A series of blends of Acrylonitrile-Butadiene-Styrene (ABS) and Polycarbonate (PC) were prepared and some of their thermal and mechanical properties were determined. The Young’s modulus changed gradually and monotoni...A series of blends of Acrylonitrile-Butadiene-Styrene (ABS) and Polycarbonate (PC) were prepared and some of their thermal and mechanical properties were determined. The Young’s modulus changed gradually and monotonically with the polycarbonate content. This effect was tentatively explained as the antiplasticization of the PC which is ascribed to the chain mobility, which permits the PC chains to pack more tightly, to the secondary cross-linking between the PC chains, or to the secondary attachment of bulky side-chains to the PC, thus producing steric hindrance to the rotation of the PC main chains. The experimental values found for the impact strength were intermediate between those of the neat polymers, depending upon the dispersed rubber particles of butadiene in the matrix of SAN (Styrene-Acrylonitrile), and the dispersed PC particles which generally make the ABS more brittle. A maximum value of about 88 KJ/m2 for the impact strength was observed for the blend with 90% PC. This may be attributed to the strong polymer-polymer interactions for this particular composition. The variations in the heat deflection temperature HDT and the Vicat softening point with the blend composition were very similar, and allowed us to assume that the phase inversion between the matrices of the two polymers takes place at 50% PC. The morphology of the blends revealed by SEM observation, show a co-continuous structure.展开更多
This paper experimentally studies the tensile deformation behavior of poly- carbonate （PC）, acrylonitrile-butadiene-styrene （ABS）, and PC/ABS blends （with the blending ratios of PC to ABS being 80：20, 60：40, 50...This paper experimentally studies the tensile deformation behavior of poly- carbonate （PC）, acrylonitrile-butadiene-styrene （ABS）, and PC/ABS blends （with the blending ratios of PC to ABS being 80：20, 60：40, 50：50, and 40：60） from low to high strain rates. Using the universal MTS-810 machine and the split Hopkinson tension bar （SHTB） testing system, the quasi-static and impact tension tests are carried out at the room temperature. The curves of the true stress and the true strain are obtained. The deformation behaviors of PC, ABS, and PC/ABS blends are characterized in detail. The linear relationship between the strain rate and the yielding stress is given.展开更多
The cation—conductive blends plasticized with propylene carbonate were prepared. The blends exhibited good mechanical strength and single—cation conduction over a wide range of plasticizer composition. The plasticiz...The cation—conductive blends plasticized with propylene carbonate were prepared. The blends exhibited good mechanical strength and single—cation conduction over a wide range of plasticizer composition. The plasticizer not only increases the conductivity of the blends but also decreases the electrochemical interface resistance between the blend and lithium electrode. The carrier in the blends obviously grows in number.展开更多
Films of polymethyl methacrylate (PMMA)/polycarbonate (PC) polymer blend doped silicon carbide (SiC) nanopowder are synthesized by the casting method. The study for the structural, optical and electrical behavior of P...Films of polymethyl methacrylate (PMMA)/polycarbonate (PC) polymer blend doped silicon carbide (SiC) nanopowder are synthesized by the casting method. The study for the structural, optical and electrical behavior of PMMA/PC blend without and with low contents (≤0.8 wt%) of SiC is done. The change of the structure is investigated from X-ray spectra. After the addition of SiC, the intensity of the main X-ray halo peak at 2θ = 20.26°of PMMA/PC is decreased, attributed to an interaction between PMMA/PC. It’s clear that SiC is causing an increase in the amorphous regions inside the PMMA/PC blend. The peaks related to SiC are not found attributed using a small amount of SiC with complete dissolution of SiC. The shift of the intensity for IR bands has supported an interaction between all components. The values of the optical band gap from UV-Vis spectra using indirect transition are decreased with the increase of SiC. The values of the electrical conductivity are low at low frequency attributed to the charge accumulation at the electrode which takes place. The conductivity is increased as the increase of frequency due to the mobility of charge carriers. Furthermore, the conductivity is increased with the increase of SiC contents. The values of ε' and ε'' are very high at the lower frequency and they decrease when the frequency is increased attributed to the effect. The plot of both Z' and Z'' shows dramatic decrease with the increase of frequency.展开更多
The miscibility,mechanical properties,morphology and toughening mechanism of PC/PBA-PMMA blends wereinvestigated.The dynamic mechanical results show that PC/PBA-PMMA blend has good miscibility and strong interfacialad...The miscibility,mechanical properties,morphology and toughening mechanism of PC/PBA-PMMA blends wereinvestigated.The dynamic mechanical results show that PC/PBA-PMMA blend has good miscibility and strong interfacialadhesion.The Izod impact strength of blend PC/PBA-PMMA with 4%(volume fraction)PBA-PMMA core-shell modifier is16 times higher than that of pure PC.The core-shell volume fraction and thickness of the PMMA shell have effect on thetoughness of PC/PBA-PMMA blends.As PMMA volume fraction increases,the toughness of PC/PBA-PMMA blendincreases,and reaches a maximum value at 30% volume fraction of PMMA or so.The tensile properties of PC/PBA-PMMAblend with a minimum amount of PBA-PMMA modifier show that brittle-tough transition has no significant variance incomparison with that of pure PC.The scanning electron microscopic(SEM)observation indicates that the tougheningmechanism of the blend with the pseudo-ductile matrix modified by small core-shell latex polymer particles is the synergeticeffect of cavitation and shear yielding of the matrix.展开更多
文摘A series of blends of Acrylonitrile-Butadiene-Styrene (ABS) and Polycarbonate (PC) were prepared and some of their thermal and mechanical properties were determined. The Young’s modulus changed gradually and monotonically with the polycarbonate content. This effect was tentatively explained as the antiplasticization of the PC which is ascribed to the chain mobility, which permits the PC chains to pack more tightly, to the secondary cross-linking between the PC chains, or to the secondary attachment of bulky side-chains to the PC, thus producing steric hindrance to the rotation of the PC main chains. The experimental values found for the impact strength were intermediate between those of the neat polymers, depending upon the dispersed rubber particles of butadiene in the matrix of SAN (Styrene-Acrylonitrile), and the dispersed PC particles which generally make the ABS more brittle. A maximum value of about 88 KJ/m2 for the impact strength was observed for the blend with 90% PC. This may be attributed to the strong polymer-polymer interactions for this particular composition. The variations in the heat deflection temperature HDT and the Vicat softening point with the blend composition were very similar, and allowed us to assume that the phase inversion between the matrices of the two polymers takes place at 50% PC. The morphology of the blends revealed by SEM observation, show a co-continuous structure.
