摘要
Cracking morphology in the fusion zone of HQ130 high strength steel was researched by 'the y-slit test' and 'three-point bend test', ultrasonic test and microscope. HQ130 and QJ63 high strength steel was welded by Ar+CO2 gas shielded arc welding under the condition without preheating. Experimental results indicated that welding cracks were produced in the partially melted zone of the weld root of HQ130 steel side and propagated parallel to the fusion zone. The cracks were developed alternatively between the weld and the partially melted zone, and are not strictly ruptured at W/F (weld metal/fusion zone) boundary surface. Controlling weld heat input (E) about 16 kJ/cm could make the cracking rate lowest and satisfy the performance requirement of welded joint zone.
Cracking morphology in the fusion zone of HQ130 high strength steel was researched by 'the y-slit test' and 'three-point bend test', ultrasonic test and microscope. HQ130 and QJ63 high strength steel was welded by Ar+CO2 gas shielded arc welding under the condition without preheating. Experimental results indicated that welding cracks were produced in the partially melted zone of the weld root of HQ130 steel side and propagated parallel to the fusion zone. The cracks were developed alternatively between the weld and the partially melted zone, and are not strictly ruptured at W/F (weld metal/fusion zone) boundary surface. Controlling weld heat input (E) about 16 kJ/cm could make the cracking rate lowest and satisfy the performance requirement of welded joint zone.