Sm(Co_(bal)Fe_(0.245)Cu_(0.07)Zr_(0.02))7.8(at%)sintered magnets with high remanence(B_(r)~1.15 T)were prepared using a traditional powder metallurgy method.Tunable magnetic properties,especially intrinsic coercivity(...Sm(Co_(bal)Fe_(0.245)Cu_(0.07)Zr_(0.02))7.8(at%)sintered magnets with high remanence(B_(r)~1.15 T)were prepared using a traditional powder metallurgy method.Tunable magnetic properties,especially intrinsic coercivity(H_(cj)),were obtained through adjusting isothermal procedure parameters.H_(cj)of the magnets increases from 305 to 752 kA·m^(-1)with isothermal annealing time increasing from 3 to 20 h,while B_(r) of the magnets almost keeps constant.From the bright field transmission electron microscopy(TEM)images,it is found that:(1)there is dispersed precipitated phase with very small size in the magnet annealed for 3 h,while the magnets annealed for 20 h have distinct and intact cellular structure;(2)the number density of Z-phase in magnet annealed for 20 h is bigger than that for 3 h.Besides,the finer microstructures were studied with high-resolution transmission electron microscopy(HRTEM).展开更多
The effect of Sm-rich liquid phase （Sm2Co3） on magnetic properties and microstructure of 2：17-type Sin-Co magnet was studied. Three phases existed in liquid phase ingot, and took on white, dark grey and grey, respe...The effect of Sm-rich liquid phase （Sm2Co3） on magnetic properties and microstructure of 2：17-type Sin-Co magnet was studied. Three phases existed in liquid phase ingot, and took on white, dark grey and grey, respectively. It was found that the composition of the grey area was similar to the nominal one. Our results indicated that the optimal composition was obtained at 3 wt.% liquid phase added, and the magnetic properties were B^I 1.58 kGs, Hci〉26 kOe, （BH）m=29.51 MGOe. Br increased by 3%, Hci was 13 times larger, and （B/-/）m was 6 times bigger than none liquid phase magnets. Moreover, with the aging time decreasing from 20 to 8 h, the squareness of the demagnetization curves got better, while the coercivity of the samples decreased. It revealed that Sm（Co,Cu）5 phase also precipitated at particle boundaries. It maybe also enhanced the coercivity.展开更多
In order to counteract the demagnetization caused by eddy current loss,widespread attention has been devoted to increasing the resistivity of permanent magnets.We prepared 2:17-type Sm Co magnets doped with different ...In order to counteract the demagnetization caused by eddy current loss,widespread attention has been devoted to increasing the resistivity of permanent magnets.We prepared 2:17-type Sm Co magnets doped with different ZrO_(2)contents and investigated the influence of the ZrO_(2)content on the magnetic properties and resistive anisotropism.The results showed that not only was the resistivity of the magnet improved,but,in addition,the coercivity of the magnet was significantly increased.The microstructure was studied with TEM,which showed that ZrO_(2)doping was able to cause a decrease in the lamellar phase density and the growth of cellular structures.The increased grain boundaries and Sm_(2)O_(3)phases were favorable to the improvement of resistivity.The decrease of the lamellar phases caused a narrowing of the resistive anisotropism.The additional Cu in the center of the cellular boundaries was the main reason for the enhancement of Hcj.However,an excessive amount caused an increase of the Zr_6(Fe Co)_(23)phase and a deterioration of the cellular structure,thereby leading to a decrease in coercivity.展开更多
基金the National Basic Research Program of China(No.2014CB643701)the National Natural Science Foundation of China(No.51171048)。
文摘Sm(Co_(bal)Fe_(0.245)Cu_(0.07)Zr_(0.02))7.8(at%)sintered magnets with high remanence(B_(r)~1.15 T)were prepared using a traditional powder metallurgy method.Tunable magnetic properties,especially intrinsic coercivity(H_(cj)),were obtained through adjusting isothermal procedure parameters.H_(cj)of the magnets increases from 305 to 752 kA·m^(-1)with isothermal annealing time increasing from 3 to 20 h,while B_(r) of the magnets almost keeps constant.From the bright field transmission electron microscopy(TEM)images,it is found that:(1)there is dispersed precipitated phase with very small size in the magnet annealed for 3 h,while the magnets annealed for 20 h have distinct and intact cellular structure;(2)the number density of Z-phase in magnet annealed for 20 h is bigger than that for 3 h.Besides,the finer microstructures were studied with high-resolution transmission electron microscopy(HRTEM).
