The corrosion rate,together with corrosive wear and corrosion coefficient under load,of alloy CD-4MCu in 69% H_3PO_4 or 69% H_3PO_4+500 ppm NaCl solution measured,and the morphology of their wear tracks was then obser...The corrosion rate,together with corrosive wear and corrosion coefficient under load,of alloy CD-4MCu in 69% H_3PO_4 or 69% H_3PO_4+500 ppm NaCl solution measured,and the morphology of their wear tracks was then observed by SEM.The alloy CD-4MCu is revealed to be superior in corrosive wear resistance to stainless steel 304 and even to Carpenter 20Cb3,a high corrosion resisting alloy.From its features of duplex phase structure,it could be suggested that the weight loss related to mechanical factor was improved by existence of austenitic phase due to its deformation strengthening.展开更多
在强光照射下,CdS量子点易发生光腐蚀现象,通过金属掺杂和复合的方式可以提高CdS的光催化性能和光稳定性。采用水热法合成了Zn掺杂CdS/g-C_(3)N_(4)复合纳米材料(Zn-CdS/g-C_(3)N_(4))。利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、...在强光照射下,CdS量子点易发生光腐蚀现象,通过金属掺杂和复合的方式可以提高CdS的光催化性能和光稳定性。采用水热法合成了Zn掺杂CdS/g-C_(3)N_(4)复合纳米材料(Zn-CdS/g-C_(3)N_(4))。利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)和傅里叶变换红外光谱(FT-IR)等手段对Zn-CdS/g-C_(3)N_(4)复合材料的形貌、结构和组成等进行了表征。结果表明,Zn-CdS纳米颗粒附着在g-C_(3)N_(4)表面上,从而形成Zn-CdS/g-C_(3)N_(4)复合材料,且复合后材料带隙减小,光生电子-空穴复合率降低。在500 W Xe灯照射下,研究了Zn-CdS/g-C_(3)N_(4)对罗丹明B(RhB)的光催化降解性能。在最优条件下,光照40 min后,所制备的Zn-CdS/g-C_(3)N_(4)对RhB的光催化降解效率达99%。此外,所合成的Zn-CdS/g-C_(3)N_(4)复合材料光稳定性较高、可再生性好。这归因于Zn和Cd的协同作用以及与g-C_(3)N_(4)的复合,促进了光生载流子的分离和转移。展开更多
A simple two-step hydrothermal method synthesized four different CdS/Fe_(3)O_(4)photocatalysts with varying ratios of mass of CdS to Fe_(3)O_(4).The composition and morphology of the prepared samples were investigated...A simple two-step hydrothermal method synthesized four different CdS/Fe_(3)O_(4)photocatalysts with varying ratios of mass of CdS to Fe_(3)O_(4).The composition and morphology of the prepared samples were investigated using X-ray diffraction(XRD),Raman spectrum,X-ray photoelectron spectroscopy(XPS),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).Solid UV reflectance spectra testing found that CdS/Fe_(3)O_(4)nanocomposites had good light absorption throughout the spectral range,promoting their photocatalytic properties.Under visible light irradiation,CdS/Fe_(3)O_(4)(2∶5)with a mass ratio of 2∶5 exhibited excellent photocatalytic perfor-mance,with a degradation rate of 98.8%for rhodamine B.Furthermore,after five cycles of photocatalytic degrada-tion reaction,the rhodamine B degradation rate remained at 96.2%,indicating that the photocatalysts have good pho-tocatalytic stability.展开更多
文摘The corrosion rate,together with corrosive wear and corrosion coefficient under load,of alloy CD-4MCu in 69% H_3PO_4 or 69% H_3PO_4+500 ppm NaCl solution measured,and the morphology of their wear tracks was then observed by SEM.The alloy CD-4MCu is revealed to be superior in corrosive wear resistance to stainless steel 304 and even to Carpenter 20Cb3,a high corrosion resisting alloy.From its features of duplex phase structure,it could be suggested that the weight loss related to mechanical factor was improved by existence of austenitic phase due to its deformation strengthening.
文摘在强光照射下,CdS量子点易发生光腐蚀现象,通过金属掺杂和复合的方式可以提高CdS的光催化性能和光稳定性。采用水热法合成了Zn掺杂CdS/g-C_(3)N_(4)复合纳米材料(Zn-CdS/g-C_(3)N_(4))。利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)和傅里叶变换红外光谱(FT-IR)等手段对Zn-CdS/g-C_(3)N_(4)复合材料的形貌、结构和组成等进行了表征。结果表明,Zn-CdS纳米颗粒附着在g-C_(3)N_(4)表面上,从而形成Zn-CdS/g-C_(3)N_(4)复合材料,且复合后材料带隙减小,光生电子-空穴复合率降低。在500 W Xe灯照射下,研究了Zn-CdS/g-C_(3)N_(4)对罗丹明B(RhB)的光催化降解性能。在最优条件下,光照40 min后,所制备的Zn-CdS/g-C_(3)N_(4)对RhB的光催化降解效率达99%。此外,所合成的Zn-CdS/g-C_(3)N_(4)复合材料光稳定性较高、可再生性好。这归因于Zn和Cd的协同作用以及与g-C_(3)N_(4)的复合,促进了光生载流子的分离和转移。
文摘A simple two-step hydrothermal method synthesized four different CdS/Fe_(3)O_(4)photocatalysts with varying ratios of mass of CdS to Fe_(3)O_(4).The composition and morphology of the prepared samples were investigated using X-ray diffraction(XRD),Raman spectrum,X-ray photoelectron spectroscopy(XPS),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).Solid UV reflectance spectra testing found that CdS/Fe_(3)O_(4)nanocomposites had good light absorption throughout the spectral range,promoting their photocatalytic properties.Under visible light irradiation,CdS/Fe_(3)O_(4)(2∶5)with a mass ratio of 2∶5 exhibited excellent photocatalytic perfor-mance,with a degradation rate of 98.8%for rhodamine B.Furthermore,after five cycles of photocatalytic degrada-tion reaction,the rhodamine B degradation rate remained at 96.2%,indicating that the photocatalysts have good pho-tocatalytic stability.