To improve the high-temperature oxidation resistance of TiAlNb9 alloy,a Cr-Al-Y co-deposition coating was prepared on the alloy surface by the pack cementation method.The microstructure of the coating was analyzed by ...To improve the high-temperature oxidation resistance of TiAlNb9 alloy,a Cr-Al-Y co-deposition coating was prepared on the alloy surface by the pack cementation method.The microstructure of the coating was analyzed by scanning electron microscope,energy dispersive spectrometer,and X-ray diffractometer,and the high-temperature oxidation properties of the substrate and coating at 1273 K were compared and studied.The results show that the Cr-Al-Y coating is about 30μm in thickness,and it has a dense structure and good film-substrate bonding.The coating includes an outer layer composed of TiCr_(2),TiCr,Ti_(4)Cr,and(Ti,Nb)Cr_(4) phases as well as an inner layer composed of Ti_(2)Al,and Nb-richγ-TiAl interdiffusion zone.The TiAlNb9 substrate forms an oxide layer composed of TiO_(2) and Al_(2)O_(3) at 1273 K.Due to its loose and porous structure,TiO_(2) oxide film cannot effectively isolate the internal diffusion of element O,resulting in continuous oxidation damage to the substrate.The Cr-Al-Y co-deposition coating forms a dense Cr_(2)O_(3) and Al_(2)O_(3) oxide layer during oxidation,effectively preventing the internal diffusion of element O and significantly improving the high-temperature oxidation resistance of the substrate alloy.展开更多
为了分析Al-Y-Fe三元合金的玻璃形成能力和热稳定性,采用熔体急冷法制备了Al(100-2x)YxFex(其中x=3,4,5,6,7,8,9)、Al89Y5Fe6、Al88Y5Fe7和Al87Y5Fe8合金条带.利用x-射线衍射(XRD)及透射电子显微镜(TEM)表征了急冷态和部分晶化后条带的...为了分析Al-Y-Fe三元合金的玻璃形成能力和热稳定性,采用熔体急冷法制备了Al(100-2x)YxFex(其中x=3,4,5,6,7,8,9)、Al89Y5Fe6、Al88Y5Fe7和Al87Y5Fe8合金条带.利用x-射线衍射(XRD)及透射电子显微镜(TEM)表征了急冷态和部分晶化后条带的结构,运用示差扫描量热仪(DSC)分析了合金的玻璃转变和晶化行为.结果表明,Al88Y6Fe6、Al84Y7Fe7、Al89Y5Fe6和Al88Y5Fe7可以形成完全非晶合金;Al88Y5Fe7非晶合金280℃等温退火30 min析出纳米尺寸Al晶体,370℃等温退火30 min Al晶体发生进一步长大并有金属间化合物析出.展开更多
基金National Natural Science Foundation of China(52161009)Innovation Project of Postgraduate Students in North Minzu University(YCX24104)。
文摘To improve the high-temperature oxidation resistance of TiAlNb9 alloy,a Cr-Al-Y co-deposition coating was prepared on the alloy surface by the pack cementation method.The microstructure of the coating was analyzed by scanning electron microscope,energy dispersive spectrometer,and X-ray diffractometer,and the high-temperature oxidation properties of the substrate and coating at 1273 K were compared and studied.The results show that the Cr-Al-Y coating is about 30μm in thickness,and it has a dense structure and good film-substrate bonding.The coating includes an outer layer composed of TiCr_(2),TiCr,Ti_(4)Cr,and(Ti,Nb)Cr_(4) phases as well as an inner layer composed of Ti_(2)Al,and Nb-richγ-TiAl interdiffusion zone.The TiAlNb9 substrate forms an oxide layer composed of TiO_(2) and Al_(2)O_(3) at 1273 K.Due to its loose and porous structure,TiO_(2) oxide film cannot effectively isolate the internal diffusion of element O,resulting in continuous oxidation damage to the substrate.The Cr-Al-Y co-deposition coating forms a dense Cr_(2)O_(3) and Al_(2)O_(3) oxide layer during oxidation,effectively preventing the internal diffusion of element O and significantly improving the high-temperature oxidation resistance of the substrate alloy.
文摘为了分析Al-Y-Fe三元合金的玻璃形成能力和热稳定性,采用熔体急冷法制备了Al(100-2x)YxFex(其中x=3,4,5,6,7,8,9)、Al89Y5Fe6、Al88Y5Fe7和Al87Y5Fe8合金条带.利用x-射线衍射(XRD)及透射电子显微镜(TEM)表征了急冷态和部分晶化后条带的结构,运用示差扫描量热仪(DSC)分析了合金的玻璃转变和晶化行为.结果表明,Al88Y6Fe6、Al84Y7Fe7、Al89Y5Fe6和Al88Y5Fe7可以形成完全非晶合金;Al88Y5Fe7非晶合金280℃等温退火30 min析出纳米尺寸Al晶体,370℃等温退火30 min Al晶体发生进一步长大并有金属间化合物析出.