Pt/BaO/Al_2O_3 catalysts with different BaO loadings prepared from Al_2O_3 nanorods(Pt/BaO/Al_2O_3-nr) and irregular Al_2O_3 nanoparticles(Pt/BaO/Al_2O_3-np) were investigated for NOx storage and reduction(NSR). The P...Pt/BaO/Al_2O_3 catalysts with different BaO loadings prepared from Al_2O_3 nanorods(Pt/BaO/Al_2O_3-nr) and irregular Al_2O_3 nanoparticles(Pt/BaO/Al_2O_3-np) were investigated for NOx storage and reduction(NSR). The Pt/BaO/Al_2O_3 materials derived from Al_2O_3 nanorods always exhibited much higher NOx storage capacity(NSC) over the whole temperature range of 100–400°C than the corresponding Pt/BaO/Al_2O_3-np samples containing the same BaO loading, giving the maximum NSC value of 966.9 μmol/gcatat 400°C, 1.4 times higher than that of Pt/BaO/Al_2O_3-np. Higher catalytic performance of nanorod-supported NSR samples was also observed during lean-rich cyclic conditions(90 sec vs. 5 sec), giving more than 98% NOx conversion at 300–450°C over the Pt/BaO/Al_2O_3-nr sample with 15% BaO loading. To reveal this dependence on the shape of the support during the NSR process, a series of characterization techniques including the Brunauer–Emmett–Teller(BET) method,X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), H_2 temperature programmed reduction(H2-TPR), and in situ diffuse reflectance infrared Fourier transform spectroscopy(DRIFTS) were also conducted. It was found that intimate contact of Ba–Al and Ba–Pt sites was achieved over the Pt/BaO/Al_2O_3 surface when using Al_2O_3-nr as a support.This strong interaction among the multi-components of Pt/BaO/Al_2O_3-nr thus triggered the formation of surface nitrite and nitrate during the lean period, and also accelerated the reverse spillover of ad-NOxspecies onto the Pt surface, enhancing their reduction and leading to high NSR performance.展开更多
Bi0.9Ba0.lFeO3 （BBFO）/La2/3Srl/3MnO3 （LSMO） heterostructures are fabricated on LaA103 （100） substrates by pulsed laser deposition. Giant remnant polarization value （~ 85 μC/cm2） and large saturated magnetizat...Bi0.9Ba0.lFeO3 （BBFO）/La2/3Srl/3MnO3 （LSMO） heterostructures are fabricated on LaA103 （100） substrates by pulsed laser deposition. Giant remnant polarization value （~ 85 μC/cm2） and large saturated magnetization value （~ 12.4 emu/cm3） for BBFO/LSMO heterostructures are demonstrated at room temperature. Mixed ferroelectric domain structures and low leakage current are observed and in favor of enhanced ferroelectrie properties in the BBFO/LSMO het- erostructures. The magnetic field-dependent magnetization measurements reveal the enhancement in the magnetic moment and improved magnetic hysteresis loop originating from the BBFO/LSMO interface. The heterostructure is proved to be effective in enhancing the ferroelectric and ferromagnetic performances in multiferroic BFO films at room temperature.展开更多
基金supported by the National Natural Science Foundation of China (Nos.21673277 and 21637005)the National Key R&D Program of China (No.2017YFC0211105)+1 种基金the Science and Technology Program of Tianjin,China (No.16YFXTSF00290)the K.C.Wong Education Foundation
文摘Pt/BaO/Al_2O_3 catalysts with different BaO loadings prepared from Al_2O_3 nanorods(Pt/BaO/Al_2O_3-nr) and irregular Al_2O_3 nanoparticles(Pt/BaO/Al_2O_3-np) were investigated for NOx storage and reduction(NSR). The Pt/BaO/Al_2O_3 materials derived from Al_2O_3 nanorods always exhibited much higher NOx storage capacity(NSC) over the whole temperature range of 100–400°C than the corresponding Pt/BaO/Al_2O_3-np samples containing the same BaO loading, giving the maximum NSC value of 966.9 μmol/gcatat 400°C, 1.4 times higher than that of Pt/BaO/Al_2O_3-np. Higher catalytic performance of nanorod-supported NSR samples was also observed during lean-rich cyclic conditions(90 sec vs. 5 sec), giving more than 98% NOx conversion at 300–450°C over the Pt/BaO/Al_2O_3-nr sample with 15% BaO loading. To reveal this dependence on the shape of the support during the NSR process, a series of characterization techniques including the Brunauer–Emmett–Teller(BET) method,X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), H_2 temperature programmed reduction(H2-TPR), and in situ diffuse reflectance infrared Fourier transform spectroscopy(DRIFTS) were also conducted. It was found that intimate contact of Ba–Al and Ba–Pt sites was achieved over the Pt/BaO/Al_2O_3 surface when using Al_2O_3-nr as a support.This strong interaction among the multi-components of Pt/BaO/Al_2O_3-nr thus triggered the formation of surface nitrite and nitrate during the lean period, and also accelerated the reverse spillover of ad-NOxspecies onto the Pt surface, enhancing their reduction and leading to high NSR performance.
基金supported by the National Natural Science Foundation of China(Grant No.61078057)the Natural Science Foundation of Shannxi Province,China(Grant No.2011GM6013)+2 种基金the Foundation for Fundamental Research of Northwestern Polytechnical University of China(Grant Nos.JC20110270 and 3102014JCQ01029)the Open Project of Key Laboratory for Magnetism and Magnetic Materials of Ministry of Education,Lanzhou University,China(Grant Nos.LZUMMM2013001 and LZUMMM2014007)the Scholarship Fund of China(Grant No.201303070058)
文摘Bi0.9Ba0.lFeO3 （BBFO）/La2/3Srl/3MnO3 （LSMO） heterostructures are fabricated on LaA103 （100） substrates by pulsed laser deposition. Giant remnant polarization value （~ 85 μC/cm2） and large saturated magnetization value （~ 12.4 emu/cm3） for BBFO/LSMO heterostructures are demonstrated at room temperature. Mixed ferroelectric domain structures and low leakage current are observed and in favor of enhanced ferroelectrie properties in the BBFO/LSMO het- erostructures. The magnetic field-dependent magnetization measurements reveal the enhancement in the magnetic moment and improved magnetic hysteresis loop originating from the BBFO/LSMO interface. The heterostructure is proved to be effective in enhancing the ferroelectric and ferromagnetic performances in multiferroic BFO films at room temperature.