Pressure histories were tested in a 500-L chamber to identify the pressure load in confined explosion from aluminized explosives. Different aluminized explosives with Al/O, ranging from 0.25 to 1.23, were used. The re...Pressure histories were tested in a 500-L chamber to identify the pressure load in confined explosion from aluminized explosives. Different aluminized explosives with Al/O, ranging from 0.25 to 1.23, were used. The recorded pressure curves could express the reflection of initial shock wave and the after burning combustion of aluminum. As there is no objective way to gain quasi-static pressure(P_(QS)),method of multipoint averaging was used in smoothing the original pressure curves to gain the P_(QS). The P_(QS),rising time of pressure(t_(QS)) which stands for the duration of the initial reflected shock wave, and attenuation coefficient(ω) which stands for the supportive effects of the combustion of aluminum to the P_(QS) are used to characterize the pressure load in the confined explosion from aluminized explosives. The research results showed that the Al/O significantly affected the three characteristic quantities. With the increase of Al/O, the P_(QS) increased at first and decreased later, gaining maximum at Al/O=0.99; the t_(QS)sustained growth and the ω decreased at first and increased later, gaining minimum at AI/O=0.99.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
文摘Pressure histories were tested in a 500-L chamber to identify the pressure load in confined explosion from aluminized explosives. Different aluminized explosives with Al/O, ranging from 0.25 to 1.23, were used. The recorded pressure curves could express the reflection of initial shock wave and the after burning combustion of aluminum. As there is no objective way to gain quasi-static pressure(P_(QS)),method of multipoint averaging was used in smoothing the original pressure curves to gain the P_(QS). The P_(QS),rising time of pressure(t_(QS)) which stands for the duration of the initial reflected shock wave, and attenuation coefficient(ω) which stands for the supportive effects of the combustion of aluminum to the P_(QS) are used to characterize the pressure load in the confined explosion from aluminized explosives. The research results showed that the Al/O significantly affected the three characteristic quantities. With the increase of Al/O, the P_(QS) increased at first and decreased later, gaining maximum at Al/O=0.99; the t_(QS)sustained growth and the ω decreased at first and increased later, gaining minimum at AI/O=0.99.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。