The preparation of peroxodisulfated zirconia titania(PSZT) solid super acid has been investigated as function of molar ratio of Ti to Zr, impregnation time, calcination time and temperature in esterification of maleic...The preparation of peroxodisulfated zirconia titania(PSZT) solid super acid has been investigated as function of molar ratio of Ti to Zr, impregnation time, calcination time and temperature in esterification of maleic anhydride with n octanol. The highest yield of dioctyl maleate was 98 2% at the optimum reaction conditions.展开更多
The addition of platinum over the B2O3/TiO2-ZrO2 remarkably enhanced its catalytic stability in the vapor phase Beckmann rearrangement of cyclohexanone oxime under the carder gas of H2. The content of coke deposited ...The addition of platinum over the B2O3/TiO2-ZrO2 remarkably enhanced its catalytic stability in the vapor phase Beckmann rearrangement of cyclohexanone oxime under the carder gas of H2. The content of coke deposited on catalyst surface was decreased from 1.92% over the B2O3/TiO2-ZrO2 to 1.14% over the platinum promoted B2O3/TiO2-ZrO2 after reaction of six hours. This result indicates that the platinum added on the B2O3/TiO2-ZrO2 catalyst plays an important role in reducing the coke formation on the catalyst surface.展开更多
文摘The preparation of peroxodisulfated zirconia titania(PSZT) solid super acid has been investigated as function of molar ratio of Ti to Zr, impregnation time, calcination time and temperature in esterification of maleic anhydride with n octanol. The highest yield of dioctyl maleate was 98 2% at the optimum reaction conditions.
文摘The addition of platinum over the B2O3/TiO2-ZrO2 remarkably enhanced its catalytic stability in the vapor phase Beckmann rearrangement of cyclohexanone oxime under the carder gas of H2. The content of coke deposited on catalyst surface was decreased from 1.92% over the B2O3/TiO2-ZrO2 to 1.14% over the platinum promoted B2O3/TiO2-ZrO2 after reaction of six hours. This result indicates that the platinum added on the B2O3/TiO2-ZrO2 catalyst plays an important role in reducing the coke formation on the catalyst surface.