High-temperature experiments were carried out for the slag systems of“FeO”−SiO_(2)−CaO−Al_(2)O_(3)and“FeO”−SiO_(2)−CaO−MgO at 1200℃and p(O_(2))of 10^(−7)kPa.The equilibrated samples were quenched,and the phase co...High-temperature experiments were carried out for the slag systems of“FeO”−SiO_(2)−CaO−Al_(2)O_(3)and“FeO”−SiO_(2)−CaO−MgO at 1200℃and p(O_(2))of 10^(−7)kPa.The equilibrated samples were quenched,and the phase compositions were measured by electron probe microanalysis(EPMA).A series of pseudo-ternary and pseudo-binary phase diagrams are constructed to demonstrate their applications in copper smelting process and evaluation of the thermodynamic database.Spinel and tridymite are identified to be the major primary phases in the composition range related to the copper smelting slags.It is found that the operating window of the smelting slag is primarily determined by w_(Fe)/w_(SiO_(2))ratio in the slag.Both MgO and Al_(2)O_(3)in the slag reduce the operating window which requires extra fluxing agent to keep the slag to be fully liquid.Complex spinel solid solutions cause inaccurate predictions of the current thermodynamic database.展开更多
The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for ...The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for lower costs and higher economic benefits in high-carbon ferrochrome production process.This study calculated the activity of CrO_(x)in slag and investigated the distribution behavior of Cr between slag and alloy.Theω(MgO)/ω(Al_(2)O_(3))was 1.0,and the w(CaO)/w(SiO_(2))was from 0.2 to 0.6 in this study.The calculation and experimental results showed that the main phases of the slag were chrome-containing spinel,magnesium-aluminum spinel,olivine and melilite.The content of spinel in slag decreased with the increasing w(CaO)/w(SiO_(2)),and the w(CrO_(x))in spinel also reduced,but the content of melilite increased.The distribution ratio of Cr between slag and alloy decreased with the increase of slag basicity at 1600℃,meansning that increasing the w(CaO)/w(SiO_(2))of slag can improve the recovery of Cr in chromite smelting process.展开更多
The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyse...The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.展开更多
基金supprted by the National Natural Science Foundation of China(5140620851406214)the Science&Technology Research Project of Guangdong Province(2013B050800008)~~
文摘High-temperature experiments were carried out for the slag systems of“FeO”−SiO_(2)−CaO−Al_(2)O_(3)and“FeO”−SiO_(2)−CaO−MgO at 1200℃and p(O_(2))of 10^(−7)kPa.The equilibrated samples were quenched,and the phase compositions were measured by electron probe microanalysis(EPMA).A series of pseudo-ternary and pseudo-binary phase diagrams are constructed to demonstrate their applications in copper smelting process and evaluation of the thermodynamic database.Spinel and tridymite are identified to be the major primary phases in the composition range related to the copper smelting slags.It is found that the operating window of the smelting slag is primarily determined by w_(Fe)/w_(SiO_(2))ratio in the slag.Both MgO and Al_(2)O_(3)in the slag reduce the operating window which requires extra fluxing agent to keep the slag to be fully liquid.Complex spinel solid solutions cause inaccurate predictions of the current thermodynamic database.
基金Project(2023XQLH055)supported by Central South University Graduate Research Innovation Project(University-Enterprise Joint Project),China。
文摘The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for lower costs and higher economic benefits in high-carbon ferrochrome production process.This study calculated the activity of CrO_(x)in slag and investigated the distribution behavior of Cr between slag and alloy.Theω(MgO)/ω(Al_(2)O_(3))was 1.0,and the w(CaO)/w(SiO_(2))was from 0.2 to 0.6 in this study.The calculation and experimental results showed that the main phases of the slag were chrome-containing spinel,magnesium-aluminum spinel,olivine and melilite.The content of spinel in slag decreased with the increasing w(CaO)/w(SiO_(2)),and the w(CrO_(x))in spinel also reduced,but the content of melilite increased.The distribution ratio of Cr between slag and alloy decreased with the increase of slag basicity at 1600℃,meansning that increasing the w(CaO)/w(SiO_(2))of slag can improve the recovery of Cr in chromite smelting process.
基金Projects(51264023,51364020,U1202271)supported by the National Natural Science Foundation of ChinaProject(IRT1250)supported by the Program for Innovative Research Team in University of Ministry of Education of ChinaProject(2014HA003)supported by the Science and Technology Leading Talent of Yunnan Province,China
文摘The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.