A hydrophobic coating of the silica fiber reinforced silica composites(SiO2f/SiO2) was synthesized by sol-gel method using methyltriethoxy-silane(MTES) and boric acid(B(OH)3) as raw materials. The relationship among b...A hydrophobic coating of the silica fiber reinforced silica composites(SiO2f/SiO2) was synthesized by sol-gel method using methyltriethoxy-silane(MTES) and boric acid(B(OH)3) as raw materials. The relationship among boron doping, chemical structure of precursors and durability of hydrophobic coatings was discussed. The Si-O-B and methyl groups were successfully introduced in the gel precursors according to the FT-IR and XPS results. The resins were filled in the internal and surface holes of the SiO2f/SiO2 composites partially or completely, which is beneficial to reduce the physical adsorption of the moisture. In addition, hydroxyl groups of the SiO2f/SiO2 composites reacted with the resins and hydrophobic methyl groups were introduced, leading to the reduction of the chemical adsorption of water. Also, the boron doping was beneficial to enhancing the physical cross-linking between the coating and the SiO2f/SiO2 composites, and improved the adhesion of the coating to the substrate. The results show that the optimal hydrophobic coating with contact angle 130.33°, moisture absorption 0.33% and adhesion level 1 is obtained when the molar ratio of MTES to B(OH)3 is 10:4. The real permittivity of M10B4 is constant in the range of 2.32–2.51 and the dielectric tangent loss is constant in the range of 5.5 × 10-4–8.7 × 10-3. The hydrophobic coating has excellent dielectric properties.展开更多
以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积...以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积分数与材料性能之间的关系,对织物结构进行了优化。结果表明,经法向增强2.5D Si O2f/Si O2复合材料的经向力学性能较现有2.5D复合材料有显著提高,该材料在较低密度下(1.6 g/cm3),经向拉伸强度与现有材料(1.65 g/cm3)持平,且经向压缩强度接近现有材料的4.3倍。展开更多
基金supported by the Taishan Scholar Project(No.ts201511080)the National Natural Science Foundation of China(Nos.51672059,51172050,51102060 and 51302050)the Natural Scientific Research Innovation Foundation in Harbin Institute of Technology(No.HIT.NSRIF.2014129)
文摘A hydrophobic coating of the silica fiber reinforced silica composites(SiO2f/SiO2) was synthesized by sol-gel method using methyltriethoxy-silane(MTES) and boric acid(B(OH)3) as raw materials. The relationship among boron doping, chemical structure of precursors and durability of hydrophobic coatings was discussed. The Si-O-B and methyl groups were successfully introduced in the gel precursors according to the FT-IR and XPS results. The resins were filled in the internal and surface holes of the SiO2f/SiO2 composites partially or completely, which is beneficial to reduce the physical adsorption of the moisture. In addition, hydroxyl groups of the SiO2f/SiO2 composites reacted with the resins and hydrophobic methyl groups were introduced, leading to the reduction of the chemical adsorption of water. Also, the boron doping was beneficial to enhancing the physical cross-linking between the coating and the SiO2f/SiO2 composites, and improved the adhesion of the coating to the substrate. The results show that the optimal hydrophobic coating with contact angle 130.33°, moisture absorption 0.33% and adhesion level 1 is obtained when the molar ratio of MTES to B(OH)3 is 10:4. The real permittivity of M10B4 is constant in the range of 2.32–2.51 and the dielectric tangent loss is constant in the range of 5.5 × 10-4–8.7 × 10-3. The hydrophobic coating has excellent dielectric properties.
文摘以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积分数与材料性能之间的关系,对织物结构进行了优化。结果表明,经法向增强2.5D Si O2f/Si O2复合材料的经向力学性能较现有2.5D复合材料有显著提高,该材料在较低密度下(1.6 g/cm3),经向拉伸强度与现有材料(1.65 g/cm3)持平,且经向压缩强度接近现有材料的4.3倍。