The reaction behaviours of A1203 and SiO2 in high alumina coal fly ash under various alkali hydrothermal conditions were studied. The means of XRD, XRF, FTIR and SEM were used to measure the mineral phase and morpholo...The reaction behaviours of A1203 and SiO2 in high alumina coal fly ash under various alkali hydrothermal conditions were studied. The means of XRD, XRF, FTIR and SEM were used to measure the mineral phase and morphology of the solid samples obtained by different alkali hydrothermal treatments as well as the leaching ratio of SiO2 to A1203 in alkali solution. The results showed that with the increase of the hydrothermal treating temperature from 75 to 160 ~C, phillipsite-Na, zeolite A, zeolite P, and hydroxysodalite were produced sequentially while the mullite and corundum phase still remained. Zeolite P was massively formed at low-alkali concentration and the hydroxysodalite was predominantly obtained at high-alkali concentration. By the dissolution of aluminosilicate glass and the formation of zeolites together, the leaching efficiency of SiO2 can reach 42.13% with the mass ratio of A1203/SIO2 up to 2.19：1.展开更多
Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution was studied.The effect of leaching temperature,mass ratio of NaOH to SiO2 and stirring speed on SiO2 leaching rate was inve...Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution was studied.The effect of leaching temperature,mass ratio of NaOH to SiO2 and stirring speed on SiO2 leaching rate was investigated.The results show that increasing leaching temperature,mass ratio of NaOH to SiO2 and stirring speed increases SiO2 leaching rate.The SiO2 leaching rate is 95.66%under the optimized conditions.There are two stages for the SiO2 leaching process,and the leaching reaction is very rapid in the first stage but quite slow in the second stage.The whole leaching process follows the shrinking core model,and the outer diffusion of no product layer is the rate-controlling step.The activation energies of the first and second stages are calculated to be8.492 kJ/mol and 8.668 kJ/mol,respectively.The kinetic equations of the first and the second stages were obtained,respectively.展开更多
基金Project(2652014017) supported by the Fundamental Research Funds for the Central Universities,China
文摘The reaction behaviours of A1203 and SiO2 in high alumina coal fly ash under various alkali hydrothermal conditions were studied. The means of XRD, XRF, FTIR and SEM were used to measure the mineral phase and morphology of the solid samples obtained by different alkali hydrothermal treatments as well as the leaching ratio of SiO2 to A1203 in alkali solution. The results showed that with the increase of the hydrothermal treating temperature from 75 to 160 ~C, phillipsite-Na, zeolite A, zeolite P, and hydroxysodalite were produced sequentially while the mullite and corundum phase still remained. Zeolite P was massively formed at low-alkali concentration and the hydroxysodalite was predominantly obtained at high-alkali concentration. By the dissolution of aluminosilicate glass and the formation of zeolites together, the leaching efficiency of SiO2 can reach 42.13% with the mass ratio of A1203/SIO2 up to 2.19：1.
基金Project (2007CB613603) supported by the National Basic Research Program of ChinaProject (2013M530934) supported by the Postdoctoral Science Foundation of China
文摘Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution was studied.The effect of leaching temperature,mass ratio of NaOH to SiO2 and stirring speed on SiO2 leaching rate was investigated.The results show that increasing leaching temperature,mass ratio of NaOH to SiO2 and stirring speed increases SiO2 leaching rate.The SiO2 leaching rate is 95.66%under the optimized conditions.There are two stages for the SiO2 leaching process,and the leaching reaction is very rapid in the first stage but quite slow in the second stage.The whole leaching process follows the shrinking core model,and the outer diffusion of no product layer is the rate-controlling step.The activation energies of the first and second stages are calculated to be8.492 kJ/mol and 8.668 kJ/mol,respectively.The kinetic equations of the first and the second stages were obtained,respectively.