Ni-Re/SiO2 catalysts with controllable Ni particle sizes(4.5–18.0 nm)were synthesized to investigate the effects of the particle size on the amination of monoethanolamine(MEA).The catalysts were characterized by vari...Ni-Re/SiO2 catalysts with controllable Ni particle sizes(4.5–18.0 nm)were synthesized to investigate the effects of the particle size on the amination of monoethanolamine(MEA).The catalysts were characterized by various techniques and evaluated for the amination reaction in a trickle bed reactor at 170℃,8.0 MPa,and 0.5 h^-1 liquid hourly space velocity of MEA(LHSVMEA)in NH3/H2 atmosphere.The Ni-Re/SiO2 catalyst with the lowest Ni particle size(4.5 nm)exhibited the highest yield(66.4%)of the desired amines(ethylenediamine(EDA)and piperazine(PIP)).The results of the analysis show that the turnover frequency of MEA increased slightly(from 193 to 253 h^-1)as the Ni particle sizes of the Ni-Re/SiO2 catalysts increased from 4.5 to 18.0 nm.Moreover,the product distribution could be adjusted by varying the Ni particle size.The ratio of primary to secondary amines increased from 1.0 to 2.0 upon increasing the Ni particle size from 4.5 to 18.0 nm.Further analyses reveal that the Ni particle size influenced the electronic properties of surface Ni,which in turn affected the adsorption of MEA and the reaction pathway of MEA amination.Compared to those of small Ni particles,large particles possessed a higher proportion of high-coordinated terrace Ni sites and a higher surface electron density,which favored the amination of MEA and NH3 to form EDA.展开更多
The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface wit...The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface within 3 s and its dynamic contact angles can be expressed by a power law θ d= k(t+a) -n with the n value 0.98. Less than 50%(molar fraction) SiO 2 addition can accelerate the dynamic water spreading rate on the TiO 2 SiO 2 films and the optimum molar fraction of SiO 2 amount corresponding to as annealed, air plasma, and UV irradiation treatment process is 15%, 10% and 20%, respectively.展开更多
基金supported by the National Natural Science Foundation of China(21273227)Strategic Priority Research Program of Chinese Academy of Sciences(XDB17000000)~~
文摘Ni-Re/SiO2 catalysts with controllable Ni particle sizes(4.5–18.0 nm)were synthesized to investigate the effects of the particle size on the amination of monoethanolamine(MEA).The catalysts were characterized by various techniques and evaluated for the amination reaction in a trickle bed reactor at 170℃,8.0 MPa,and 0.5 h^-1 liquid hourly space velocity of MEA(LHSVMEA)in NH3/H2 atmosphere.The Ni-Re/SiO2 catalyst with the lowest Ni particle size(4.5 nm)exhibited the highest yield(66.4%)of the desired amines(ethylenediamine(EDA)and piperazine(PIP)).The results of the analysis show that the turnover frequency of MEA increased slightly(from 193 to 253 h^-1)as the Ni particle sizes of the Ni-Re/SiO2 catalysts increased from 4.5 to 18.0 nm.Moreover,the product distribution could be adjusted by varying the Ni particle size.The ratio of primary to secondary amines increased from 1.0 to 2.0 upon increasing the Ni particle size from 4.5 to 18.0 nm.Further analyses reveal that the Ni particle size influenced the electronic properties of surface Ni,which in turn affected the adsorption of MEA and the reaction pathway of MEA amination.Compared to those of small Ni particles,large particles possessed a higher proportion of high-coordinated terrace Ni sites and a higher surface electron density,which favored the amination of MEA and NH3 to form EDA.
文摘The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface within 3 s and its dynamic contact angles can be expressed by a power law θ d= k(t+a) -n with the n value 0.98. Less than 50%(molar fraction) SiO 2 addition can accelerate the dynamic water spreading rate on the TiO 2 SiO 2 films and the optimum molar fraction of SiO 2 amount corresponding to as annealed, air plasma, and UV irradiation treatment process is 15%, 10% and 20%, respectively.