The leaching process of magnesiothermic self-propagating product generated during the multistage deep reduction process was investigated.The influence of magnesiothermic self-propagating product particle size,HCl solu...The leaching process of magnesiothermic self-propagating product generated during the multistage deep reduction process was investigated.The influence of magnesiothermic self-propagating product particle size,HCl solution concentration,and leaching solution temperature on the leaching behavior of elements Al and V was investigated.Results demonstrate that the leaching rate of Al and V is increased with the rise in leaching solution temperature,the increase in HCl solution concentration,and the enlargement of magnesiothermic self-propagating product particle size.The leaching processes of Al and V are consistent with the chemical reaction control model.When the magnesiothermic self-propagation product with D_(50) of 59.4μm is selected as the raw material,the leaching temperature is 40℃,and 1 mol/L HCl solution is employed,after leaching for 180 min,the leaching rates of Al and V are 24.8%and 12.6%,respectively.The acid-leached product exhibits a porous structure with a specific surface area of 3.5633 m^(2)/g.展开更多
基金Scientific and Technological Project of Nanyang(23KJGG017)Key Specialized Research&Development and Promotion Project(Scientific and Technological Project)of Henan Province(232102221022)+1 种基金College Students and Technology Innovation Fund Project of Nanyang Institute of Technology(2023139)Project of Doctoral Scientific Research Startup Fund of Nanyang Institute of Technology(NGBJ-2023-25)。
文摘The leaching process of magnesiothermic self-propagating product generated during the multistage deep reduction process was investigated.The influence of magnesiothermic self-propagating product particle size,HCl solution concentration,and leaching solution temperature on the leaching behavior of elements Al and V was investigated.Results demonstrate that the leaching rate of Al and V is increased with the rise in leaching solution temperature,the increase in HCl solution concentration,and the enlargement of magnesiothermic self-propagating product particle size.The leaching processes of Al and V are consistent with the chemical reaction control model.When the magnesiothermic self-propagation product with D_(50) of 59.4μm is selected as the raw material,the leaching temperature is 40℃,and 1 mol/L HCl solution is employed,after leaching for 180 min,the leaching rates of Al and V are 24.8%and 12.6%,respectively.The acid-leached product exhibits a porous structure with a specific surface area of 3.5633 m^(2)/g.