Micro-arc oxidation （MAO） process was carried out in a dual electrolyte system of NaAlO 2 and Na 3 PO 4 to develop compact, smooth and corrosion-resistant coatings on ZK60 Mg alloy by single factor experiments. The ...Micro-arc oxidation （MAO） process was carried out in a dual electrolyte system of NaAlO 2 and Na 3 PO 4 to develop compact, smooth and corrosion-resistant coatings on ZK60 Mg alloy by single factor experiments. The microstructural characteristics of coatings were investigated by X-ray diffractometry （XRD） and scanning electron microscopy （SEM） coupled with energy dispersive X-ray spectroscopy （EDS）. Test of mass loss was conducted at a 3.5% NaCl solution to assess the resistance to corrosion. The effect of every element in the dual electrolyte system on voltage—time responses during MAO process and the coating characteristic were also analyzed and discussed systematically via single factor experiments. The results reveal that the main components of NaAlO 2 and Na 3 PO 4 as well as additives of NaOH, NaB4O7 and C6H5Na3O7 demonstrate different effects on MAO process and coating characteristics. By means of single factor experiments, an optimized dual electrolyte system was developed, containing 17.5 g/L NaAlO 2, 5.0 g/LNa3 PO4, 5.0 g/L NaOH, 3.0 g/L NaB4O7 and 4.2g/LC6H5Na3O7 .展开更多
研究了Cu Al Be B形状记忆合金的成分、微观组织和相结构与阻尼和力学性能的关系 ,通过扫描电镜原位观察合金在单向拉伸应力作用下裂纹萌生和扩展的特征。结果表明 :应力诱发马氏体变体的转变使Cu Al Be B合金具有较高的阻尼性能 ;弹性...研究了Cu Al Be B形状记忆合金的成分、微观组织和相结构与阻尼和力学性能的关系 ,通过扫描电镜原位观察合金在单向拉伸应力作用下裂纹萌生和扩展的特征。结果表明 :应力诱发马氏体变体的转变使Cu Al Be B合金具有较高的阻尼性能 ;弹性各向异性和相变应变差引发晶界应力集中 ,导致合金在拉伸条件下发生晶间断裂 ;18R与 2H马氏体混合程度大时 ,会增加相变应变差引起的晶界应力集中和可能萌生的晶界裂纹源 ,大大减小合金的塑性和强度。展开更多
基金Project(JSAWT-09-02)supported by the Key Laboratory of Advanced Welding Technology of Jiangsu Province,ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘Micro-arc oxidation （MAO） process was carried out in a dual electrolyte system of NaAlO 2 and Na 3 PO 4 to develop compact, smooth and corrosion-resistant coatings on ZK60 Mg alloy by single factor experiments. The microstructural characteristics of coatings were investigated by X-ray diffractometry （XRD） and scanning electron microscopy （SEM） coupled with energy dispersive X-ray spectroscopy （EDS）. Test of mass loss was conducted at a 3.5% NaCl solution to assess the resistance to corrosion. The effect of every element in the dual electrolyte system on voltage—time responses during MAO process and the coating characteristic were also analyzed and discussed systematically via single factor experiments. The results reveal that the main components of NaAlO 2 and Na 3 PO 4 as well as additives of NaOH, NaB4O7 and C6H5Na3O7 demonstrate different effects on MAO process and coating characteristics. By means of single factor experiments, an optimized dual electrolyte system was developed, containing 17.5 g/L NaAlO 2, 5.0 g/LNa3 PO4, 5.0 g/L NaOH, 3.0 g/L NaB4O7 and 4.2g/LC6H5Na3O7 .
文摘研究了Cu Al Be B形状记忆合金的成分、微观组织和相结构与阻尼和力学性能的关系 ,通过扫描电镜原位观察合金在单向拉伸应力作用下裂纹萌生和扩展的特征。结果表明 :应力诱发马氏体变体的转变使Cu Al Be B合金具有较高的阻尼性能 ;弹性各向异性和相变应变差引发晶界应力集中 ,导致合金在拉伸条件下发生晶间断裂 ;18R与 2H马氏体混合程度大时 ,会增加相变应变差引起的晶界应力集中和可能萌生的晶界裂纹源 ,大大减小合金的塑性和强度。