Different organo-montmorillonites （OMMTs） are prepared by modifying montmorillonites （MMTs） with CTAB, PA 1010 salts/CTAB, PEG/CTAB, PVA/CTAB, PVP, PVP/ CTAB and PA 6/CTAB, respectively. These OMMTs were studied b...Different organo-montmorillonites （OMMTs） are prepared by modifying montmorillonites （MMTs） with CTAB, PA 1010 salts/CTAB, PEG/CTAB, PVA/CTAB, PVP, PVP/ CTAB and PA 6/CTAB, respectively. These OMMTs were studied by X-ray diffraction and TG. The gallery sizes of them are all larger than that of sodium MMTs. And the decomposition temperatures of them are all much higher than that of MMT and the processing temperature of PA 66, especially OM - 6 and OM - 7, the decomposition temperatures of which are 451.6℃ and 439.1℃, almost the collapse temperature of the native MMT crystal lattice which is more than 5080C. Then PA 66/Clay nanocomposites were synthesized by mixing these OMMTs with PA 66 matrix via melt intercalation. Experimental results indicate that the tensile and flexural properties increase significantly, especially those of PCN - 08. The combination property of PCN- 08 is the best. TEaM photos show that some clay platelets are present in the matrix as exfollated layers, while most of the clay platelets are present as intercalated layers.展开更多
基金Supported by Training Project For Innovitive Talents of Universities of Henan Province and Scientific Starting Funds For Returned Personnel From Abroad of Ministry of Education of China P. R.
文摘Different organo-montmorillonites （OMMTs） are prepared by modifying montmorillonites （MMTs） with CTAB, PA 1010 salts/CTAB, PEG/CTAB, PVA/CTAB, PVP, PVP/ CTAB and PA 6/CTAB, respectively. These OMMTs were studied by X-ray diffraction and TG. The gallery sizes of them are all larger than that of sodium MMTs. And the decomposition temperatures of them are all much higher than that of MMT and the processing temperature of PA 66, especially OM - 6 and OM - 7, the decomposition temperatures of which are 451.6℃ and 439.1℃, almost the collapse temperature of the native MMT crystal lattice which is more than 5080C. Then PA 66/Clay nanocomposites were synthesized by mixing these OMMTs with PA 66 matrix via melt intercalation. Experimental results indicate that the tensile and flexural properties increase significantly, especially those of PCN - 08. The combination property of PCN- 08 is the best. TEaM photos show that some clay platelets are present in the matrix as exfollated layers, while most of the clay platelets are present as intercalated layers.