The rapid development of nanotechnology has significantly revolutionized wearable electronics and expanded their functionality.Through introducing innovative solutions for energy harvesting and autonomous sensing,this...The rapid development of nanotechnology has significantly revolutionized wearable electronics and expanded their functionality.Through introducing innovative solutions for energy harvesting and autonomous sensing,this research presents a cost-effective strategy to enhance the performance of triboelectric nanogenerators(TENGs).The TENG was fabricated from polyvinylidene fluoride(PVDF)and N,N'-poly(methyl methacrylate)(PMMA)blend with a porous structure via a novel optimized quenching method.The developed approach results in a highβ-phase content(85.7%)PVDF/3wt.%PMMA porous blend,known for its superior piezoelectric properties.PVDF/3wt.%PMMA modified porous TENG demonstrates remarkable electrical output,with a dielectric constant of 40 and an open-circuit voltage of approximately 600 V.The porous matrix notably increases durability,enduring over 36000 operational cycles without performance degradation.Moreover,practical applications were explored in this research,including powering LEDs and pacemakers with a maximum power output of 750mWm^(-2).Also,TENG served as a self-powered tactile sensor for robotic applications in various temperature conditions.The work highlights the potential of the PVDF/PMMA porous blend to utilize the next-generation self-powered sensors and power small electronic devices.展开更多
The effect of substrate on the phase morphologies of PMMA/PS blend films was investigated by means of phase contrast microscope. PMMA/PS blend films were cast onto various substrates(such as glass substrate and PP sub...The effect of substrate on the phase morphologies of PMMA/PS blend films was investigated by means of phase contrast microscope. PMMA/PS blend films were cast onto various substrates(such as glass substrate and PP substrate) by spin-coating with thickness of about 10 μm. It was observed that there was a large difference of the phase inversion region between the blend films cast on glass and on PP substrates. On glass substrate, the phase inversion occurred at about \%Φ\%_m=0 4(PS mass fraction) while at \%Φ\%_m=0 5 on PP substrate. This implies that there is a shift of the phase inversion region with the change of substrate in cast polymer blend films. In other words, phase inversion region depends on the substrate. ATR-FTIR analysis was used to detect the composition of the surface and the bottom of the films(about 100 μm thick) obtained by evaporating solvent from the polymer blend solution. The ATR-FTIR spectra of the surface and the bottom of the PMMA/PS blend thin films cast on glass substrate and PP substrate showed that PMMA component preferentially segregated to glass substrate and PS component was enriched on the PP substrate. This selective segregation was due to the difference of the wetting abilities of PS and PMMA on the two kinds of substrates. The polymer-substrate interfacial tension γ were calculated and the results supported the ATR-FTIR results. It could be inferred that the shift of the phase inversion region with the change of the substrate in PMMA/PS blend film was due to the fact that the composition of the blend in the bulk changed, owing to the selective enrichment of one component of polymer blend to the substrate. In other words, the affinity between polymer and substrate can strongly influence the phase morphologies and the phase inversion region in polymer blend films.展开更多
为提高锂离子电池聚偏氟乙烯(PVDF)基聚合物隔膜对电解液体系的亲和性和导电性,引入聚甲基丙烯酸甲酯(PMMA)与聚偏氟乙烯(PVDF)进行共混,并添加有机增塑剂聚乙二醇PEG-400对PVDF基聚合物隔膜进行改性研究。采用先干法后湿法的相转化方...为提高锂离子电池聚偏氟乙烯(PVDF)基聚合物隔膜对电解液体系的亲和性和导电性,引入聚甲基丙烯酸甲酯(PMMA)与聚偏氟乙烯(PVDF)进行共混,并添加有机增塑剂聚乙二醇PEG-400对PVDF基聚合物隔膜进行改性研究。采用先干法后湿法的相转化方法制备PVDF/PMMA/PEG型聚合物隔膜。通过对制备的聚合物隔膜的孔隙率、吸液率、微观形貌和电化学性能的分析研究,确定制膜的最佳工艺条件为聚合物占溶剂质量百分比为8%,PVDF∶PMMA=7∶3,增塑剂含量为30%,非溶剂含量为3%,反应温度为45℃,在此最佳工艺条件下制备的PVDF/PMMA/PEG隔膜的离子电导率可达2.848 m S/cm,对电解液体系的亲和性和导电性得到显著提高。展开更多
基金supported by the research projects AP14869428 from the Ministry of Science and Higher Education of the Republic of Kazakhstan20122022FD4135 from Nazarbayev University.