基金supported by the National Natural Science Foundation of China (50871032)National High Technology Research and Development Program of ChinaProgram of Beijing Municipal Science & Technology
文摘The effect of Sm-rich liquid phase （Sm2Co3） on magnetic properties and microstructure of 2：17-type Sin-Co magnet was studied. Three phases existed in liquid phase ingot, and took on white, dark grey and grey, respectively. It was found that the composition of the grey area was similar to the nominal one. Our results indicated that the optimal composition was obtained at 3 wt.% liquid phase added, and the magnetic properties were B^I 1.58 kGs, Hci〉26 kOe, （BH）m=29.51 MGOe. Br increased by 3%, Hci was 13 times larger, and （B/-/）m was 6 times bigger than none liquid phase magnets. Moreover, with the aging time decreasing from 20 to 8 h, the squareness of the demagnetization curves got better, while the coercivity of the samples decreased. It revealed that Sm（Co,Cu）5 phase also precipitated at particle boundaries. It maybe also enhanced the coercivity.
基金the National Natural Science Foundation of China(Grant No.51877094)Ningbo Science and Technology Project(Grant No.2014B11009)。
文摘In order to counteract the demagnetization caused by eddy current loss,widespread attention has been devoted to increasing the resistivity of permanent magnets.We prepared 2:17-type Sm Co magnets doped with different ZrO_(2)contents and investigated the influence of the ZrO_(2)content on the magnetic properties and resistive anisotropism.The results showed that not only was the resistivity of the magnet improved,but,in addition,the coercivity of the magnet was significantly increased.The microstructure was studied with TEM,which showed that ZrO_(2)doping was able to cause a decrease in the lamellar phase density and the growth of cellular structures.The increased grain boundaries and Sm_(2)O_(3)phases were favorable to the improvement of resistivity.The decrease of the lamellar phases caused a narrowing of the resistive anisotropism.The additional Cu in the center of the cellular boundaries was the main reason for the enhancement of Hcj.However,an excessive amount caused an increase of the Zr_6(Fe Co)_(23)phase and a deterioration of the cellular structure,thereby leading to a decrease in coercivity.
文摘目的探讨2型糖尿病(T2DM)大血管病变患者血清IL-17的表达水平及意义。方法 162例T2DM患者,根据是否合并大血管病变,分为大血管病变组90例和无血管病变组72例,另选同期健康查体者68例作为正常对照组。采用酶联免疫吸附法(ELISA)测定三组人群空腹静脉血中IL-17水平,统计IL-17与各临床指标间的关系,分析其影响因素。同时,根据T2DM大血管病变患者颈动脉内膜中层厚度,探讨有无颈动脉增厚对IL-17水平的影响。结果 T2DM合并大血管病变组血清IL-17水平显著高于无血管病变组及正常对照组,T2DM无大血管病变组高于正常对照组(P<0.01)。T2DM大血管病变患者中,颈动脉增厚组IL-17水平明显高于无颈动脉增厚组(P<0.05)。在大血管病变组IL-17与BMI、2 h PG、hs-CRP、TG、LDL-C呈正相关,而与HDL-C呈负相关。多元逐步回归分析显示IL-17、hs-CRP和LDL-C是T2DM大血管病变的主要影响因素。结论T2DM大血管病变组和颈动脉增厚组血清IL-17表达均增高,提示IL-17参与糖尿病大血管病变的炎症反应过程。IL-17可能是T2DM大血管病变的独立危险因素,在糖尿病大血管病变发生、发展中发挥重要作用。