V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for N...V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.展开更多
基于密度泛函理论的第一性原理方法,通过计算表面能确定La Fe O_3(010)表面为最稳定的吸附表面,研究了H_2分子在La Fe O_3(010)表面的吸附性质。La Fe O_3(010)表面存在La O和Fe O_2两种终止表面,但吸附主要发生在Fe O_2终止表面,由于La...基于密度泛函理论的第一性原理方法,通过计算表面能确定La Fe O_3(010)表面为最稳定的吸附表面,研究了H_2分子在La Fe O_3(010)表面的吸附性质。La Fe O_3(010)表面存在La O和Fe O_2两种终止表面,但吸附主要发生在Fe O_2终止表面,由于La Fe O_3(010)表面弛豫的影响,使得凹凸不平的表面层增加了表面原子与H原子的接触面积,表面晶胞的纵向体积增加约2.5%,有利于H原子向晶体内扩散。研究发现,H_2分子在La Fe O_3(010)表面主要存在3种化学吸附方式:第一种吸附发生在O-O桥位,2个H原子分别吸附在2个O原子上,形成2个-OH基,这是最佳吸附位置,此时H原子与表面O原子的作用主要是H1s与O_2p轨道杂化作用的结果,H-O之间为典型的共价键。H_2分子的解离能垒为1.542 e V,说明表面需要一定的热条件,H_2分子才会发生解离吸附;第二种吸附发生在Fe-O桥位,1个H原子吸附在O原子上形成1个-OH基,另一个H原子吸附在Fe原子上形成金属键;第三种吸附发生在O顶位,2个H原子吸附在同一个O原子上,形成H_2O分子,此时H_2O分子与表面形成物理吸附,H_2O分子逃离表面后容易形成氧空位。此外,H_2分子在La Fe O_3(010)表面还可以发生物理吸附。展开更多
基金supported by the National Natural Science Foundation of China (51372137)the National High Technology Research and Development Program of China (863 Program,2015AA034603)~~
文摘V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.
文摘基于密度泛函理论的第一性原理方法,通过计算表面能确定La Fe O_3(010)表面为最稳定的吸附表面,研究了H_2分子在La Fe O_3(010)表面的吸附性质。La Fe O_3(010)表面存在La O和Fe O_2两种终止表面,但吸附主要发生在Fe O_2终止表面,由于La Fe O_3(010)表面弛豫的影响,使得凹凸不平的表面层增加了表面原子与H原子的接触面积,表面晶胞的纵向体积增加约2.5%,有利于H原子向晶体内扩散。研究发现,H_2分子在La Fe O_3(010)表面主要存在3种化学吸附方式:第一种吸附发生在O-O桥位,2个H原子分别吸附在2个O原子上,形成2个-OH基,这是最佳吸附位置,此时H原子与表面O原子的作用主要是H1s与O_2p轨道杂化作用的结果,H-O之间为典型的共价键。H_2分子的解离能垒为1.542 e V,说明表面需要一定的热条件,H_2分子才会发生解离吸附;第二种吸附发生在Fe-O桥位,1个H原子吸附在O原子上形成1个-OH基,另一个H原子吸附在Fe原子上形成金属键;第三种吸附发生在O顶位,2个H原子吸附在同一个O原子上,形成H_2O分子,此时H_2O分子与表面形成物理吸附,H_2O分子逃离表面后容易形成氧空位。此外,H_2分子在La Fe O_3(010)表面还可以发生物理吸附。