The billets of Al-Zn-Mg-Cu-Zr and Al-Zn-Mg-Cu-Zr-0.5Er alloys were prepared by semi-continuous direct chill casting （DCC）.The effects of trace Er on microstructure of Al-Zn-Mg-Cu-Zr alloy under as-cast and homogeniz...The billets of Al-Zn-Mg-Cu-Zr and Al-Zn-Mg-Cu-Zr-0.5Er alloys were prepared by semi-continuous direct chill casting （DCC）.The effects of trace Er on microstructure of Al-Zn-Mg-Cu-Zr alloy under as-cast and homogenization conditions were studied.The results show that the grain morphology is large dendritic structure and the grain size increases obviously by the addition of 0.5% Er.Moreover,most of Er element in the alloy segregates at grain boundary during solidification,resulting in ternary Al8Cu4Er phase.After homogenization,most of the MgZn2 phase at grain boundary has dissolved back to Al matrix in the two alloys.In the Er-containing alloy,the dissolution temperature of Al8Cu4Er phase is about 575 °C.Therefore,the homogenization treatment cannot eliminate Al8Cu4Er phase validity.展开更多
基金Project(50875031) supported by the National Natural Science Foundation of ChinaProject(2005CB623705) supported by National Basic Research Program of China
文摘The billets of Al-Zn-Mg-Cu-Zr and Al-Zn-Mg-Cu-Zr-0.5Er alloys were prepared by semi-continuous direct chill casting （DCC）.The effects of trace Er on microstructure of Al-Zn-Mg-Cu-Zr alloy under as-cast and homogenization conditions were studied.The results show that the grain morphology is large dendritic structure and the grain size increases obviously by the addition of 0.5% Er.Moreover,most of Er element in the alloy segregates at grain boundary during solidification,resulting in ternary Al8Cu4Er phase.After homogenization,most of the MgZn2 phase at grain boundary has dissolved back to Al matrix in the two alloys.In the Er-containing alloy,the dissolution temperature of Al8Cu4Er phase is about 575 °C.Therefore,the homogenization treatment cannot eliminate Al8Cu4Er phase validity.