Iron（Ⅲ）-doped nanostructure TiO2-coated SiO2 （TiO2/SiO2） particles were prepared using the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized employing...Iron（Ⅲ）-doped nanostructure TiO2-coated SiO2 （TiO2/SiO2） particles were prepared using the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized employing the sol-gel method with TiChas a precursor. The samples were characterized by Fourier transform infrared spectroscopy （FTIR）, SEM, EDS, XPS, and XRD. The experimental results show that TiO2 nanopowders on the surface of SiO2 particles are well distributed, the amount of TiO2 is increased with the adding of coating layers, the pure anatase-TiO2 coating layers are synthesized at 500℃, and the photocatalytic activity of Fe^3＋-doped TiO2/SiO2 is higher than that of undoped TiO2/SiO2.展开更多
To research the influence of oxygen flow rate on the structural and optical properties of TiO2 thin film,TiO2 films on glass were deposited by reactive magnetron sputtering.The microstructure and optical properties we...To research the influence of oxygen flow rate on the structural and optical properties of TiO2 thin film,TiO2 films on glass were deposited by reactive magnetron sputtering.The microstructure and optical properties were measured by X-ray diffractometry,AFM and UV-VIS transmittance spectroscopy,respectively.The results show that the films deposited at oxygen flow rate of 10 mL/min has the lowest roughness and the highest transmittance.The absorption angle shifts to longer wavelengths as oxygen flow rates increase from 5 to 10 mL/min,then to shorter ones as the oxygen flow rate increase from 10 to 30 mL/min.The band gap is 3.38 eV,which is nearly constant in the experiment.For the TiO2 thin films deposited at 10 mL/min of oxyge flow rate,there are nano-crystalline structures,which are suitable for anti-reflection(AR) coating in the solar cells structure system.展开更多
Anti-reflective (AR) single layer of silica-titania (SiO2-TiO2) coatings were obtained from sols containing pyromellitic dianhydride (PMDA) derivatives and Ti and Si precursors on glass substrate by dip-coating method...Anti-reflective (AR) single layer of silica-titania (SiO2-TiO2) coatings were obtained from sols containing pyromellitic dianhydride (PMDA) derivatives and Ti and Si precursors on glass substrate by dip-coating method. The coatings showed very high optical quality and the transmission was improved to up to 98.5%. Furthermore, the coatings also presented good mechanical stability.展开更多
基金the Nationnal Natural Science Foundation of China (No. 50342016).
文摘Iron（Ⅲ）-doped nanostructure TiO2-coated SiO2 （TiO2/SiO2） particles were prepared using the layer-by-layer assembly technique and their photocatalytic property was studied. TiO2 colloids were synthesized employing the sol-gel method with TiChas a precursor. The samples were characterized by Fourier transform infrared spectroscopy （FTIR）, SEM, EDS, XPS, and XRD. The experimental results show that TiO2 nanopowders on the surface of SiO2 particles are well distributed, the amount of TiO2 is increased with the adding of coating layers, the pure anatase-TiO2 coating layers are synthesized at 500℃, and the photocatalytic activity of Fe^3＋-doped TiO2/SiO2 is higher than that of undoped TiO2/SiO2.
基金Project(08FJ1002) supported by the Hunan Province Key Project of Science and Technology,China
文摘To research the influence of oxygen flow rate on the structural and optical properties of TiO2 thin film,TiO2 films on glass were deposited by reactive magnetron sputtering.The microstructure and optical properties were measured by X-ray diffractometry,AFM and UV-VIS transmittance spectroscopy,respectively.The results show that the films deposited at oxygen flow rate of 10 mL/min has the lowest roughness and the highest transmittance.The absorption angle shifts to longer wavelengths as oxygen flow rates increase from 5 to 10 mL/min,then to shorter ones as the oxygen flow rate increase from 10 to 30 mL/min.The band gap is 3.38 eV,which is nearly constant in the experiment.For the TiO2 thin films deposited at 10 mL/min of oxyge flow rate,there are nano-crystalline structures,which are suitable for anti-reflection(AR) coating in the solar cells structure system.
基金The authors gratefully acknowledge the financial support of the Brazilian research funding agency CNPq and the Coordination for the Improvement of Higher Education Personnel(CAPES)
文摘Anti-reflective (AR) single layer of silica-titania (SiO2-TiO2) coatings were obtained from sols containing pyromellitic dianhydride (PMDA) derivatives and Ti and Si precursors on glass substrate by dip-coating method. The coatings showed very high optical quality and the transmission was improved to up to 98.5%. Furthermore, the coatings also presented good mechanical stability.