The NdCl_3/MgCl_2 bisupported catalyst was prepared by using NdCl_3 ,MgCl_2, (CH_3)_2(CH_2)_2 OH and TiCl_4. It is shown that the structure of bisupported catalyst was different from those of either NdCl_3 or MgCl_2 s...The NdCl_3/MgCl_2 bisupported catalyst was prepared by using NdCl_3 ,MgCl_2, (CH_3)_2(CH_2)_2 OH and TiCl_4. It is shown that the structure of bisupported catalyst was different from those of either NdCl_3 or MgCl_2 single supported catalyst. A peculiar type of kinetic curve for ethylene polymerization was found.展开更多
The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,an...The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,and a univariant line related to the secondary crystallization with a minimum M(68.5 wt-% NdCl_3,2.7 wt-% MgCl_2,28.8 wt-% LiCl_2 441℃)in the system.展开更多
Two surfaces correponding to LaCl_3 and α-solid solution(MgCl_2.LiCl) respectively: and one secondary crystallization curve with a minimum M at 63.8 wt-％ LaCl_3,2.0 wt-％ MgCl_2,34.2 wt-％ LiCl and 492℃ were fonud ...Two surfaces correponding to LaCl_3 and α-solid solution(MgCl_2.LiCl) respectively: and one secondary crystallization curve with a minimum M at 63.8 wt-％ LaCl_3,2.0 wt-％ MgCl_2,34.2 wt-％ LiCl and 492℃ were fonud by means of DTA.In combination with liquidus determination.an approach was also made to the alteration in LnCl_3-MgCl_2-LiCl svstem,where Lu denotes La.Ce.Pr or Nd.展开更多
Three surfaces corresponding to the primary crystallization of PrCl_3,CaCl_2 and MgCl_2 respectively,3 univariant curves related to the secondary crystallization and a ternary eutectic(44.8 wt-% PrCl_3,31.8 wt-% CaCl_...Three surfaces corresponding to the primary crystallization of PrCl_3,CaCl_2 and MgCl_2 respectively,3 univariant curves related to the secondary crystallization and a ternary eutectic(44.8 wt-% PrCl_3,31.8 wt-% CaCl_2,546℃)were found in system PrCl_3-CaCl_2-MgCl_2 by means of DTA.A reaction occurs in this system: L=PrCl_3+CaCl_2+MgCl_2.展开更多
Based on the thermodynamically self-consistent analysis and optimization of three sub-binary systems of the ternary system PrCl_3-CaCl_2-MgCl_2,the thermodynamics of this ternary system has been studied.Using Hillert ...Based on the thermodynamically self-consistent analysis and optimization of three sub-binary systems of the ternary system PrCl_3-CaCl_2-MgCl_2,the thermodynamics of this ternary system has been studied.Using Hillert model and taking MgCl_2 as an asymmetric component,the PrCl_3-CaCl_2-MgCl_2 phase diagram has been calculated.The agreement between calculated and measured compositions and temperatures at deflecting points on liquidus is good.The system is a simple eutectic one with a eutectic point at 26.0mol% PrCl_3, 41.5mol% CaCl_2,32.5mol% MgCl_2;560℃(calculated)and 26.0mol% PrCl_3,39.4mol% CaCl_2,34.6mol% MgCl_2;546℃(measured),respectively.展开更多
文摘The NdCl_3/MgCl_2 bisupported catalyst was prepared by using NdCl_3 ,MgCl_2, (CH_3)_2(CH_2)_2 OH and TiCl_4. It is shown that the structure of bisupported catalyst was different from those of either NdCl_3 or MgCl_2 single supported catalyst. A peculiar type of kinetic curve for ethylene polymerization was found.
文摘The liquidus of ternary system NdCl_3-MgCl_2-LiCl has been determined by means of DTA.It was found that there are two surfaces corresponding to the primary crystallization of NdCl_3 and α-(MgCl_2,LiCl)respectively,and a univariant line related to the secondary crystallization with a minimum M(68.5 wt-% NdCl_3,2.7 wt-% MgCl_2,28.8 wt-% LiCl_2 441℃)in the system.
文摘Two surfaces correponding to LaCl_3 and α-solid solution(MgCl_2.LiCl) respectively: and one secondary crystallization curve with a minimum M at 63.8 wt-％ LaCl_3,2.0 wt-％ MgCl_2,34.2 wt-％ LiCl and 492℃ were fonud by means of DTA.In combination with liquidus determination.an approach was also made to the alteration in LnCl_3-MgCl_2-LiCl svstem,where Lu denotes La.Ce.Pr or Nd.
文摘Three surfaces corresponding to the primary crystallization of PrCl_3,CaCl_2 and MgCl_2 respectively,3 univariant curves related to the secondary crystallization and a ternary eutectic(44.8 wt-% PrCl_3,31.8 wt-% CaCl_2,546℃)were found in system PrCl_3-CaCl_2-MgCl_2 by means of DTA.A reaction occurs in this system: L=PrCl_3+CaCl_2+MgCl_2.
基金Project Supported by National Natural Science Foundation of China
文摘Based on the thermodynamically self-consistent analysis and optimization of three sub-binary systems of the ternary system PrCl_3-CaCl_2-MgCl_2,the thermodynamics of this ternary system has been studied.Using Hillert model and taking MgCl_2 as an asymmetric component,the PrCl_3-CaCl_2-MgCl_2 phase diagram has been calculated.The agreement between calculated and measured compositions and temperatures at deflecting points on liquidus is good.The system is a simple eutectic one with a eutectic point at 26.0mol% PrCl_3, 41.5mol% CaCl_2,32.5mol% MgCl_2;560℃(calculated)and 26.0mol% PrCl_3,39.4mol% CaCl_2,34.6mol% MgCl_2;546℃(measured),respectively.