Additive manufacturing (AM) of high-strength metallic alloys frequently encounters detrimental distortion and cracking, attributed to the accumulation of thermal stresses. These issues significantly impede the practic...Additive manufacturing (AM) of high-strength metallic alloys frequently encounters detrimental distortion and cracking, attributed to the accumulation of thermal stresses. These issues significantly impede the practical application of as-printed components. This study examines the Mg-15Gd-1Zn-0.4Zr (GZ151K, wt.%) alloy, a prototypical high-strength casting Mg-RE alloy, fabricated through laser powder bed fusion (LPBF). Despite achieving ultra-high strength, the GZ151K alloy concurrently exhibits a pronounced cold-cracking susceptibility. The as-printed GZ151K alloy consists of almost fully fine equiaxed grains with an average grain size of merely 2.87 µm. Subsequent direct aging (T5) heat treatment induces the formation of dense prismatic β' precipitates. Consequently, the LPBF-T5 GZ151K alloy manifests an ultra-high yield strength of 405 MPa, surpassing all previously reported yield strengths for Mg alloys fabricated via LPBF and even exceeding that of its extrusion-T5 counterpart. Interestingly, as-printed GZ151K samples with a build height of 2 mm exhibit no cracking, whereas samples with build heights ranging from 4 to 18 mm demonstrate severe cold cracking. Thermal stress simulation also suggests that the cold cracking susceptibility increases significantly with increasing build height. The combination of high thermal stress and low ductility in the as-printed GZ151K alloy culminates in a high cold cracking susceptibility. This study offers novel insights into the intricate issue of cold cracking in the LPBF process of high-strength Mg alloys, highlighting the critical balance between achieving high strength and mitigating cold cracking susceptibility.展开更多
In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc wel...In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.展开更多
Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long li...Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X 70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The thickness of plate steel was 14.7 mm and 10.3 mm . The results reveal that X 70 pipeline steel has good crack resistance. The research has important value for the construction of large scale pipeline engineering and the application of domestic X 70 pipeline steel.展开更多
Cracking morphology in the fusion zone of HQ130 high strength steel was researched by 'the y-slit test' and 'three-point bend test', ultrasonic test and microscope. HQ130 and QJ63 high strength steel w...Cracking morphology in the fusion zone of HQ130 high strength steel was researched by 'the y-slit test' and 'three-point bend test', ultrasonic test and microscope. HQ130 and QJ63 high strength steel was welded by Ar+CO2 gas shielded arc welding under the condition without preheating. Experimental results indicated that welding cracks were produced in the partially melted zone of the weld root of HQ130 steel side and propagated parallel to the fusion zone. The cracks were developed alternatively between the weld and the partially melted zone, and are not strictly ruptured at W/F (weld metal/fusion zone) boundary surface. Controlling weld heat input (E) about 16 kJ/cm could make the cracking rate lowest and satisfy the performance requirement of welded joint zone.展开更多
Maximum hardness test in weld heat-affected zone（HAZ）,oblique Y-groove cracking test and mechanical property test of welding joint of 1 000 MPa grade ultra-low carbon bainitic steel were carried out,so as to researc...Maximum hardness test in weld heat-affected zone（HAZ）,oblique Y-groove cracking test and mechanical property test of welding joint of 1 000 MPa grade ultra-low carbon bainitic steel were carried out,so as to research the weldability of the steel.The results show that the steel has lower cold cracking sensitivity,and preheating temperature of 100 ℃ can help completely eliminate cold cracks,generating good process weldability.The increase of preheating temperature can reduce the hardening degree of heat-affected zone.The strength of welding joint decreases and hardness reduces when heat inputs increase,and excellent mechanical properties can be obtained when low welding heat inputs are used.Fine lath bainites of different orientations combined with a few granular bainites that effectively split the original coarse austenite grains are the foundation of good properties.展开更多
基金supported by the National Key Research and Development Program of China(No.2021YFB3701000)the National Natural Science Foundation of China(Nos.51971130,52201129,U21A2047,51821001,U2037601)+2 种基金support by the China Postdoctoral Science Foun-dation(2023M742219)the Postdoctoral Fellowship Program of CPSF under Grant Number GZB20240419support by the Ministry of Education,Singapore,under its Academic Research Fund Tier 2(MOE-T2EP50221-0013).