文摘The rapid development of nanotechnology has significantly revolutionized wearable electronics and expanded their functionality.Through introducing innovative solutions for energy harvesting and autonomous sensing,this research presents a cost-effective strategy to enhance the performance of triboelectric nanogenerators(TENGs).The TENG was fabricated from polyvinylidene fluoride(PVDF)and N,N'-poly(methyl methacrylate)(PMMA)blend with a porous structure via a novel optimized quenching method.The developed approach results in a highβ-phase content(85.7%)PVDF/3wt.%PMMA porous blend,known for its superior piezoelectric properties.PVDF/3wt.%PMMA modified porous TENG demonstrates remarkable electrical output,with a dielectric constant of 40 and an open-circuit voltage of approximately 600 V.The porous matrix notably increases durability,enduring over 36000 operational cycles without performance degradation.Moreover,practical applications were explored in this research,including powering LEDs and pacemakers with a maximum power output of 750mWm^(-2).Also,TENG served as a self-powered tactile sensor for robotic applications in various temperature conditions.The work highlights the potential of the PVDF/PMMA porous blend to utilize the next-generation self-powered sensors and power small electronic devices.
文摘The effect of substrate on the phase morphologies of PMMA/PS blend films was investigated by means of phase contrast microscope. PMMA/PS blend films were cast onto various substrates(such as glass substrate and PP substrate) by spin-coating with thickness of about 10 μm. It was observed that there was a large difference of the phase inversion region between the blend films cast on glass and on PP substrates. On glass substrate, the phase inversion occurred at about \%Φ\%_m=0 4(PS mass fraction) while at \%Φ\%_m=0 5 on PP substrate. This implies that there is a shift of the phase inversion region with the change of substrate in cast polymer blend films. In other words, phase inversion region depends on the substrate. ATR-FTIR analysis was used to detect the composition of the surface and the bottom of the films(about 100 μm thick) obtained by evaporating solvent from the polymer blend solution. The ATR-FTIR spectra of the surface and the bottom of the PMMA/PS blend thin films cast on glass substrate and PP substrate showed that PMMA component preferentially segregated to glass substrate and PS component was enriched on the PP substrate. This selective segregation was due to the difference of the wetting abilities of PS and PMMA on the two kinds of substrates. The polymer-substrate interfacial tension γ were calculated and the results supported the ATR-FTIR results. It could be inferred that the shift of the phase inversion region with the change of the substrate in PMMA/PS blend film was due to the fact that the composition of the blend in the bulk changed, owing to the selective enrichment of one component of polymer blend to the substrate. In other words, the affinity between polymer and substrate can strongly influence the phase morphologies and the phase inversion region in polymer blend films.
文摘为提高锂离子电池聚偏氟乙烯(PVDF)基聚合物隔膜对电解液体系的亲和性和导电性,引入聚甲基丙烯酸甲酯(PMMA)与聚偏氟乙烯(PVDF)进行共混,并添加有机增塑剂聚乙二醇PEG-400对PVDF基聚合物隔膜进行改性研究。采用先干法后湿法的相转化方法制备PVDF/PMMA/PEG型聚合物隔膜。通过对制备的聚合物隔膜的孔隙率、吸液率、微观形貌和电化学性能的分析研究,确定制膜的最佳工艺条件为聚合物占溶剂质量百分比为8%,PVDF∶PMMA=7∶3,增塑剂含量为30%,非溶剂含量为3%,反应温度为45℃,在此最佳工艺条件下制备的PVDF/PMMA/PEG隔膜的离子电导率可达2.848 m S/cm,对电解液体系的亲和性和导电性得到显著提高。