A new environmental friendly catalyst, H3PW6Mo6O40/TiO2 was prepared. The optimum conditions have been found, that is, mass ratio of m （TiO2）： m （H3PW6Mo6O40） is 1：2.0, volume of water is 30 mL, the reflux react...A new environmental friendly catalyst, H3PW6Mo6O40/TiO2 was prepared. The optimum conditions have been found, that is, mass ratio of m （TiO2）： m （H3PW6Mo6O40） is 1：2.0, volume of water is 30 mL, the reflux reaction time is 2 h, and activated temperature is 150 ℃. H3PW6Mo6O40/TiO2 was used as catalyst in catalytic synthesis ofacetals and ketals. Effects ofn （aldehyde（ketone））： n （glycol）, catalyst dosage and reaction time on yield were investigated. Optimal conditions were： n（aldehyde （ketone））： n （glycol）=1.0 ： 1.4; mass fraction of catalyst to reactants, 0.8%; reaction time, 1.0 h and cyclohexane as water-stripped reagent, 10 mL. Under these conditions, yields of acetals and ketals can reach 53.0% -86.9 0%展开更多
The fatigue crack growth rate of a novel Ti-6Al-4V-1Mo titanium alloy,which is developed for laser directed energy deposition technique,was investigated before and after cyclic heat treatment(CHT).Changes in microstru...The fatigue crack growth rate of a novel Ti-6Al-4V-1Mo titanium alloy,which is developed for laser directed energy deposition technique,was investigated before and after cyclic heat treatment(CHT).Changes in microstructure,fracture surfaces,and crack growth paths were analyzed before and after CHT.Results indicate that in the stable crack growth region,the growth rates for the as-deposited and cyclic heat-treated specimens follow the relationships da/dN=1.8651×10^(−8)(ΔK)^(3.2271)and da/dN=1.4112×10^(−8)(ΔK)^(3.1125),respectively.Compared with that at the as-deposited state,the microstructure after CHT is transformed from a uniform basket-weave microstructure to a dual-phase microstructure consisting of near-sphericalαandβ-transformed matrix phases.The cyclic process also disrupts the continuity of the grain boundaryα(αGB)at the primaryβ-phase grain boundary.The coarsening of primaryαand the disruption ofαGB continuity are the primary factors to release stress concentration and promote crack deflection,thereby decreasing the fatigue crack growth rate.Additionally,the increased occurrence of crack branching,secondary cracking,and crack bridging in cyclic heat-treated specimens further reduces the crack driving force and slows the fatigue crack growth rate.展开更多
基金Acknowledgements： This work was financially supported by the Natural Science Foundation of Hubei Province, China （No. 2005ABA053） and the National Natural Science Foundation of China （No. 20471044）.
文摘A new environmental friendly catalyst, H3PW6Mo6O40/TiO2 was prepared. The optimum conditions have been found, that is, mass ratio of m （TiO2）： m （H3PW6Mo6O40） is 1：2.0, volume of water is 30 mL, the reflux reaction time is 2 h, and activated temperature is 150 ℃. H3PW6Mo6O40/TiO2 was used as catalyst in catalytic synthesis ofacetals and ketals. Effects ofn （aldehyde（ketone））： n （glycol）, catalyst dosage and reaction time on yield were investigated. Optimal conditions were： n（aldehyde （ketone））： n （glycol）=1.0 ： 1.4; mass fraction of catalyst to reactants, 0.8%; reaction time, 1.0 h and cyclohexane as water-stripped reagent, 10 mL. Under these conditions, yields of acetals and ketals can reach 53.0% -86.9 0%
基金National Key Research and Development Program of China(2024YFB4610803)。
文摘The fatigue crack growth rate of a novel Ti-6Al-4V-1Mo titanium alloy,which is developed for laser directed energy deposition technique,was investigated before and after cyclic heat treatment(CHT).Changes in microstructure,fracture surfaces,and crack growth paths were analyzed before and after CHT.Results indicate that in the stable crack growth region,the growth rates for the as-deposited and cyclic heat-treated specimens follow the relationships da/dN=1.8651×10^(−8)(ΔK)^(3.2271)and da/dN=1.4112×10^(−8)(ΔK)^(3.1125),respectively.Compared with that at the as-deposited state,the microstructure after CHT is transformed from a uniform basket-weave microstructure to a dual-phase microstructure consisting of near-sphericalαandβ-transformed matrix phases.The cyclic process also disrupts the continuity of the grain boundaryα(αGB)at the primaryβ-phase grain boundary.The coarsening of primaryαand the disruption ofαGB continuity are the primary factors to release stress concentration and promote crack deflection,thereby decreasing the fatigue crack growth rate.Additionally,the increased occurrence of crack branching,secondary cracking,and crack bridging in cyclic heat-treated specimens further reduces the crack driving force and slows the fatigue crack growth rate.