基金supported by the National Natural Science Foundation of China (No. 11142004)the Shang-hai Leading Academic Discipline Project (No. S30106)the Innovative Foundation of Shanghai University
文摘This paper experimentally studies the tensile deformation behavior of poly- carbonate （PC）, acrylonitrile-butadiene-styrene （ABS）, and PC/ABS blends （with the blending ratios of PC to ABS being 80：20, 60：40, 50：50, and 40：60） from low to high strain rates. Using the universal MTS-810 machine and the split Hopkinson tension bar （SHTB） testing system, the quasi-static and impact tension tests are carried out at the room temperature. The curves of the true stress and the true strain are obtained. The deformation behaviors of PC, ABS, and PC/ABS blends are characterized in detail. The linear relationship between the strain rate and the yielding stress is given.
文摘The cation—conductive blends plasticized with propylene carbonate were prepared. The blends exhibited good mechanical strength and single—cation conduction over a wide range of plasticizer composition. The plasticizer not only increases the conductivity of the blends but also decreases the electrochemical interface resistance between the blend and lithium electrode. The carrier in the blends obviously grows in number.
文摘Films of polymethyl methacrylate (PMMA)/polycarbonate (PC) polymer blend doped silicon carbide (SiC) nanopowder are synthesized by the casting method. The study for the structural, optical and electrical behavior of PMMA/PC blend without and with low contents (≤0.8 wt%) of SiC is done. The change of the structure is investigated from X-ray spectra. After the addition of SiC, the intensity of the main X-ray halo peak at 2θ = 20.26°of PMMA/PC is decreased, attributed to an interaction between PMMA/PC. It’s clear that SiC is causing an increase in the amorphous regions inside the PMMA/PC blend. The peaks related to SiC are not found attributed using a small amount of SiC with complete dissolution of SiC. The shift of the intensity for IR bands has supported an interaction between all components. The values of the optical band gap from UV-Vis spectra using indirect transition are decreased with the increase of SiC. The values of the electrical conductivity are low at low frequency attributed to the charge accumulation at the electrode which takes place. The conductivity is increased as the increase of frequency due to the mobility of charge carriers. Furthermore, the conductivity is increased with the increase of SiC contents. The values of ε' and ε'' are very high at the lower frequency and they decrease when the frequency is increased attributed to the effect. The plot of both Z' and Z'' shows dramatic decrease with the increase of frequency.
基金This work was supported by the National Natural Science Foundation of China(Nos.5030301750373044+8 种基金50253002500730242007403720490220503900905002700120023003)the Special Funds for Major State Basic Research Projects(No.2003CB615600)the Chi
文摘The miscibility,mechanical properties,morphology and toughening mechanism of PC/PBA-PMMA blends wereinvestigated.The dynamic mechanical results show that PC/PBA-PMMA blend has good miscibility and strong interfacialadhesion.The Izod impact strength of blend PC/PBA-PMMA with 4%(volume fraction)PBA-PMMA core-shell modifier is16 times higher than that of pure PC.The core-shell volume fraction and thickness of the PMMA shell have effect on thetoughness of PC/PBA-PMMA blends.As PMMA volume fraction increases,the toughness of PC/PBA-PMMA blendincreases,and reaches a maximum value at 30% volume fraction of PMMA or so.The tensile properties of PC/PBA-PMMAblend with a minimum amount of PBA-PMMA modifier show that brittle-tough transition has no significant variance incomparison with that of pure PC.The scanning electron microscopic(SEM)observation indicates that the tougheningmechanism of the blend with the pseudo-ductile matrix modified by small core-shell latex polymer particles is the synergeticeffect of cavitation and shear yielding of the matrix.