The effect of graft yield on both the thermo-responsive hydraulicpermeability and the therrno-responsive diffusional permeability through porous membranes withplasma-grafted poly(N-isopropylacrylamide) (PNIPAM) gates ...The effect of graft yield on both the thermo-responsive hydraulicpermeability and the therrno-responsive diffusional permeability through porous membranes withplasma-grafted poly(N-isopropylacrylamide) (PNIPAM) gates was investigated. Both thermo-responsiveflat membranes and core-shell microcapsule membranes with a wide range of graft yield of PNIPAM wereprepared using a plasma-graft pore-filling polymerization method. The grafted PNIPAM was formedhomogeneously throughout the entire thickness of both the flat polyethylene membranes and themicrocapsule polyamide membranes. Both the hydraulic permeability and the diffusional permeabilitywere heavily dependent on the PNIPAM graft yield. With increasing the graft yield, the hydraulicpermeability (water flux) decreases rapidly at 25℃ because of the decrease of the pore size;however, the water flux at 40℃ increases firstly to a peak because of the increase ofhydrophobicity of the pore surface, and then decreases and finally tends to zero because of the poresize becoming smaller and smaller. For the diffusional permeability, the temperature showsdifferent effects on the diffusional permeability coefficients of solutes across the membranes. Whenthe graft yield was low, the diffusional coefficient of solute across the membrane was higher attemperature above the lower critical solution temperature (LCST) than that below the LCST; however,when the graft yield was high, the diffusional coefficient was lower at temperature above the LCSTthan that below the LCST. It is very important to choose or design a proper graft yield of PNIPAMfor obtaining a desired thermo-responsive 'on/off' hydraulic or diffusional permeability.展开更多
Radiation induced grafting of various polymers with different monomers proved to be an attractive means to modify the physical or chemical properties of polymeric materials or textile fabrics. In the present work, rad...Radiation induced grafting of various polymers with different monomers proved to be an attractive means to modify the physical or chemical properties of polymeric materials or textile fabrics. In the present work, radiation induced grafting of viscose rayon fabrics, consisting mainly of cellulose fibers, with acrylic acid monomer has been carried out. The grafting yields have been thoroughly studied as a function of different applied experimental parameters. The impact of the graft yield on the physical properties of the fabrics such as tensile strength, elongation, swelling, moisture absorption, crease recovery angle and also the dyeing properties of the fabrics has been studied. The effect of increasing the contact time of the fabric and monomer solution, at room temperature, after stopping irradiation has been studied in detail as well as the effect of temperature on the irradiated samples also after stopping irradiation. The best grafting yield was obtained on irradiating viscose rayon fabric in methanol-water solvent containing acrylic acid monomer, at a dose 20 kGys, then heating for 7 hours at 80℃ and finally keeping the samples at room temperature for about 20 hours. That treatment significantly increased the final graft yield.展开更多
In the present work, graft copolymerization of polyacrylonitrile onto chitosan has been carried out in the presence of ceric ammonium nitrate redox initiator. Optimization of grafting of polyacrylonitrile onto chito-s...In the present work, graft copolymerization of polyacrylonitrile onto chitosan has been carried out in the presence of ceric ammonium nitrate redox initiator. Optimization of grafting of polyacrylonitrile onto chito-san was performed by varying the process parameters such as ceric ammonium nitrate (CAN) concentration, polyacrylonitrile concentration and reaction time to study their influence on percent grafting and grafting ef-ficiency. The optimum reaction conditions obtained for grafting of acrylonitrile onto chitosan were reaction time 55 mins, CAN concentration 1% in Con. HNO3, and polyacrylonitrile concentration 0.75 mol/L. The characterization of the grafted products by means of FTIR, thermal analysis, X-ray diffraction and scanning electron microscopy furnished the evidence of grafting of polyacrylonitrile onto chitosan.展开更多
在同向双螺杆挤出机中通过熔融接枝反应制备了EPM g GMA ,将其与PBT在转矩流变仪中熔融共混可以获得增韧的PBT工程塑料 .实验中EPM g GMA接枝率的测定采用红外工作曲线法 ,选用CCl4 做溶剂以避免溶剂对样品吸收峰的干扰 .随着EPM g GMA...在同向双螺杆挤出机中通过熔融接枝反应制备了EPM g GMA ,将其与PBT在转矩流变仪中熔融共混可以获得增韧的PBT工程塑料 .实验中EPM g GMA接枝率的测定采用红外工作曲线法 ,选用CCl4 做溶剂以避免溶剂对样品吸收峰的干扰 .随着EPM g GMA接枝率的增加 ,PBT EPM g GMA的缺口冲击强度相应提高 ,共混物中EPM g GMA的粒径尺寸减小 ,当EPM g GMA的接枝率为 4 7mL 1 0 0gEPM时 ,EPM g GMA的粒径尺寸可达 0 5 μm ,PBT EPM g GMA的缺口冲击强度达到 5 1 6kJ m2 ,是纯PBT的 3展开更多
基金Supported by the National Natural Science Foundation of China(No.29876022).
