A method for preparing novel ceramics was developed in this study. Different ratios red muds were added to steel slags to optimize the preparation of novel ceramics by a traditional ceramic preparation process. The si...A method for preparing novel ceramics was developed in this study. Different ratios red muds were added to steel slags to optimize the preparation of novel ceramics by a traditional ceramic preparation process. The sintering mechanism, microstructure, and performance were studied by X-ray diffraction techniques, scanning electron microscopy, and combined experiments of linear shrinkage, water absorption, and flexural strength. The results confirmed that red mud can reduce the volumetric instabilities through the complementarity of red mud and ferroalloy slag. The crystal phases in the ceramics are all pyroxene group minerals, including diopside ferrian, augite, and diopside. The flexural strength of the ceramic that contains 40 wt% red mud and was prepared at the optimal sintering temperature(1140°C) is greater than 93 MPa; its corresponding water absorption is less than 0.05%.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51474028)the National Key Research and Development Program of China(No.2017YFC0210301)+2 种基金the China Postdoctoral Science Foundation(No.2017M621034)the Japan Society for the Promotion of Science(JSPS)the Alexander von Humboldt(AvH)Foundation for their financial support
文摘A method for preparing novel ceramics was developed in this study. Different ratios red muds were added to steel slags to optimize the preparation of novel ceramics by a traditional ceramic preparation process. The sintering mechanism, microstructure, and performance were studied by X-ray diffraction techniques, scanning electron microscopy, and combined experiments of linear shrinkage, water absorption, and flexural strength. The results confirmed that red mud can reduce the volumetric instabilities through the complementarity of red mud and ferroalloy slag. The crystal phases in the ceramics are all pyroxene group minerals, including diopside ferrian, augite, and diopside. The flexural strength of the ceramic that contains 40 wt% red mud and was prepared at the optimal sintering temperature(1140°C) is greater than 93 MPa; its corresponding water absorption is less than 0.05%.