摘要
The preparation of alumina with large surface area, certain phase and porosimetry has always been one of important researches. A new method using much less sucrose (the molar ratio of sucrose to Al 3+=0 5) was developed to prepare γ-Al 2O 3 with large surface area and high thermal stability. Firstly,ammonium hydroxide was dropped to aqueous solution of aluminum nitrate and sucrose. The resulted precipitate in suspension was heated until a homogeneous gel was obtained. Then the gel was dehydrated at 110 ℃ to get a fluffy black precursor. Finally, γ-Al 2O 3 with A=345 m2/g was prepared by calcining the precursor at 600 ℃ for 24 h. The precursor and the obtained γ-Al 2O 3 were characterized by DTA-TG, N 2 adsorption-desorption isotherms, XRD and TEM. According to the dispersion behaviors of organic compounds on supports, the related mechanism was discussed.
The preparation of alumina with large surface area, certain phase and porosimetry has always been one of important researches. A new method using much less sucrose (the molar ratio of sucrose to Al 3+=0 5) was developed to prepare γ-Al 2O 3 with large surface area and high thermal stability. Firstly,ammonium hydroxide was dropped to aqueous solution of aluminum nitrate and sucrose. The resulted precipitate in suspension was heated until a homogeneous gel was obtained. Then the gel was dehydrated at 110 ℃ to get a fluffy black precursor. Finally, γ-Al 2O 3 with A=345 m2/g was prepared by calcining the precursor at 600 ℃ for 24 h. The precursor and the obtained γ-Al 2O 3 were characterized by DTA-TG, N 2 adsorption-desorption isotherms, XRD and TEM. According to the dispersion behaviors of organic compounds on supports, the related mechanism was discussed.
出处
《催化学报》
SCIE
CAS
CSCD
北大核心
2004年第5期341-343,共3页
基金
国家自然科学基金资助项目 (2 0 173 0 0 2 )
国家重点基础研究发展规划项目 (G2 0 0 0 0 775 0 3 )
关键词
蔗糖
氧化铝
比表面积
孔径分布
alumina, sucrose, specific surface area, pore size distribution