Mgo-Cao refractories are widely used in the iron and steel metalurgy industry due to their advantages of purifying molten steel,high refractoriness,good thermal shock resistance,and excellent corrosion resistance to b...Mgo-Cao refractories are widely used in the iron and steel metalurgy industry due to their advantages of purifying molten steel,high refractoriness,good thermal shock resistance,and excellent corrosion resistance to basic slags.However,hydration occurs during the manufacturing,storage,and transportation of refractories,which severely limits their application.Mgo-CaO clinker is the main raw material for Mgo-Cao refractories,and its hydration resistance determines the development of the latter case.Herein,the Mgo-Cao clinker was modified using myristic acid as the modifying agent by the liquid-phase deposition method.The effects of the particle size of the raw materials,concentration of myristic acid,treatment temperature and time on the phase composition and hydration resistance of the modified Mgo-Cao clinkers were investigated in detail.The results show that the samples with an agent concentration of 0.25 mol L^(-1) and treated at 25℃ for 1 h exhibit the optimal hydration resistance properties,namely a low hydration mass gain rate(0.23%)and a large water contact angle(152.9).展开更多
The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for ...The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for lower costs and higher economic benefits in high-carbon ferrochrome production process.This study calculated the activity of CrO_(x)in slag and investigated the distribution behavior of Cr between slag and alloy.Theω(MgO)/ω(Al_(2)O_(3))was 1.0,and the w(CaO)/w(SiO_(2))was from 0.2 to 0.6 in this study.The calculation and experimental results showed that the main phases of the slag were chrome-containing spinel,magnesium-aluminum spinel,olivine and melilite.The content of spinel in slag decreased with the increasing w(CaO)/w(SiO_(2)),and the w(CrO_(x))in spinel also reduced,but the content of melilite increased.The distribution ratio of Cr between slag and alloy decreased with the increase of slag basicity at 1600℃,meansning that increasing the w(CaO)/w(SiO_(2))of slag can improve the recovery of Cr in chromite smelting process.展开更多
基金National Natural Science Foundation of China(Grants 52202025 and U23A20559)Natural Science Foundation of Hubei Province(Grant 2022CFB629)+1 种基金"The 14^(th)Five-Year Plan"Hubei Provincial Advantaged Characteristic Disciplines(Groups)Project of Wuhan University of Science and Technology(2023A0307).
文摘Mgo-Cao refractories are widely used in the iron and steel metalurgy industry due to their advantages of purifying molten steel,high refractoriness,good thermal shock resistance,and excellent corrosion resistance to basic slags.However,hydration occurs during the manufacturing,storage,and transportation of refractories,which severely limits their application.Mgo-CaO clinker is the main raw material for Mgo-Cao refractories,and its hydration resistance determines the development of the latter case.Herein,the Mgo-Cao clinker was modified using myristic acid as the modifying agent by the liquid-phase deposition method.The effects of the particle size of the raw materials,concentration of myristic acid,treatment temperature and time on the phase composition and hydration resistance of the modified Mgo-Cao clinkers were investigated in detail.The results show that the samples with an agent concentration of 0.25 mol L^(-1) and treated at 25℃ for 1 h exhibit the optimal hydration resistance properties,namely a low hydration mass gain rate(0.23%)and a large water contact angle(152.9).
基金Project(2023XQLH055)supported by Central South University Graduate Research Innovation Project(University-Enterprise Joint Project),China。
文摘The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for lower costs and higher economic benefits in high-carbon ferrochrome production process.This study calculated the activity of CrO_(x)in slag and investigated the distribution behavior of Cr between slag and alloy.Theω(MgO)/ω(Al_(2)O_(3))was 1.0,and the w(CaO)/w(SiO_(2))was from 0.2 to 0.6 in this study.The calculation and experimental results showed that the main phases of the slag were chrome-containing spinel,magnesium-aluminum spinel,olivine and melilite.The content of spinel in slag decreased with the increasing w(CaO)/w(SiO_(2)),and the w(CrO_(x))in spinel also reduced,but the content of melilite increased.The distribution ratio of Cr between slag and alloy decreased with the increase of slag basicity at 1600℃,meansning that increasing the w(CaO)/w(SiO_(2))of slag can improve the recovery of Cr in chromite smelting process.