Investigation has been made on the causes of hot cracking in the surfacing layer of Ni_3Al basealloy by analysing the solidification process of fusion pool and the distribution of thermal stresses. The re-sults show t...Investigation has been made on the causes of hot cracking in the surfacing layer of Ni_3Al basealloy by analysing the solidification process of fusion pool and the distribution of thermal stresses. The re-sults show that the cracking is directly related to both the occurrence of eutectic phase β' (NiAI) within theinterdendritic region and high thernial stresses in the surfacing layer ,and which are caused by selecting highwelding rate. When the process of electric arc weld is changed from straight line rnovement to that along’Z’pattern,the cracking in the surfacing layer of Ni_3Al base alloy is prevented owing to being reduced of boththe cooling rate of liquid in the fusion liool and the speed of the moving heat source. Lowering the outputpower of the electric arc welding could lead to the reducing of rnelting volume of the base material ,and lowerthe arnount of iron atoms dissolving in the fusion pool ,so that the trend of the eutectic reaction within the in-terdendritic region is reduced,and which is helpful to suppress the cracking in the surfacing layer of Ni_3Albase alloy.展开更多
基金supported by the foundation of '863' high technology in China
文摘Investigation has been made on the causes of hot cracking in the surfacing layer of Ni_3Al basealloy by analysing the solidification process of fusion pool and the distribution of thermal stresses. The re-sults show that the cracking is directly related to both the occurrence of eutectic phase β' (NiAI) within theinterdendritic region and high thernial stresses in the surfacing layer ,and which are caused by selecting highwelding rate. When the process of electric arc weld is changed from straight line rnovement to that along’Z’pattern,the cracking in the surfacing layer of Ni_3Al base alloy is prevented owing to being reduced of boththe cooling rate of liquid in the fusion liool and the speed of the moving heat source. Lowering the outputpower of the electric arc welding could lead to the reducing of rnelting volume of the base material ,and lowerthe arnount of iron atoms dissolving in the fusion pool ,so that the trend of the eutectic reaction within the in-terdendritic region is reduced,and which is helpful to suppress the cracking in the surfacing layer of Ni_3Albase alloy.