文摘The effect of graft yield on both the thermo-responsive hydraulicpermeability and the therrno-responsive diffusional permeability through porous membranes withplasma-grafted poly(N-isopropylacrylamide) (PNIPAM) gates was investigated. Both thermo-responsiveflat membranes and core-shell microcapsule membranes with a wide range of graft yield of PNIPAM wereprepared using a plasma-graft pore-filling polymerization method. The grafted PNIPAM was formedhomogeneously throughout the entire thickness of both the flat polyethylene membranes and themicrocapsule polyamide membranes. Both the hydraulic permeability and the diffusional permeabilitywere heavily dependent on the PNIPAM graft yield. With increasing the graft yield, the hydraulicpermeability (water flux) decreases rapidly at 25℃ because of the decrease of the pore size;however, the water flux at 40℃ increases firstly to a peak because of the increase ofhydrophobicity of the pore surface, and then decreases and finally tends to zero because of the poresize becoming smaller and smaller. For the diffusional permeability, the temperature showsdifferent effects on the diffusional permeability coefficients of solutes across the membranes. Whenthe graft yield was low, the diffusional coefficient of solute across the membrane was higher attemperature above the lower critical solution temperature (LCST) than that below the LCST; however,when the graft yield was high, the diffusional coefficient was lower at temperature above the LCSTthan that below the LCST. It is very important to choose or design a proper graft yield of PNIPAMfor obtaining a desired thermo-responsive 'on/off' hydraulic or diffusional permeability.
文摘Radiation induced grafting of various polymers with different monomers proved to be an attractive means to modify the physical or chemical properties of polymeric materials or textile fabrics. In the present work, radiation induced grafting of viscose rayon fabrics, consisting mainly of cellulose fibers, with acrylic acid monomer has been carried out. The grafting yields have been thoroughly studied as a function of different applied experimental parameters. The impact of the graft yield on the physical properties of the fabrics such as tensile strength, elongation, swelling, moisture absorption, crease recovery angle and also the dyeing properties of the fabrics has been studied. The effect of increasing the contact time of the fabric and monomer solution, at room temperature, after stopping irradiation has been studied in detail as well as the effect of temperature on the irradiated samples also after stopping irradiation. The best grafting yield was obtained on irradiating viscose rayon fabric in methanol-water solvent containing acrylic acid monomer, at a dose 20 kGys, then heating for 7 hours at 80℃ and finally keeping the samples at room temperature for about 20 hours. That treatment significantly increased the final graft yield.
文摘In the present work, graft copolymerization of polyacrylonitrile onto chitosan has been carried out in the presence of ceric ammonium nitrate redox initiator. Optimization of grafting of polyacrylonitrile onto chito-san was performed by varying the process parameters such as ceric ammonium nitrate (CAN) concentration, polyacrylonitrile concentration and reaction time to study their influence on percent grafting and grafting ef-ficiency. The optimum reaction conditions obtained for grafting of acrylonitrile onto chitosan were reaction time 55 mins, CAN concentration 1% in Con. HNO3, and polyacrylonitrile concentration 0.75 mol/L. The characterization of the grafted products by means of FTIR, thermal analysis, X-ray diffraction and scanning electron microscopy furnished the evidence of grafting of polyacrylonitrile onto chitosan.