An optimized low-temperature chromizing process at 500℃ was realized on a plain medium-carbon steel with 0.45 wt pct carbon via a duplex chromizing process which consists of a precursor plasma nitriding, and a follow...An optimized low-temperature chromizing process at 500℃ was realized on a plain medium-carbon steel with 0.45 wt pct carbon via a duplex chromizing process which consists of a precursor plasma nitriding, and a followed salt bath thermoreactive deposition and diffusion （TRD） chromizing process. CrN layer with a thin diffusion layer underneath was formed. The duplex chromizing process was studied by optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. It was found that the chromizing speed at 500℃ was successfully enhanced by adding more Cr-Fe powders into the salt bath, and the CrN layer formed at the cost of the prior nitride compound layer. A CrN layer with average 8.1/~m in thickness and 1382 HV0.01 in microhardness was formed on the substrate by duplex chromizing at 500℃ for 24 h. Further more, the CrN layer consisted of nanocrystalline CrN grains.展开更多
Conventional titanium alloy may be ignited and burnt under high temperature, high pressure and high gas flow velocity condition. In order to avoid this problem,burn-resistant alloying layers were made on the surface o...Conventional titanium alloy may be ignited and burnt under high temperature, high pressure and high gas flow velocity condition. In order to avoid this problem,burn-resistant alloying layers were made on the surface of Ti-6Al-4V and Ti-6.5Al-0.3Mo-1.5Zr-0.25Si titanium alloys by using double glow plasma surface alloying technology (DG Technology). Two typical burn-resistant layers Ti-Cr and Ti-Mo were made by DG plasma chromizing and DG plasma molybdenizing, respectively. Burn-resistant properties were tested by layer ignition method using 2 kW laser machine. Ignition experiments result reveals that the ignition temperature of alloyed layer with Mo and Cr concentration above 10% is about 200℃higher than ignition temperature of Ti-6Al-4V substrate.展开更多
基金This work was financially supported by the National Natural Science Foundation of China(Granted No.50671038).
文摘An optimized low-temperature chromizing process at 500℃ was realized on a plain medium-carbon steel with 0.45 wt pct carbon via a duplex chromizing process which consists of a precursor plasma nitriding, and a followed salt bath thermoreactive deposition and diffusion （TRD） chromizing process. CrN layer with a thin diffusion layer underneath was formed. The duplex chromizing process was studied by optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. It was found that the chromizing speed at 500℃ was successfully enhanced by adding more Cr-Fe powders into the salt bath, and the CrN layer formed at the cost of the prior nitride compound layer. A CrN layer with average 8.1/~m in thickness and 1382 HV0.01 in microhardness was formed on the substrate by duplex chromizing at 500℃ for 24 h. Further more, the CrN layer consisted of nanocrystalline CrN grains.
基金Project(50271045) supported by the National Natural Science Foundation of China
文摘Conventional titanium alloy may be ignited and burnt under high temperature, high pressure and high gas flow velocity condition. In order to avoid this problem,burn-resistant alloying layers were made on the surface of Ti-6Al-4V and Ti-6.5Al-0.3Mo-1.5Zr-0.25Si titanium alloys by using double glow plasma surface alloying technology (DG Technology). Two typical burn-resistant layers Ti-Cr and Ti-Mo were made by DG plasma chromizing and DG plasma molybdenizing, respectively. Burn-resistant properties were tested by layer ignition method using 2 kW laser machine. Ignition experiments result reveals that the ignition temperature of alloyed layer with Mo and Cr concentration above 10% is about 200℃higher than ignition temperature of Ti-6Al-4V substrate.