Reinforced Baked Clay (RBC) seems to be potential alternative of Reinforced Cement Concrete (RCC) for construction of low cost houses. In order to utilize RBC as a construction material for buildings, it is necessary ...Reinforced Baked Clay (RBC) seems to be potential alternative of Reinforced Cement Concrete (RCC) for construction of low cost houses. In order to utilize RBC as a construction material for buildings, it is necessary to understand compression behaviour of baked clay. In this paper, relation between cube crushing strength and cylinder strength of baked clay is presented. For this purpose, clay beams were cast in a mould and compacted at a pressure of 6 MPa. The clay beams were dried and fired in a kiln at a temperature of 900?C. Cubes of 150 mm size were sawed from a baked clay beam. Cylinders of 150 mm diameter and 300 mm height were cut, from another baked clay beam, using core cutter machine. Both the cubes and cylinders were tested for compressive strength in Universal Testing Machine. The results showed that the cube crushing strength of baked clay was 25 MPa and the ratio of the compressive strength of the cylinders and the cubes was found to be 0.6. Suggestions for improvement of compressive strength of baked clay cylinders are also discussed.展开更多
Failure of concrete structures leading to collapse of buildings has initiated various researches on the quality of construction materials. Collapse of buildings resulting to injuries, loss of lives and investments has...Failure of concrete structures leading to collapse of buildings has initiated various researches on the quality of construction materials. Collapse of buildings resulting to injuries, loss of lives and investments has been largely attributed to use of poor quality concrete ingredients. Information on the effect of silt and clay content and organic impurities present in building sand being supplied in Nairobi County and its environs as well as their effect to the compressive strength of concrete was lacking. The objective of this research was to establish level of silt, clay and organic impurities present in building sand and its effect on compressive strength of concrete. This paper presents the findings on the quality of building sand as sourced from eight supply points in Nairobi County and its environs and the effects of these sand impurities to the compressive strength of concrete. 27 sand samples were tested for silt and clay contents and organic impurities in accordance with BS 882 and ASTM C40 respectively after which 13 sand samples with varying level of impurities were selected for casting of concrete cubes. 150 mm × 150 mm × 150 mm concrete cubes were cast using concrete mix of 1:1.5:3:0.57 (cement:sand:coarse aggregates:water) and were tested for compressive strength at the age of 7, 14 and 28 days. The investigation used cement, coarse aggregates (crushed stones) and water of similar characteristics while sand used had varying levels of impurities and particle shapes and texture. The results of the investigations showed that 86.2% of the sand samples tested exceeded the allowable limit of silt and clay content while 77% exceeded the organic content limit. The level of silt and clay content ranged from 42% to 3.3% for while organic impurities ranged from 0.029 to 0.738 photometric ohms for the unwashed sand samples. With regard to compressive strength, 38% of the concrete cubes made from sand with varying sand impurities failed to meet the design strength of 25 Mpa at the age of 28 days. A combined regression equation of with R2 = 0.444 was generated predicting compressive strength varying levels of silt and clay impurities (SCI), and organic impurities (ORG) in sand. This implies that 44% of concrete’s compressive strength is contributed by combination of silt and clay content and organic impurities in sand. Other factors such as particle shapes, texture, workability and mode of sand formation also play a key role in determination of concrete strength. It is concluded that sand found in Nairobi County and its environs contain silt and clay content and organic impurities that exceed the allowable limits and these impurities result in significant reduction in concrete’s compressive strength. It is recommended that the concrete design mix should always consider the strength reduction due to presence of these impurities to ensure that target strength of the resultant concrete is achieved. Formulation of policies governing monitoring of quality of building sand in Kenya and other developed countries is recommended.展开更多
文摘Reinforced Baked Clay (RBC) seems to be potential alternative of Reinforced Cement Concrete (RCC) for construction of low cost houses. In order to utilize RBC as a construction material for buildings, it is necessary to understand compression behaviour of baked clay. In this paper, relation between cube crushing strength and cylinder strength of baked clay is presented. For this purpose, clay beams were cast in a mould and compacted at a pressure of 6 MPa. The clay beams were dried and fired in a kiln at a temperature of 900?C. Cubes of 150 mm size were sawed from a baked clay beam. Cylinders of 150 mm diameter and 300 mm height were cut, from another baked clay beam, using core cutter machine. Both the cubes and cylinders were tested for compressive strength in Universal Testing Machine. The results showed that the cube crushing strength of baked clay was 25 MPa and the ratio of the compressive strength of the cylinders and the cubes was found to be 0.6. Suggestions for improvement of compressive strength of baked clay cylinders are also discussed.
文摘Failure of concrete structures leading to collapse of buildings has initiated various researches on the quality of construction materials. Collapse of buildings resulting to injuries, loss of lives and investments has been largely attributed to use of poor quality concrete ingredients. Information on the effect of silt and clay content and organic impurities present in building sand being supplied in Nairobi County and its environs as well as their effect to the compressive strength of concrete was lacking. The objective of this research was to establish level of silt, clay and organic impurities present in building sand and its effect on compressive strength of concrete. This paper presents the findings on the quality of building sand as sourced from eight supply points in Nairobi County and its environs and the effects of these sand impurities to the compressive strength of concrete. 27 sand samples were tested for silt and clay contents and organic impurities in accordance with BS 882 and ASTM C40 respectively after which 13 sand samples with varying level of impurities were selected for casting of concrete cubes. 150 mm × 150 mm × 150 mm concrete cubes were cast using concrete mix of 1:1.5:3:0.57 (cement:sand:coarse aggregates:water) and were tested for compressive strength at the age of 7, 14 and 28 days. The investigation used cement, coarse aggregates (crushed stones) and water of similar characteristics while sand used had varying levels of impurities and particle shapes and texture. The results of the investigations showed that 86.2% of the sand samples tested exceeded the allowable limit of silt and clay content while 77% exceeded the organic content limit. The level of silt and clay content ranged from 42% to 3.3% for while organic impurities ranged from 0.029 to 0.738 photometric ohms for the unwashed sand samples. With regard to compressive strength, 38% of the concrete cubes made from sand with varying sand impurities failed to meet the design strength of 25 Mpa at the age of 28 days. A combined regression equation of with R2 = 0.444 was generated predicting compressive strength varying levels of silt and clay impurities (SCI), and organic impurities (ORG) in sand. This implies that 44% of concrete’s compressive strength is contributed by combination of silt and clay content and organic impurities in sand. Other factors such as particle shapes, texture, workability and mode of sand formation also play a key role in determination of concrete strength. It is concluded that sand found in Nairobi County and its environs contain silt and clay content and organic impurities that exceed the allowable limits and these impurities result in significant reduction in concrete’s compressive strength. It is recommended that the concrete design mix should always consider the strength reduction due to presence of these impurities to ensure that target strength of the resultant concrete is achieved. Formulation of policies governing monitoring of quality of building sand in Kenya and other developed countries is recommended.