文摘Additive manufacturing (AM) of high-strength metallic alloys frequently encounters detrimental distortion and cracking, attributed to the accumulation of thermal stresses. These issues significantly impede the practical application of as-printed components. This study examines the Mg-15Gd-1Zn-0.4Zr (GZ151K, wt.%) alloy, a prototypical high-strength casting Mg-RE alloy, fabricated through laser powder bed fusion (LPBF). Despite achieving ultra-high strength, the GZ151K alloy concurrently exhibits a pronounced cold-cracking susceptibility. The as-printed GZ151K alloy consists of almost fully fine equiaxed grains with an average grain size of merely 2.87 µm. Subsequent direct aging (T5) heat treatment induces the formation of dense prismatic β' precipitates. Consequently, the LPBF-T5 GZ151K alloy manifests an ultra-high yield strength of 405 MPa, surpassing all previously reported yield strengths for Mg alloys fabricated via LPBF and even exceeding that of its extrusion-T5 counterpart. Interestingly, as-printed GZ151K samples with a build height of 2 mm exhibit no cracking, whereas samples with build heights ranging from 4 to 18 mm demonstrate severe cold cracking. Thermal stress simulation also suggests that the cold cracking susceptibility increases significantly with increasing build height. The combination of high thermal stress and low ductility in the as-printed GZ151K alloy culminates in a high cold cracking susceptibility. This study offers novel insights into the intricate issue of cold cracking in the LPBF process of high-strength Mg alloys, highlighting the critical balance between achieving high strength and mitigating cold cracking susceptibility.
基金Armament Research Board (ARMREB),New Delhi for funding this projectwork (Project No MAA/03/41)
文摘In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.
文摘Gas Transmitting From West to East Project' is significant. It should ensure the welding quality and safety of pipeline. The task is very arduous to guarantee the quality of the project in the condition of long line, complex weather and geology features. In this paper, the welding cold cracking susceptibility of domestic X 70 pipeline steel adopted by the project, which is one of the most interesting questions of welding quality about petrol pipeline, was studied by means of oblique Y groove cracking test. The crack ratio of surface and section was tested under the conditions of different welding materials and preheat temperature .The thickness of plate steel was 14.7 mm and 10.3 mm . The results reveal that X 70 pipeline steel has good crack resistance. The research has important value for the construction of large scale pipeline engineering and the application of domestic X 70 pipeline steel.
文摘Cracking morphology in the fusion zone of HQ130 high strength steel was researched by 'the y-slit test' and 'three-point bend test', ultrasonic test and microscope. HQ130 and QJ63 high strength steel was welded by Ar+CO2 gas shielded arc welding under the condition without preheating. Experimental results indicated that welding cracks were produced in the partially melted zone of the weld root of HQ130 steel side and propagated parallel to the fusion zone. The cracks were developed alternatively between the weld and the partially melted zone, and are not strictly ruptured at W/F (weld metal/fusion zone) boundary surface. Controlling weld heat input (E) about 16 kJ/cm could make the cracking rate lowest and satisfy the performance requirement of welded joint zone.
基金Item Sponsored by National Science and Technology Support Plan Project of China(2007BAE51B07)
文摘Maximum hardness test in weld heat-affected zone（HAZ）,oblique Y-groove cracking test and mechanical property test of welding joint of 1 000 MPa grade ultra-low carbon bainitic steel were carried out,so as to research the weldability of the steel.The results show that the steel has lower cold cracking sensitivity,and preheating temperature of 100 ℃ can help completely eliminate cold cracks,generating good process weldability.The increase of preheating temperature can reduce the hardening degree of heat-affected zone.The strength of welding joint decreases and hardness reduces when heat inputs increase,and excellent mechanical properties can be obtained when low welding heat inputs are used.Fine lath bainites of different orientations combined with a few granular bainites that effectively split the original coarse austenite grains are the foundation of good properties.