Thermoelectric properties of spark-plasma-sintering prepared bulk materials EuxNay□zSn1–x–y–zTe above room temperature were investigated. The implementation of Eu and Na into the SnTe lattice was monitored by refi...Thermoelectric properties of spark-plasma-sintering prepared bulk materials EuxNay□zSn1–x–y–zTe above room temperature were investigated. The implementation of Eu and Na into the SnTe lattice was monitored by refinement of lattice parameters as well as energy dispersive X-ray spectroscopy（EDXS）. The binary SnTe achieved the highest ZT value of 0.63 at 786 K, and showed a hole concentration of 4.6′10^19 cm^–3 at 300 K. In comparison with pristine SnTe, the samples containing Eu had lower carrier mobility but higher Hall carrier concentration. For Eu- and Na-substituted samples, the increased hole concentration was unfavorable for the improvement of thermoelectric properties.展开更多
基金supported by Young Eastern Scholar Project of Shanghai Municipal Education Commission(QD2015031)
文摘Thermoelectric properties of spark-plasma-sintering prepared bulk materials EuxNay□zSn1–x–y–zTe above room temperature were investigated. The implementation of Eu and Na into the SnTe lattice was monitored by refinement of lattice parameters as well as energy dispersive X-ray spectroscopy（EDXS）. The binary SnTe achieved the highest ZT value of 0.63 at 786 K, and showed a hole concentration of 4.6′10^19 cm^–3 at 300 K. In comparison with pristine SnTe, the samples containing Eu had lower carrier mobility but higher Hall carrier concentration. For Eu- and Na-substituted samples, the increased hole concentration was unfavorable for the improvement of thermoelectric properties.