A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation.The X-ray diffractometry,Raman measurement,and X-ray photoelectron...A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation.The X-ray diffractometry,Raman measurement,and X-ray photoelectron spectroscopy show that the Sb2O3/Sb2S3/FeOOH thin films are successfully prepared.SEM−EDS analyses reveal that the surface of Sb2O3/Sb2S3 thin films becomes rough after the immersion in the FeCl3 solution.The optimized impregnation time is found to be 8 h.The FeOOH co-catalyst loaded Sb2O3/Sb2S3 electrode exhibits an enhanced photocurrent density of 0.45 mA/cm2 at 1.23 V versus RHE under simulated 1 sun,which is approximately 1.41 times compared to the photocurrent density of the unloaded one.Through the further tests of UV−Vis spectroscopy,the electrochemical impedance spectra,and the PEC measurements,the enhancement can result from the increased light-harvesting ability,the decreased interface transmission impedance,and the remarkably enhanced carrier injection efficiency.展开更多
This study was conducted to do exposure assessment of the possible migration of antimony trioxide （Sb203） from Polyethylene terephthalate （PET） food contact materials （FCM）. Consumption Factor （CF） and Food-ty...This study was conducted to do exposure assessment of the possible migration of antimony trioxide （Sb203） from Polyethylene terephthalate （PET） food contact materials （FCM）. Consumption Factor （CF） and Food-type Distribution Factor （fT） were calculated from survey data with reference to the US FDA method. The most conservative migration conditions were obtained by testing Sb migration from PET FCM based on the Chinese national standard of GB/T 5009.101-2003[1].展开更多
To explore thin transparent electroluminescence and electric conductive films by sol-gel technique, Sb2O3 doped n-type ZnO ceramics powders were prepared by sol-gel technique and photoluminescence properties were meas...To explore thin transparent electroluminescence and electric conductive films by sol-gel technique, Sb2O3 doped n-type ZnO ceramics powders were prepared by sol-gel technique and photoluminescence properties were measured. Then, the influences of composition and heat treatment temperature on photoluminescence properties were investigated in detail. With respect to the dopant concentration, about 1mol% addition of Sb2O3 was effective to increase photoluminescence intensity. With respect to heat treatment temperature, 800℃ was appropriate, and rather higher heat treatment temperature resulted in the formation of Zn7Sb2O12 and decrease the intensity. The excited ultraviolet wavelength of 200nm was proper to intense photoluminescence.展开更多
基金Project(51674298)supported by the National Natural Science Foundation of ChinaProject(2017JJ3384)supported by the Natural Science Foundation of Hunan Province,ChinaProject(2018M630910)supported by the China Postdoctoral Science Foundation。
文摘A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation.The X-ray diffractometry,Raman measurement,and X-ray photoelectron spectroscopy show that the Sb2O3/Sb2S3/FeOOH thin films are successfully prepared.SEM−EDS analyses reveal that the surface of Sb2O3/Sb2S3 thin films becomes rough after the immersion in the FeCl3 solution.The optimized impregnation time is found to be 8 h.The FeOOH co-catalyst loaded Sb2O3/Sb2S3 electrode exhibits an enhanced photocurrent density of 0.45 mA/cm2 at 1.23 V versus RHE under simulated 1 sun,which is approximately 1.41 times compared to the photocurrent density of the unloaded one.Through the further tests of UV−Vis spectroscopy,the electrochemical impedance spectra,and the PEC measurements,the enhancement can result from the increased light-harvesting ability,the decreased interface transmission impedance,and the remarkably enhanced carrier injection efficiency.
基金financially supported by the Beijing Natural Science Foundation-Sanyuan Joint FundingNo.15S00033
文摘This study was conducted to do exposure assessment of the possible migration of antimony trioxide （Sb203） from Polyethylene terephthalate （PET） food contact materials （FCM）. Consumption Factor （CF） and Food-type Distribution Factor （fT） were calculated from survey data with reference to the US FDA method. The most conservative migration conditions were obtained by testing Sb migration from PET FCM based on the Chinese national standard of GB/T 5009.101-2003[1].
文摘To explore thin transparent electroluminescence and electric conductive films by sol-gel technique, Sb2O3 doped n-type ZnO ceramics powders were prepared by sol-gel technique and photoluminescence properties were measured. Then, the influences of composition and heat treatment temperature on photoluminescence properties were investigated in detail. With respect to the dopant concentration, about 1mol% addition of Sb2O3 was effective to increase photoluminescence intensity. With respect to heat treatment temperature, 800℃ was appropriate, and rather higher heat treatment temperature resulted in the formation of Zn7Sb2O12 and decrease the intensity. The excited ultraviolet wavelength of 200nm was proper to intense photoluminescence.