tropsch synthesis was investigated. XRD, BET and CO2 adsorption experiments were carried out to provide better insight into the relationship therein. The results showed that the selectivity of C5＋ hydrocarbon products was dependent on the mole ratio of Fe^2＋/Fe^3＋, which was represented by a hump-shaped curve. Catalysts with precursors containing Fe3O4 phase favored the magnetite spinal formation during F-T reaction, while Fe（1-x）O-based catalysts were more likely to favor the formation and growth of the iron carbide crystals.展开更多
Two types of small iron clusters supported on γ-Al2O3-RT（dehydroxylated at room temperature） and γ-Al2O3-800 （dehydroxylated at 800 ℃） were prepared by solvated metal atom impregnation （SMAI） techniques. The ...Two types of small iron clusters supported on γ-Al2O3-RT（dehydroxylated at room temperature） and γ-Al2O3-800 （dehydroxylated at 800 ℃） were prepared by solvated metal atom impregnation （SMAI） techniques. The iron atom precursor complex, bis（toluene）iron（0） formed in the metal atom reactor, was impregnated into γ-Al2O3 having different concentrations of surface hydroxyl groups to study the effect of surface hydroxylation on the crucial stage of iron cluster formation. Catalysts prepared in this way were characterized by TEM, Mǒssbauer, and chemisorption measurements, and the results show that higher concentration of surface hydroxyl groups of γ-Al2O3-RT favors the formation of more positively charged supported iron cluster Fen/γ-Al2O3-RT, and the lower concentration of surface hydroxyl groups of γ-Al2O3-800 favors the formation of basically neutral supported iron cluster Fen/γ-Al2O3-800. The measured results also indicate that the higher concentration of surface hydroxyl groups causes the rapid decomposition of precursor complex, bis（toluene）iron（0）, and favors the formation of relatively large iron cluster. Consequently, these two types of catalysts show different catalytic properties in Fischer-Tropsch reaction. The catalytic pattern of Fen/γ-Al2O3-RT in F-T reaction is similar to that of the unreduced γ-Fe2O3 and that of Fen/γ-Al2O3-800 is similar to that of the reduced α-Fe2O3.展开更多
基金supported by the Chang Jiang Scholars Programme of China, the Key research and development project of Xinjiang Uygur Autonomous Region (2017B02012)the Natural Science Foundation of Xinjiang University (BS62331)the Xinjiang Uygur Autonomous Region 100 Young Doctors Introduction Program。
文摘Mechanochemical synthesis has been applied for many novel material preparations and gained more and more attention due to green and high-efficiency recently. In order to explore the influences of iron precursors on structure and performance of iron molybdate catalyst prepared by mechanochemical route, three typical and cheap iron precursors have been used in preparation of iron molybdate catalyst. Many characterization methods have been employed to obtain the physical and chemical properties of iron molybdate catalyst. Results indicate that iron precursors have the significant impact on the phase composition, crystal morphology and catalytic performance in the conversion of methanol to formaldehyde. It is hard to regulate the phase composition by changing Mo/Fe mole ratios for Fe2(SO4)3 as iron precursor. In addition, as for Fe2(SO4)3, the formaldehyde yield is lower than that from iron molybdate catalyst prepared with Fe(NO3)3·9H2O due to the reduction in Fe2(MoO4)3 phase as active phase. Based on mechanochemical and coprecipitation method, the solvent water could be a key factor for the formation of MoO3 and Fe2(MoO4) for FeCl3·6H2O and Fe2(SO4)3 as precursors. Iron molybdate catalyst prepared with Fe(NO3)3·9H2O by mechanochemical route, shows the best methanol conversion and formaldehyde yield in this reaction.
文摘The effect of the precursor composition of fused iron catalyst on the performance of Fischer-Tropsch synthesis was investigated. XRD, BET and CO2 adsorption experiments were carried out to provide better insight into the relationship therein. The results showed that the selectivity of C5＋ hydrocarbon products was dependent on the mole ratio of Fe^2＋/Fe^3＋, which was represented by a hump-shaped curve. Catalysts with precursors containing Fe3O4 phase favored the magnetite spinal formation during F-T reaction, while Fe（1-x）O-based catalysts were more likely to favor the formation and growth of the iron carbide crystals.
文摘Two types of small iron clusters supported on γ-Al2O3-RT（dehydroxylated at room temperature） and γ-Al2O3-800 （dehydroxylated at 800 ℃） were prepared by solvated metal atom impregnation （SMAI） techniques. The iron atom precursor complex, bis（toluene）iron（0） formed in the metal atom reactor, was impregnated into γ-Al2O3 having different concentrations of surface hydroxyl groups to study the effect of surface hydroxylation on the crucial stage of iron cluster formation. Catalysts prepared in this way were characterized by TEM, Mǒssbauer, and chemisorption measurements, and the results show that higher concentration of surface hydroxyl groups of γ-Al2O3-RT favors the formation of more positively charged supported iron cluster Fen/γ-Al2O3-RT, and the lower concentration of surface hydroxyl groups of γ-Al2O3-800 favors the formation of basically neutral supported iron cluster Fen/γ-Al2O3-800. The measured results also indicate that the higher concentration of surface hydroxyl groups causes the rapid decomposition of precursor complex, bis（toluene）iron（0）, and favors the formation of relatively large iron cluster. Consequently, these two types of catalysts show different catalytic properties in Fischer-Tropsch reaction. The catalytic pattern of Fen/γ-Al2O3-RT in F-T reaction is similar to that of the unreduced γ-Fe2O3 and that of Fen/γ-Al2O3-800 is similar to that of the reduced α-Fe2O3.