TiB2/Al-30Si composites were fabricated via in-situ melt reaction under high-energy ultrasonic field. The microstructure and wear properties of the composite were investigated by XRD, SEM and dry sliding testing. The ...TiB2/Al-30Si composites were fabricated via in-situ melt reaction under high-energy ultrasonic field. The microstructure and wear properties of the composite were investigated by XRD, SEM and dry sliding testing. The results indicate that TiB2 reinforcement particles are uniformly distributed in the aluminum matrix under high-energy ultrasonic field. The morphology of the TiB2 particles is in circle-shape or quadrangle-shape, and the size of the particles is 0.1-1.5μm. The primary silicon particles are in quadrangle-shape and the average size of them is about 10μm. Hardness values of the Al-30Si matrix alloy and the TiB2/Al-30Si composites considerably increase as the high energy ultrasonic power increases. In particular, the maximum hardness value of the in-situ composites is about 1.3 times as high as that of the matrix alloy when the ultrasonic power is 1.2 kW, reaching 412 MPa. Meanwhile, the wear resistance of the in-situ TiB2/Al-30Si composites prepared under high-energy ultrasonic field is obviously improved and is insensitive to the applied loads of the dry sliding testing.展开更多
基金Project(52265043)supported by the National Natural Science Foundation of ChinaProject(2021A1515010470)supported by the Natural Science Foundation of Guangdong Province,China+1 种基金Project(ZK2023(014))supported by the Guizhou Provincial Science and Technology Projects,ChinaProject(YQK[2023]011)supported by the Outstanding Youth Science and Technology Talent Project of Guizhou Province,China。
基金Project(51174098)supported by the National Natural Science Foundation of ChinaProject(kjsmcx0903)supported by the Foundation of the Jiangsu Province Key Laboratory of Materials Tribology,China+2 种基金Project(1202015B)supported by the Postdoctoral Science Foundation of Jiangsu Province,ChinaProject(03)supported by the Undergraduate Practice-Innovation Training Foundation of Jiangsu University,ChinaProjects(GY2012020,GY2013032)supported by the Science and Technology Support Plan Project Foundation of Zhenjiang City,China
文摘TiB2/Al-30Si composites were fabricated via in-situ melt reaction under high-energy ultrasonic field. The microstructure and wear properties of the composite were investigated by XRD, SEM and dry sliding testing. The results indicate that TiB2 reinforcement particles are uniformly distributed in the aluminum matrix under high-energy ultrasonic field. The morphology of the TiB2 particles is in circle-shape or quadrangle-shape, and the size of the particles is 0.1-1.5μm. The primary silicon particles are in quadrangle-shape and the average size of them is about 10μm. Hardness values of the Al-30Si matrix alloy and the TiB2/Al-30Si composites considerably increase as the high energy ultrasonic power increases. In particular, the maximum hardness value of the in-situ composites is about 1.3 times as high as that of the matrix alloy when the ultrasonic power is 1.2 kW, reaching 412 MPa. Meanwhile, the wear resistance of the in-situ TiB2/Al-30Si composites prepared under high-energy ultrasonic field is obviously improved and is insensitive to the applied loads of the dry sliding testing.
基金Project(NCET-07-0234)supported by the Program for New Century Excellent Talents in University,ChinaProject(20060400813)supported by the Postdoctoral Science Foundation of China
