The effects of Ce addition on the microstructure of Mg-6Zn-1Mn alloy during casting, homogenization, hot extrusion, T4, T6 and T4＋two-step aging were investigated. The mechanical properties of alloys with and without...The effects of Ce addition on the microstructure of Mg-6Zn-1Mn alloy during casting, homogenization, hot extrusion, T4, T6 and T4＋two-step aging were investigated. The mechanical properties of alloys with and without Ce were compared. The results showed that Ce had an obvious effect on the microstructure of ZM61-0.5Ce alloy by restricting the occurrence of dynamic recrystallization and restraining the grain growth during extrusion and heat treatment subsequently. A new binary phase Mg 12 Ce was identified in ZM61-0.5Ce alloy, which distributed at grain boundaries and was broken to small particles distributed at grain boundaries along extrusion direction during extrusion. The mechanical properties of as-extruded ZM61-0.5Ce alloy were improved with the addition of Ce. The improved tensile properties of as-extruded ZM61-0.5Ce alloy were due to the finer grain sizes as compared to ZM61 alloy. However, the UTS and YS decreased severely and the elongation increased when ZM61-0.5Ce was treated by T6 and T4＋two-step aging. Brittle Mg 12 Ce phase, which was distributed at the grain boundary areas and cannot dissolve into the Mg matrix after solution treatment, became crack source under tensile stress.展开更多
The effect of cold plastic deformation between solution treatment and artificial aging on the age-hardening response and mechanical properties of alloy was investigated by micro-hardness test,tensile test,optical micr...The effect of cold plastic deformation between solution treatment and artificial aging on the age-hardening response and mechanical properties of alloy was investigated by micro-hardness test,tensile test,optical microscopy（OM） and TEM observation.After solution treatment at 420 ℃ for 1 h,three kinds of pre-deformation strains,i.e.0,5% and 10%,were applied to extruded ZM61 bars.Age-hardening curves show that pre-deformation can significantly accelerate the precipitation kinetics and increase peak-hardness value;however,as pre-deformation strain rises from 5% to 10%,there is no gain in peak hardness value.The room temperature（RT） tensile properties demonstrate that increasing the pre-deformation degree can enhance the yield strength（YS） and ultimate tensile strength（UTS） but moderately reduce elongation（EL）;furthermore,the enhancement of YS is larger than that of UTS.No twin can be observed in 5% pre-deformed microstructure;however,a large number of twins are activated after 10% pre-deformation.The peak-aged TEM microstructure shows that pre-deformation can increase the number density of rod-shaped β 1 ＇ precipitates which play a key role in strengthening ZM61 alloy.展开更多
基金Project(2007CB613700)supported by the National Basic Research Program of ChinaProject(2007BAG06B04)supported by the National Key Technology R&D Program+2 种基金Project(CSTC,2009AB4008)supported by the Chongqing Sci&Tech ProgramProject(50725413)supported by the National Natural Science Foundation of ChinaProject(CDJXS10132202)supported by the Fundamental Research Funds for the Central Universities, China
文摘The effects of Ce addition on the microstructure of Mg-6Zn-1Mn alloy during casting, homogenization, hot extrusion, T4, T6 and T4＋two-step aging were investigated. The mechanical properties of alloys with and without Ce were compared. The results showed that Ce had an obvious effect on the microstructure of ZM61-0.5Ce alloy by restricting the occurrence of dynamic recrystallization and restraining the grain growth during extrusion and heat treatment subsequently. A new binary phase Mg 12 Ce was identified in ZM61-0.5Ce alloy, which distributed at grain boundaries and was broken to small particles distributed at grain boundaries along extrusion direction during extrusion. The mechanical properties of as-extruded ZM61-0.5Ce alloy were improved with the addition of Ce. The improved tensile properties of as-extruded ZM61-0.5Ce alloy were due to the finer grain sizes as compared to ZM61 alloy. However, the UTS and YS decreased severely and the elongation increased when ZM61-0.5Ce was treated by T6 and T4＋two-step aging. Brittle Mg 12 Ce phase, which was distributed at the grain boundary areas and cannot dissolve into the Mg matrix after solution treatment, became crack source under tensile stress.
基金Project(2007CB613700) supported by the National Basic Research Program of ChinaProject(50725413) supported by the National Natural Science Foundation of China+2 种基金Project(CDJXS11132228) supported by the Fundamental Research Funds for the Central Universities,ChinaProjects(2010DFR50010,2008DFR50040) supported by International Cooperation Program,ChinaProjects (CSTC2009AB4008,2010CSTC-HDLS) supported by Chongqing Sci & Tech Program,China
文摘The effect of cold plastic deformation between solution treatment and artificial aging on the age-hardening response and mechanical properties of alloy was investigated by micro-hardness test,tensile test,optical microscopy（OM） and TEM observation.After solution treatment at 420 ℃ for 1 h,three kinds of pre-deformation strains,i.e.0,5% and 10%,were applied to extruded ZM61 bars.Age-hardening curves show that pre-deformation can significantly accelerate the precipitation kinetics and increase peak-hardness value;however,as pre-deformation strain rises from 5% to 10%,there is no gain in peak hardness value.The room temperature（RT） tensile properties demonstrate that increasing the pre-deformation degree can enhance the yield strength（YS） and ultimate tensile strength（UTS） but moderately reduce elongation（EL）;furthermore,the enhancement of YS is larger than that of UTS.No twin can be observed in 5% pre-deformed microstructure;however,a large number of twins are activated after 10% pre-deformation.The peak-aged TEM microstructure shows that pre-deformation can increase the number density of rod-shaped β 1 ＇ precipitates which play a key role in strengthening ZM61 alloy.