The flexural strength reliability of bulk metallic glasses （BMGs） plates is analyzed using Weibull statistics. The Weibull modulus （m） and characteristic strength （σ0） of the Zr48Cu45AI7 BMG are 34 and 2630 MPa...The flexural strength reliability of bulk metallic glasses （BMGs） plates is analyzed using Weibull statistics. The Weibull modulus （m） and characteristic strength （σ0） of the Zr48Cu45AI7 BMG are 34 and 2630 MPa, respectively, which are much higher than the values of fine ceramics （m 〈 30, σ0 〈 1600 MPa）. In particular, the m values obtained by flexural strength and compressive strength statistics of the Mg61Cu28Gd11 BMG are 5 and 33, respectively, indicating that the m values of BMGs are test method dependent, and only the m values obtained by flexural strength statistics can be used to make a convincible comparison with those of ceramics.展开更多
基金supported by the Zhejiang Provincial Natural Science Foundation of China(Grant No.Q12E010015)the Ningbo Municipal Natural Science Foundation(Grant No.2015A610074)
文摘The flexural strength reliability of bulk metallic glasses （BMGs） plates is analyzed using Weibull statistics. The Weibull modulus （m） and characteristic strength （σ0） of the Zr48Cu45AI7 BMG are 34 and 2630 MPa, respectively, which are much higher than the values of fine ceramics （m 〈 30, σ0 〈 1600 MPa）. In particular, the m values obtained by flexural strength and compressive strength statistics of the Mg61Cu28Gd11 BMG are 5 and 33, respectively, indicating that the m values of BMGs are test method dependent, and only the m values obtained by flexural strength statistics can be used to make a convincible comparison with those of ceramics.