Magnetic refrigeration is a revolutionary, efficient, environmentally friendly cooling technology, which is on the threshold of commercialization. The magnetic rare earth materials are utilized as the magnetic refrige...Magnetic refrigeration is a revolutionary, efficient, environmentally friendly cooling technology, which is on the threshold of commercialization. The magnetic rare earth materials are utilized as the magnetic refrigerants in most cooling devices, and for many cooling application the Nd2Fe14B permanent magnets are employed as the source of the magnetic field. The status of the near room temperature magnetic cooling was reviewed.展开更多
A multi-finger structure power SiGe HBT device （with an emitter area of about 166μm^2） is fabricated with very simple 2μm double-mesa technology. The DC current gain β is 144.25. The B-C junction breakdown voltag...A multi-finger structure power SiGe HBT device （with an emitter area of about 166μm^2） is fabricated with very simple 2μm double-mesa technology. The DC current gain β is 144.25. The B-C junction breakdown voltage reaches 9V with a collector doping concentration of 1 × 10^17cm^-3 and a collector thickness of 400nm. Though our data are influenced by large additional RF probe pads, the device exhibits a maximum oscillation frequency fmax of 10.1GHz and a cut-off frequency fτ of 1.8GHz at a DC bias point of IC=10mA and VCE = 2.5V.展开更多
Based on the Fermi's golden rule and the theory of Boltzmann collision term approximation, a physically-based model for hole scattering rate(SR) in strained Si1-x Gex/(100)Si was presented, which takes into accoun...Based on the Fermi's golden rule and the theory of Boltzmann collision term approximation, a physically-based model for hole scattering rate(SR) in strained Si1-x Gex/(100)Si was presented, which takes into account a variety of scattering mechanisms,including ionized impurity, acoustic phonon, non-polar optical phonon and alloy disorder scattering. It is indicated that the SRs of acoustic phonon and non-polar optical phonon decrease under the strain, and the total SR in strained Si1-x Gex/(100)Si also decreases obviously with increasing Ge fraction(x). Moreover, the total SR continues to show a constant tendency when x is less than 0.3. In comparison with bulk Si, the total SR of strained Si1-x Gex/(100) Si decreases by about 58%.展开更多
基金Project supported bythe U.S .Department of Energy ,Office of Basic Energy Sciences , Materials Science and Engineering Division and Astronautics Corporation of America , Milwaukee , Wisconsin
文摘Magnetic refrigeration is a revolutionary, efficient, environmentally friendly cooling technology, which is on the threshold of commercialization. The magnetic rare earth materials are utilized as the magnetic refrigerants in most cooling devices, and for many cooling application the Nd2Fe14B permanent magnets are employed as the source of the magnetic field. The status of the near room temperature magnetic cooling was reviewed.
文摘A multi-finger structure power SiGe HBT device （with an emitter area of about 166μm^2） is fabricated with very simple 2μm double-mesa technology. The DC current gain β is 144.25. The B-C junction breakdown voltage reaches 9V with a collector doping concentration of 1 × 10^17cm^-3 and a collector thickness of 400nm. Though our data are influenced by large additional RF probe pads, the device exhibits a maximum oscillation frequency fmax of 10.1GHz and a cut-off frequency fτ of 1.8GHz at a DC bias point of IC=10mA and VCE = 2.5V.
基金Project(JY0300122503)supported by the Research Fund for the Doctoral Program of Higher Education of ChinaProject(P140c090303110c0904)supported by NLAIC Research Fund,ChinaProjects(K5051225014,7214608503)supported by the Fundamental Research Funds for the Central Universities,China
文摘Based on the Fermi's golden rule and the theory of Boltzmann collision term approximation, a physically-based model for hole scattering rate(SR) in strained Si1-x Gex/(100)Si was presented, which takes into account a variety of scattering mechanisms,including ionized impurity, acoustic phonon, non-polar optical phonon and alloy disorder scattering. It is indicated that the SRs of acoustic phonon and non-polar optical phonon decrease under the strain, and the total SR in strained Si1-x Gex/(100)Si also decreases obviously with increasing Ge fraction(x). Moreover, the total SR continues to show a constant tendency when x is less than 0.3. In comparison with bulk Si, the total SR of strained Si1-x Gex/(100) Si decreases by about 58%.